Synthesis and Properties of Bio-Based Composites from Vegetable Oils and Starch

Natural polymers, such as starch, and polymers derived from renewable resources, such as vegetable oils, have been considered as alternatives to petroleum-based plastics during recent decades, due to environmental concerns. Indeed, these materials can offer a variety of advantages, such as low cost, wide availability, carbon neutrality, elevated thermal stability, and easily tunable mechanical properties. However, some of these polymers alone exhibit poor mechanical properties, making them not suitable for some applications. Hence, the reinforcement of these bio-based polymers with other materials is often considered to overcome this challenge. In this work, thermosetting composites based on tung and linseed oil resins were prepared using starch as reinforcement. Analyses from Soxhlet extractions showed that the higher the concentration of tung oil in comparison to linseed oil in the resins, the lower the mass of unreacted material, leading to an optimum resin entirely based on tung oil. Dielectric analysis (DEA), differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA) indicated that the polymerization was completed in 3 h 20 min, at 140 °C, and that the composites were thermally stable until 270 °C. Finally, dynamic mechanical analysis (DMA) confirmed that the addition of starch to the resins increased the room temperature storage modulus (E′25) from 94 MPa to 893 MPa. Composites prepared with a resin formulation that did not contain a compatibilizer exhibited E′25 of 441 MPa. The composites investigated in this work are promising candidates for applications that require improved mechanical properties.

[1]  Zhuohong Yang,et al.  A novel polyfunctional polyurethane acrylate prepolymer derived from bio-based polyols for UV-curable coatings applications , 2022, Polymer Testing.

[2]  A. Taheri-Garavand,et al.  Starch-Polyvinyl Alcohol-Based Films Reinforced with Chitosan Nanoparticles: Physical, Mechanical, Structural, Thermal and Antimicrobial Properties , 2022, Applied Sciences.

[3]  Shitong Ren,et al.  Effect of crosslink structure on mechanical properties, thermal stability and flame retardancy of natural flavonoid based epoxy resins , 2021, European Polymer Journal.

[4]  Jianxin Jiang,et al.  Catalyst-free self-healing fully bio-based vitrimers derived from tung oil: Strong mechanical properties, shape memory, and recyclability , 2021 .

[5]  Zhuohong Yang,et al.  One-pot and solvent-free synthesis of castor oil-based polyurethane acrylate oligomers for UV-curable coatings applications , 2021 .

[6]  K. Mohana,et al.  Reduced graphene oxide-epoxidized linseed oil nanocomposite: A highly efficient bio-based anti-corrosion coating material for mild steel , 2021 .

[7]  Haibo Zhang,et al.  Synthesis and characterization of bio-based epoxy thermosets using rosin-based epoxy monomer , 2021, Iranian Polymer Journal.

[8]  K. Pal,et al.  Recent trends on bioplastics synthesis and characterizations: Polylactic acid (PLA) incorporated with tapioca starch for packaging applications , 2021 .

[9]  J. Ostrauskaite,et al.  Bio-Based Crosslinked Polymers Synthesized from Functionalized Soybean Oil and Squalene by Thiol–Ene UV Curing , 2021, Materials.

[10]  U. Bornscheuer,et al.  Fatty Acids and their Derivatives as Renewable Platform Molecules for the Chemical Industry , 2021, Angewandte Chemie.

[11]  A. Genua,et al.  Chemical and mechanical reprocessed resins and bio-composites based on five epoxidized vegetable oils thermosets reinforced with flax fibers or PLA woven , 2021 .

[12]  G. Gutiérrez-López,et al.  Preparation of surfactant-free emulsions using amaranth starch modified by reactive extrusion , 2021 .

[13]  A. Gandini,et al.  The Prospering of Macromolecular Materials Based on Plant Oils within the Blooming Field of Polymers from Renewable Resources † , 2020, Polymers.

[14]  V. Langlois,et al.  Fully Bio-Based Epoxy-Amine Thermosets Reinforced with Recycled Carbon Fibers as a Low Carbon-Footprint Composite Alternative , 2020, ACS Applied Polymer Materials.

[15]  Shuangying Wei,et al.  UV LED curable epoxy soybean-oil-based waterborne PUA resin for wood coatings , 2020 .

[16]  Qiangxian Wu,et al.  Preparation and Properties of Compatible Starch‐PCL Composites: Effects of the NCO Functionality in Compatibilizer , 2020 .

[17]  R. Quirino,et al.  Bio-Based Composites with Enhanced Matrix-Reinforcement Interactions from the Polymerization of α-Eleostearic Acid , 2019, Coatings.

[18]  Z. Hui,et al.  Enhancing hydrophobicity, strength and UV shielding capacity of starch film via novel co-cross-linking in neutral conditions , 2018, Royal Society Open Science.

[19]  R. Quirino,et al.  Vegetable Oils as a Chemical Platform , 2018 .

[20]  R. Quirino,et al.  Asolectin from soybeans as a natural compatibilizer for cellulose‐reinforced biocomposites from tung oil , 2015 .

[21]  T. Karthik,et al.  Characterization and analysis of ligno-cellulosic seed fiber from Pergularia Daemia plant for textile applications , 2013, Fibers and Polymers.

[22]  R. Larock,et al.  Oat Hull Composites from Conjugated Natural Oils , 2012 .

[23]  R. Larock,et al.  Soybean and linseed oil-based composites reinforced with wood flour and wood fibers , 2012 .

[24]  R. Larock,et al.  Rice hull biocomposites, part 2: Effect of the resin composition on the properties of the composite , 2011 .

[25]  R. Larock,et al.  Morphological and Thermal Characterization of Linseed-Oil Based Polymers from Cationic and Thermal Polymerization , 2010 .

[26]  R. Larock,et al.  Synthesis and Properties of Soy Hull-reinforced Biocomposites from Conjugated Soybean Oil , 2009 .

[27]  Yongshang Lu,et al.  Preparation and properties of tung oil-based composites using spent germ as a natural filler , 2008 .

[28]  Wolfgang Frenzel,et al.  An Investigation of the Fatty Acid Composition of New and Aged Tung Oil , 2006 .

[29]  P. Dole,et al.  Mechanical properties of starch‐based materials. I. Short review and complementary experimental analysis , 2005 .

[30]  R. Larock,et al.  Novel conjugated linseed oil-styrene-divinylbenzene copolymers prepared by thermal polymerization. 1. Effect of monomer concentration on the structure and properties. , 2005, Biomacromolecules.

[31]  X. Sun,et al.  Mechanical properties of poly(lactic acid)/starch composites compatibilized by maleic anhydride. , 2004, Biomacromolecules.

[32]  Chin-San Wu Performance of an acrylic acid grafted polycaprolactone/starch composite: Characterization and mechanical properties , 2003 .

[33]  Feng-kui Li,et al.  Synthesis, structure and properties of new tung oil-styrene-divinylbenzene copolymers prepared by thermal polymerization. , 2003, Biomacromolecules.

[34]  U. Ishiaku,et al.  Effect of starch predrying on the mechanical properties of starch/poly(ε‐caprolactone) composites , 2003 .

[35]  Hongdian Lu,et al.  Luteolin-based epoxy resin with exceptional heat resistance, mechanical and flame retardant properties , 2022 .