Influence of heat treatment on slurry erosive wear resistance of Al6061 alloy

Abstract Material loss due to slurry erosion is a serious problem in many industrial applications like hydraulic turbines, slurry pumps, pipe lines, etc. where the ideal choice of engineering materials is a real challenge. Light weight aluminum alloys are finding wide applications in the field of aerospace, automobile, defence, etc. due to improved physical, mechanical and tribological properties. Among all available alloys Al6061 is extensively used owing to its reasonable strength and ease of processing. Currently these alloys are also explored as candidate materials for propeller blade of torpedoes where major failure occurs due to slurry erosive wear. In the light of the above present investigation is aimed to study the slurry erosive wear behavior of heat treated Al6061 alloy in 3.5%NaCl solution with sand particles slurry. The studies were carried out at different sand concentration (10–40%), varying rotational speed (500–1500 rpm), at different time duration (5–25 h) and varied impinging particle size (100–600 μm). The effect of heat treatment on erosive wear behavior of Al6061 alloy were studied by subjecting to solutionising at temperature of 530 °C for a duration of 2 h, followed by quenching in air, water and ice media. Both natural and artificial aging at 175 °C was performed on quenched samples from 4 to 10 h duration in steps of 2 h. The rate of material loss is found to be higher with increased sand concentration due to increased impinging action of sand particles. Increased speed of slurry rotation increases the velocity of impingement of sand particles on the surface of erodent and resulted in higher weight loss. Increased time duration up to 20 h, the wear rate increases. However, beyond this test duration, the wear rate attains a steady state with further increase in test duration. It is found that heat treatment has profound effect on slurry erosive wear resistance of Al6061 alloy. It is also observed that with increase in aging duration for all quenching medias studied there is a reduction in slurry erosive wear rate. However, ice as quenching media offers higher erosive wear resistance compared to water, air and unheat treated alloy. SEM studies were carried out on eroded surface to observe the mechanism of metal removal. The eroded surface also indicates that increased sand concentration, higher rotational speed and increased particle size resulted in severe damage on tested surfaces.

[1]  A. Crosky,et al.  Secondary precipitation in an Al–Mg–Si–Cu alloy , 2007 .

[2]  Robert J.K. Wood,et al.  Comparison of predicted and experimental erosion estimates in slurry ducts , 2004 .

[3]  On the correlation of mechanical and physical properties of 6061-T6 and 7249-T76 aluminum alloys , 2007 .

[4]  M. I. Barrena,et al.  Influence of heat treatments on the wear behaviour of an AA6092/SiC25p composite , 2004 .

[5]  I. Hutchings,et al.  The influence of corrosion on the erosion of aluminium by aqueous silica slurries , 1995 .

[6]  T. Nicholas.  An approach to fatigue life modeling in titanium-matrix composites , 1995 .

[7]  D Laux,et al.  Ultrasonic measurement of anisotropy and temperature dependence of elastic parameters by a dry coupling method applied to a 6061-T6 alloy. , 2007, Ultrasonics.

[8]  G. Addie,et al.  Experimental study on erosive wear of some metallic materials using Coriolis wear testing approach , 2005 .

[9]  S. Turenne,et al.  Influence of structural parameters on the slurry erosion resistance of squeeze-cast metal matrix composites☆ , 1991 .

[10]  D. Mondal,et al.  Mechanisms of material removal during erosion-corrosion of an Al-SiC particle composite , 1999 .

[11]  B. Prasad.  Effects of alumina particle dispersion on the erosive–corrosive wear response of a zinc-based alloy under changing slurry conditions and distance , 2000 .

[12]  M. B. House,et al.  Elevated Temperature Strength, Aging Response and Creep of Aluminum Matrix Composites , 1992 .

[13]  C. Ramesh,et al.  Wear behavior of hot extruded Al6061 based composites , 2007 .

[14]  D. Mondal,et al.  Erosive-corrosive wear of aluminum alloy composites : Influence of slurry composition and speed , 2006 .

[15]  B. K. Prasad,et al.  Study of erosive-corrosive wear characteristics of an aluminium alloy composite through factorial design of experiments , 1998 .

[16]  A. H. Yegneswaran,et al.  Wear behaviour of zinc-based alloys as influenced by alloy composition, nature of the slurry and traversal distance , 2008 .

[17]  C. Fang,et al.  The effect of humidity on the erosive wear of 6063 Al alloy , 1999 .

[18]  M. Ramachandra,et al.  Effect of reinforcement of flyash on sliding wear, slurry erosive wear and corrosive behavior of aluminium matrix composite , 2007 .

[19]  H. Conrad,et al.  Local impact damage and erosion mechanisms in WC-6wt.%Co alloys , 1988 .

[20]  H. Clark,et al.  Assessment of the erosion resistance of steels used for slurry handling and transport in mineral processing applications , 2001 .

[21]  A. Daoud,et al.  Influence of Al2O3 particulate on the aging response of A356 Al-based composites , 2002 .

[22]  J. J. Ward,et al.  An approach to material selection for corrosive-abrasive wear by systematic in-situ and laboratory testing procedures , 1985 .

[23]  S. Jain,et al.  Slurry erosion of ductile materials under normal impact condition , 2008 .

[24]  S. Caron,et al.  The effect of abrasive particle size on the slurry erosion resistance of particulate-reinforced aluminium alloy , 1990 .

[25]  H. Clark,et al.  A re-examination of the ‘particle size effect’ in slurry erosion , 2001 .

[26]  Robert J.K. Wood,et al.  Erosion of aluminium-based claddings on steel by sand in water , 2001 .

[27]  W. J.-J.,et al.  Microstructure and mechanical properties of cast (Al–Si)/SiCp composites produced by liquid and semisolid double stirring process , 2000 .