Study on Microstructure and Properties of Plasma Arc Surfacing Layer for Cutting Pick

Cutting tooth especially due to the poor quality of the shearer brazing, caused great pick consumption and delayed hours. The tooth body wear of the whole shearer picks accounts for half of its overall failure. In this experiment, the cutting pick jiont which was welded by induction brazing was strengthened by plasma arc powder surfacing, then analyse the microstructure, surface topography, and mechanical property of the weld jiont, so as to provide a new scheme for solving the tooth wear failure, and extending the service life. The pick failure problem caused by the lower hardness of the tooth tip, tooth wear, and the premature loss of hard alloy head.

M. He | Feng Yang | Ning Zhang | M. Shi | L. Yang

[1] Bin Wang,et al. Characterization of surface hardened layers on Q235 low-carbon steel treated by plasma electrolytic borocarburizing , 2013 .

[2] L. J. Yang. The effect of specimen thickness on the hardness of plasma surface hardened ASSAB 760 steel specimens , 2007 .

[3] I. Park,et al. Microstructures and mechanical properties of surface-hardened layer produced on SKD 61 steel by plasma radical nitriding , 2007 .

[4] R. Webb,et al. Plasma hydrophilic surface treatment for dehumidifying heat exchangers , 2002 .

[5] Bernd Edenhofer,et al. Plasma-carburising : a surface heat treatment process for the new century , 2001 .

[6] V. Leskovšek,et al. Wear properties of induction hardened, conventional plasma nitrided and pulse plasma nitrided AISI 4140 steel in dry sliding conditions , 1999 .

[7] M. Lei,et al. Plasma source ion nitriding of pure iron: formation of an iron nitride layer and hardened diffusion layer at low temperature , 1997 .