Effect of annealing on upconversion luminescence of ZnO : Er3+ nanocrystals and high thermal sensitivity

The effect of annealing on the upconversion luminescence of ZnO:Er3+ nanocrystals was investigated in detail. The green and the red upconverted emissions under infrared 978-nm light excitation were remarkably enhanced with an increase of annealing temperature. Moreover, for the sample annealed at 500 °C, the ratio of the intensity of 2H11/2 → 4I15/2 emission to that of 4S3/2 → 4I15/2 emission increased from less than to more than unity with an increase of the excitation density. However, the same case did not occur to the sample annealed at 700 °C, where the ratio was independent of excitation density except when the excitation density was higher than 42 700 W/cm2. This distinction was attributed mainly to the difference in energy gap between the 2H11/2 and 4S3/2 states in the two samples, originating from the local microstructure variation around Er3+ ions. In addition, a high thermal sensitivity of 0.0062/°C was obtained in the ZnO:Er3+ nanocrystals based on the temperature-dependent fluorescence intens...

[1]  G. Shan,et al.  Luminescence spectroscopy and visible upconversion properties of Er3+ in ZnO nanocrystals , 2004 .

[2]  R. Sam Niedbala,et al.  Up-converting phosphor reporters for nucleic acid microarrays , 2001, Nature Biotechnology.

[3]  A. Speghini,et al.  Concentration-Dependent Near-Infrared to Visible Upconversion in Nanocrystalline and Bulk Y2O3:Er3+ , 2003 .

[4]  Wei Chen,et al.  Nanoparticle luminescence thermometry , 2002 .

[5]  A. Speghini,et al.  Enhancement of Red Emission (4F9/2 → 4I15/2) via Upconversion in Bulk and Nanocrystalline Cubic Y2O3:Er3+ , 2002 .

[6]  E. Rosa,et al.  Strong green upconversion emission in ZrO2:Yb3+–Ho3+ nanocrystals , 2005 .

[7]  Marco Bettinelli,et al.  NIR to Visible Upconversion in Nanocrystalline and Bulk Lu2O3:Er3+ , 2002 .

[8]  A. Polman,et al.  Erbium as a probe of everything , 2001 .

[9]  Marc A. Anderson,et al.  Semiconductor clusters in the sol-gel process: quantized aggregation, gelation, and crystal growth in concentrated zinc oxide colloids , 1991 .

[10]  Stephen F Collins,et al.  Effect of strain on temperature measurements using the fluorescence intensity ratio technique (with Nd3+- and Yb3+-doped silica fibers) , 2001 .

[11]  L. M. Toth,et al.  Green Upconversion Emission from Er3+ Ion Doped into Sol-Gel Silica Glasses under Red Light (647.1 nm) Excitation , 1995 .

[12]  D. Su,et al.  Green ErIII luminescence in fractal ZnO nanolattices , 2002 .

[13]  D. Yuan,et al.  Structure evaluation and highly enhanced luminescence of Dy3+ -doped ZnO nanocrystals by Li+ doping via combustion method. , 2004, Langmuir : the ACS journal of surfaces and colloids.

[14]  Y. Aoyagi,et al.  Highly erbium-doped zinc–oxide thin film prepared by laser ablation and its 1.54 μm emission dynamics , 2000 .

[15]  A. S. Gouveia-Neto,et al.  Optical temperature sensing using upconversion fluorescence emission in Er3+/Yb3+-codoped chalcogenide glass , 1998 .

[16]  Hong Zhang,et al.  Synthesis and Characterization of Water-Soluble and Bifunctional ZnO-Au Nanocomposites , 2007 .

[17]  Yichun Liu,et al.  Effects of Er3+ concentration on UV/blue upconverted luminescence and a three-photon process in the cubic nanocrystalline Y2O3:Er3+ , 2006 .

[18]  Y. Aoyagi,et al.  Local structure analysis of an optically active center in Er-doped ZnO thin film , 2001 .

[19]  Kenneth T. V. Grattan,et al.  Comparison of fluorescence-based temperature sensor schemes: Theoretical analysis and experimental validation , 1998 .

[20]  Alfred Forchel,et al.  A Simple Colloidal Route to Planar Micropatterned Er@ZnO Amplifiers , 1999 .

[21]  Hongjiang Liu,et al.  Optical Spectroscopy and Visible Upconversion Studies of YVO4:Er3+ Nanocrystals Synthesized by a Hydrothermal Process , 2006 .

[22]  Dosi M. Dosev,et al.  Fluorescence upconversion in Sm-doped Gd2O3 , 2006 .

[23]  Xinwei Zhao,et al.  1.54 μm emission dynamics of erbium-doped zinc-oxide thin films , 2000 .

[24]  Surfactant‐Assisted Synthesis of Co‐ and Li‐Doped ZnO Nanocrystalline Samples Showing Room‐Temperature Ferromagnetism , 2006, cond-mat/0605332.

[25]  Fotios Sidiroglou,et al.  Effects of high-temperature heat treatment on Nd3+-doped optical fibers for use in fluorescence intensity ratio based temperature sensing , 2003 .

[26]  W. H. Lowdermilk,et al.  Multiphonon relaxation of rare-earth ions in oxide glasses , 1977 .

[27]  A. Forchel,et al.  Activation of 1.54 μm Er3+ fluorescence in concentrated II-VI semiconductor cluster environments , 1998 .

[28]  M. Haase,et al.  Highly Efficient Multicolour Upconversion Emission in Transparent Colloids of Lanthanide‐Doped NaYF4 Nanocrystals , 2004 .

[29]  A. Eychmüller,et al.  Annealing of Nanometer-Sized Zinc Oxide Particles , 2002 .

[30]  S. Wade,et al.  Fluorescence intensity ratio technique for optical fiber point temperature sensing , 2003 .