Evolution of defect size and strength of porous alumina during sintering

[1]  D. Munz,et al.  Correlation between long and short crack R-curves in alumina using the crack opening displacement and fracture mechanical weight function approach , 1996 .

[2]  Doh-Yeon Kim,et al.  Shrinkage of Large Isolated Pores during Hot Isostatic Pressing of Presintered Alumina Ceramics , 1995 .

[3]  A. Evans,et al.  Mechanical Properties of Partially Dense Alumina Produced from Powder Compacts , 1994 .

[4]  H. Riedel,et al.  Equilibrium pore surfaces, sintering stresses and constitutive equations for the intermediate and late stages of sintering—I. computation of equilibrium surfaces , 1994 .

[5]  A. Evans,et al.  Behavior of Large Pores During Sintering and Hot Isostatic Pressing , 1986 .

[6]  Roy W. Rice,et al.  Pores as fracture origins in ceramics , 1984 .

[7]  前仏 忠.  Strength of Reaction-bonded Silicon Nitride with Artificial Pores , 1982 .

[8]  Robert L. Coble,et al.  Effect of Porosity on Physical Properties of Sintered Alumina , 1956 .

[9]  J. Rödel,et al.  Evolution of strength determining flaws during sintering , 1996 .

[10]  J. Rödel,et al.  Reliability of alumina ceramics: Effect of grain size , 1995 .

[11]  D. S. Pearson,et al.  Influence of Interparticle Forces on the Rheological Behavior of Pressure‐Consolidated Alumina Particle Slurries , 1994 .

[12]  W. Kingery,et al.  The Sintering of Crystalline Oxides, I. Interactions Between Grain Boundaries and Pores , 1990 .

[13]  B. Kellett,et al.  Experiments on pore closure during hot isostatic pressing and forging , 1988 .

[14]  K. Phani,et al.  Young's modulus of porous brittle solids , 1987 .

[15]  F. I. Baratta.  Refinement of Stress Intensity Factor Estimates for a Peripherally Cracked Spherical Void and a Hemispherical Surface Pit , 1981 .

[16]  A. Evans,et al.  Some Effects of Cavities on the Fracture of Ceramics: I, Cylindrical Cavities , 1979 .

[17]  G. I. Barenblatt.  THE MATHEMATICAL THEORY OF EQUILIBRIUM CRACKS IN BRITTLE FRACTURE , 1962 .