Preparation and characterization of activated carbons from impregnation pitch by ZnCl2

Abstract Using an impregnation pitch from bituminous coal tar (OP) supplied by Industrias Quimicas del Nalon Company as raw material, two phases (isotropic and anisotropic) have been obtained. The latter was used as precursor for the preparation of activated carbons. First, a chemical activation process was carried out with ZnCl 2 as activating agent. The process was conducted at different concentrations and temperatures and by means of impregnation with solid zinc chloride. Optimal values were obtained for samples prepared by using a ZnCl 2 :pitch ratio equal to 3:1 (sample AZn3). Next, this sample was thermally treated at two different temperatures, i.e., 700 and 800 °C. A lose of specific surface area, microporosity and mesoporosity was observed with respect to sample AZn3, such a lose being more remarkable as temperature increased. Moreover, impregnation of the anisotropic phase of the original pitch with an aqueous solution of ZnCl 2 followed by thermal treatment resulted in a poorly developed surface area and porous texture, probably due to the presence of Zn complexes, which interfere with the activation process.

[1]  F. Rodríguez-Reinoso,et al.  Activated carbons from lignocellulosic materials by chemical and/or physical activation: an overview , 1992 .

[2]  Krishna Kadirvelu,et al.  Uptake of mercury (II) from wastewater by activated carbon from an unwanted agricultural solid by-product: coirpith , 1999 .

[3]  Á. Linares-Solano,et al.  Preparation of Pt catalysts supported on activated carbon felts (ACF) , 2002 .

[4]  F. Rodríguez-Reinoso,et al.  Preparation of activated carbon by chemical activation with ZnCl2 , 1991 .

[5]  Maria Angeles Lillo-Rodenas,et al.  Understanding chemical reactions between carbons and NaOH and KOH: An insight into the chemical activation mechanism , 2003 .

[6]  Harry Marsh,et al.  Introduction to carbon technologies , 1997 .

[7]  H. Teng,et al.  Activated carbon production from low ash subbituminous coal with CO2 activation , 1998 .

[8]  Dan D. Edie,et al.  Carbon-Carbon Materials and Composites , 1994 .

[9]  R. Menéndez,et al.  A novel method for mesophase separation , 1997 .

[10]  Dolores Lozano-Castelló,et al.  Preparation of activated carbons from spanish anthracite. II. Activation by NaOH , 2001 .

[11]  H. Tseng,et al.  Carbon materials as catalyst supports for SO2 oxidation: catalytic activity of CuO–AC , 2003 .

[12]  X. Py,et al.  Pitch pyrolysis kinetics: isothermal heat treatment experiments and model , 2000 .

[13]  R. Menéndez,et al.  Influence of matrix precursors on the microstructure and mechanical properties of C/C composites , 1995 .

[14]  S. Chander,et al.  Single component and multi-component adsorption of metal ions by activated carbons , 2001 .

[15]  Guohua Chen,et al.  Preparation of carbon adsorbents with high surface area and a model for calculating surface area , 2002 .

[16]  E. Teller,et al.  On a Theory of the van der Waals Adsorption of Gases , 1940 .

[17]  Mohammed M. Farid,et al.  Adsorption kinetics for the removal of chromium(VI) from aqueous solution by adsorbents derived from used tyres and sawdust , 2001 .