Mechanical and microstructural properties of robotic Cold Metal Transfer (CMT) welded 5083-H111 and 6082-T651 aluminum alloys

H111 and 6082-T651 aluminum alloys used particularly in shipbuilding industry especially for the sake of their high corrosion resistance and moderate strength, were welded using Pulsed Robotic Cold Metal Transfer (CMT)-Metal Inert Gas (MIG) technology. Joints were fabricated as both similar and dis- similar alloy welds using plates with a thickness of 6 mm. Non-destructive tests such as visual and radio- logical examination were conducted before further destructive tests. Tensile, bend and fatigue tests were applied to specimens extracted from welded joints. Fracture surfaces of fatigue samples were examined by light optical microscopy (LOM) and scanning electron microscopy (SEM). Also macro and microstruc- tures of weld zones were investigated and micro hardness profiles were obtained. In accordance with results, CMT-MIG provides good joint efficiency with high welding speed, and good tensile and fatigue performance.

[1]  G. Mathers.  The welding of aluminium and its alloys , 2002 .

[2]  A. Jesus,et al.  Fatigue crack growth in friction stir welds of 6082-T6 and 6061-T6 aluminium alloys: A comparison , 2008 .

[3]  J. Kaufman.  Introduction to Aluminum Alloys and Tempers , 2000 .

[4]  Mats Ericsson,et al.  Influence of welding speed on the fatigue of friction stir welds, and comparison with MIG and TIG , 2003 .

[5]  D. Scott MacKenzie,et al.  Physical metallurgy and processes , 2003 .

[6]  E. Taban,et al.  Microstructural and mechanical properties of double-sided MIG, TIG and friction stir welded 5083-H321 aluminium alloy , 2006 .

[7]  K. Young,et al.  Evaluation of cold metal transfer (CMT) process for welding aluminium alloy , 2006 .

[8]  P.M.S.T. de Castro,et al.  Mechanical and metallurgical characterization of friction stir welding joints of AA6061-T6 with AA6082-T6 , 2009 .

[9]  Karl-Heinrich Grote,et al.  Springer handbook of mechanical engineering , 2009 .

[10]  Wolfgang Beitz,et al.  Handbook of mechanical engineering , 1994 .

[11]  N. Geoffroy,et al.  Fatigue behaviour of an arc welded Al–Si–Mg Alloy , 2007 .

[12]  Rajiv S. Mishra,et al.  Friction Stir Welding and Processing , 2007 .

[13]  Qi Zhou,et al.  Microstructure characteristics and mechanical properties of cold metal transfer welding Mg/Al dissimilar metals , 2012 .

[14]  Antonino Squillace,et al.  Effect of welding parameters on mechanical and microstructural properties of AA6082 joints produced by friction stir welding , 2008 .

[15]  Yao Liu,et al.  Microstructure and mechanical properties of aluminum 5083 weldments by gas tungsten arc and gas metal arc welding , 2012 .

[16]  E. Kaluç,et al.  Comparison between microstructure characteristics and joint performance of 5086-H32 aluminium alloy welded by MIG, TIG and friction stir welding processes , 2007 .

[17]  P.M.S.T. de Castro,et al.  Fatigue behaviour of FSW and MIG weldments for two aluminium alloys , 2007 .

[18]  R. Cao,et al.  Cold Metal Transfer joining of magnesium AZ31B-to-aluminum A6061-T6 , 2013 .

[19]  P. He,et al.  The CMT short-circuiting metal transfer process and its use in thin aluminium sheets welding , 2009 .

[20]  William R. Oates,et al.  Materials and applications , 1996 .

[21]  J. Wang,et al.  Microstructure of Al–Mg dissimilar weld made by cold metal transfer MIG welding , 2008 .

[22]  Dheerendra Kumar Dwivedi,et al.  Thin sheet welding of Al 6082 alloy by AC pulse-GMA and AC wave pulse-GMA welding , 2009 .

[23]  D. Scott MacKenzie,et al.  Handbook of Aluminum : Vol. 1: Physical Metallurgy and Processes , 2003 .

[24]  Marek Szkodo,et al.  Friction Stir Welds (FSW) of aluminium alloy AW6082-T6 , 2007 .