Chemiresistor-type NO gas sensor based on nickel phthalocyanine thin films

Abstract The sensing characteristics of nickel phthalocyanine (NiPc) thin films for use in a chemiresistor-type nitric oxide gas sensor are discussed. The gas-sensing properties, including current transient, sensitivity, response time, and aging, are studied. A kinetic model proposed in the literature for sensing NO2 with lead phthalocyanine (PbPc) thin films, in which adsorption involves displacement of surface adsorbed O2 from a range of heterogeneous sites, can be used to explain our experimental results. It is inferred that exposure to NO concentrations lower than 50 ppm only involves the population of weak adsorption sites, while exposure to NO concentrations higher than 50 ppm may involve the population of stronger adsorption sites. Repeated step changes in NO concentrations of 50 ppm could result in a significant change in response currents within the first five cycles, presumably due to the presence of an irreversible adsorption. Further analysis of current responses reveals that the lower the concentration of NO, the larger the sensitivity. For a lower concentration range, between 5 and 50 ppm NO, the sensitivity lies between 0.41 and 0.42, while for a higher concentration range, between 50 and 500 ppm, the sensitivity decreases to about 0.17 to 0.19.

[1]  R. A. Collins,et al.  The effects of humidity on phthalocyanine NO2 and NH3 sensors , 1990 .

[2]  R. A. Collins,et al.  Adsorption and bulk diffusion of chlorine in monoclinic lead phthalocyanine thin film gas sensors , 1993 .

[3]  Mahmoud Z. Iskandarani,et al.  Effect of electrode geometry on gas sensitivity of lead phthalocyanine thin films , 1992 .

[4]  John D. Wright,et al.  Kinetic factors in the response of organometallic semiconductor gas sensors , 1989 .

[5]  C. Maleysson,et al.  Thin layers of poly(fluoroaluminium-phthalocyanine) , 1987 .

[6]  A. Pauly,et al.  Conductivity and gas species content of (AlPcF)n thin films exposed to O2 or NO2 , 1994 .

[7]  J. R. Bates,et al.  Gas sensors and analysers , 1997 .

[8]  A. Pauly,et al.  Doping mechanisms of phthalocyanines by oxidizing gases: Application to gas sensors , 1994 .

[9]  J. Hsieh,et al.  Response characteristics of lead phthalocyanine gas sensor: Effect of operating temperature and postdeposition annealing , 1996 .

[10]  G. Heiland,et al.  Electrical and optical properties of phthalocyanine films , 1987 .

[11]  John D. Wright,et al.  A microprocessor-controlled nitrogen dioxide sensing system , 1991 .

[12]  J. Hsieh,et al.  Titanyl phthalocyanine gas sensor for NO2 detection , 1998 .

[13]  T. A. Jones,et al.  A highly sensitive NO2 sensor based on electrical conductivity changes in phthalocyanine films , 1984 .

[14]  Shinji Kanefusa,et al.  The detection of H2 gas by metal phthalocyanine-based gas sensors , 1992 .

[15]  Y. Park,et al.  Enhancement of the NO2-sensing capability of copper phthalocyanine by measuring the realtive resistance change , 1996 .

[16]  J. Lando,et al.  Gas-sensing mechanism of phthalocyanine Langmuir-Blodgett films , 1994 .

[17]  S. C. Thorpe,et al.  Mössbauer and microstructural studies of iron phthalocyanine as a potential gas sensor , 1993 .

[18]  J. Simon,et al.  Lutetium bisphthalocyanine thin films for gas detection , 1992 .

[19]  D. Jiang,et al.  Interaction between copper tetra-4(2,4-ditert-amylphenoxy) phthalocyanine Langmuir-Blodgett films as a gas-sensitive sensor and NH3 , 1991 .

[20]  M. Campbell.  Sensor Systems for Environmental Monitoring , 1996 .