Mechanical and thermal properties of gelatin films at different degrees of glutaraldehyde crosslinking.

The mechanical, thermal, swelling and release properties of glutaraldehyde (GTA) crosslinked gelatin films have been investigated in order to verify the influence of GTA concentration on the stability of the films. Air-dried films were submitted to treatment with GTA solutions at concentrations ranging from 0.05 to 2.5 wt%. At the smallest GTA concentration, the crosslinking degree, determined by trinitrobenzensulfonic acid assay, amounts to about 60% and increases up to values near 100%, obtained with GTA concentrations > or = 1 wt%. Simultaneously, the deformability of the films decreases, whereas the stress at break, sigmab, and the Young's modulus, E, increase. A crosslinking degree of about 85%, obtained using 0.25% GTA, is enough to prevent gelatin release in buffer solution and to provoke a significant reduction of the swelling in physiological solution. Furthermore, crosslinking greatly affects the thermal stability of the samples, as indicated by the results of differential scanning calorimetry (d.s.c.) investigation carried out on wet and air-dried films. The data suggest that the use of GTA at low concentration, which is desiderable to prevent toxicity, allows to modulate the physico-chemical properties of gelatin films, in order to obtain stable materials with a wide range of possible biomedical applications.

[1]  Simon B. Ross-Murphy,et al.  Structure and rheology of gelatin gels : recent progress , 1992 .

[2]  E. Khor Methods for the treatment of collagenous tissues for bioprostheses. , 1997, Biomaterials.

[3]  A. Veis The Macromolecular Chemistry of Gelatin , 1964 .

[4]  Roberto J. J. Williams,et al.  Thermal properties of gelatin films , 1985 .

[5]  G. Goissis,et al.  Biocompatibility studies of anionic collagen membranes with different degree of glutaraldehyde cross-linking. , 1999, Biomaterials.

[6]  J. Feijen,et al.  Characterization of the Network Structure of Carbodiimide Cross-Linked Gelatin Gels , 1999 .

[7]  J. Feijen,et al.  Glutaraldehyde as a crosslinking agent for collagen-based biomaterials , 1995 .

[8]  A. Bigi,et al.  Differential scanning calorimetry and X-ray diffraction study of tendon collagen thermal denaturation , 1987 .

[9]  A. Bigi,et al.  Drawn gelatin films with improved mechanical properties. , 1998, Biomaterials.

[10]  V. Shah,et al.  Cross-linking of gelatin capsules and its relevance to their in vitro-in vivo performance. , 1994, Journal of pharmaceutical sciences.

[11]  A. Jayakrishnan,et al.  Glutaraldehyde as a fixative in bioprostheses and drug delivery matrices. , 1996, Biomaterials.

[12]  J. Feijen,et al.  Characterization and biocompatibility of epoxy-crosslinked dermal sheep collagens. , 1999, Journal of biomedical materials research.

[13]  M. Djabourov,et al.  Conformation of gelatin chains in aqueous solutions: 1. A light and small-angle neutron scattering study , 1991 .

[14]  A. Huc,et al.  Evaluation of different chemical methods for cros-linking collagen gel, films and sponges , 1996 .

[15]  C. Nastruzzi,et al.  Gelatin microspheres: influence of preparation parameters and thermal treatment on chemico-physical and biopharmaceutical properties. , 1996, Biomaterials.

[16]  D. Speer,et al.  Biological effects of residual glutaraldehyde in glutaraldehyde-tanned collagen biomaterials. , 1980, Journal of biomedical materials research.

[17]  A. Bigi,et al.  Structural and Mechanical Properties of Crosslinked Drawn Gelatin Films , 2000 .

[18]  H. Sung,et al.  Evaluation of gelatin hydrogel crosslinked with various crosslinking agents as bioadhesives: in vitro study. , 1999, Journal of biomedical materials research.

[19]  A. Finch,et al.  Shrinkage of collagen fibres: a differential scanning calorimetric study. , 1972, Biochimica et biophysica acta.

[20]  H. Mark,et al.  Encyclopedia of polymer science and engineering , 1985 .

[21]  D. Achet,et al.  Determination of the renaturation level in gelatin films , 1995 .

[22]  Yoshiteru Watanabe,et al.  Effect of Formaldehyde on the Physicochemical Properties of Soft Gelatin Capsule Shells , 1994 .

[23]  Y Ikada,et al.  Hemostatic capability of rapidly curable glues from gelatin, poly(L-glutamic acid), and carbodiimide. , 1998, Biomaterials.

[24]  J. Renou,et al.  Effect of collagen crosslinking on collagen-water interactions (a DSC investigation). , 1989, Matrix.

[25]  K. Miyasaka,et al.  Reconstitution of collagen‐fold structure with stretching of gelatin film , 1976, Biopolymers.