The conductivity of amorphous, monoclinic, and trigonal selenium has been measured at 300°K as a function of quasihydrostatic pressure up to 150 kbar. Amorphous and monoclinic samples after exposure to pressure above 120 kbar are transformed irreversibly to the trigonal modification. This result is confirmed by the direct observation of the corresponding shift of the absorption edge. Besides conductivity, for amorphous selenium the shift of absorption edge with pressure is investigated. The resulting pressure coefficient of the band gap is in good accordance with the value obtained from the pressure dependence of the conductivity with the assumption that intrinsic conduction predominates in amorphous selenium.
An amorphem, monoklinem und trigonalem Selen wurde die Leitfahigkeit in Abhangigkeit vom quasihydrostatischen Druck bis 150 kbar bei 300°K gemessen. Amorphe und monokline Proben wandeln sich nach Belastung mit Drucken oberhalb von etwa 120 kbar irreversibel in die trigonale Modifikation um, was auch durch die damit verbundene Verschiebung der Absorptionskante nachgewiesen werden konnte. Neben der Leitfahigkeit wurde an amorphem Selen die Verschiebung der Absorptionskante durch den Druck untersucht. Der sich hieraus ergebende Druckkoeffizient des Bandabstandes stimmt recht gut mit dem Wert uberein, der aus der Druckabhangigkeit der Leitfahigkeit unter der Annahme berechnet wurde, das bei amorphem Selen Eigenleitung vorliegt.
[1]
G. Connell,et al.
Is there an intimate relation between amorphous and crystalline semiconductors
,
1972
.
[2]
L. Cartz,et al.
High‐Pressure Phase Transformations in Hexagonal and Amorphous Selenium
,
1972
.
[3]
W. Fuhs.
Piezoresistivity of trigonal SexTe1−x single crystals
,
1971
.
[4]
W. Fuhs,et al.
Elastoresistivity of amorphous semiconductors
,
1970
.
[5]
W. Spear,et al.
Electronic transport properties of some low mobility solids under high pressure
,
1970
.
[6]
G. Lucovsky,et al.
The effects of valency on transport properties in vitreous binary alloys of selenium
,
1970
.
[7]
J. Stuke,et al.
Elektrische und optische Eigenschaften von amorphem Tellur
,
1965,
March 1.
[8]
J. Stuke.
Über den elektrischen Leitungsmechanismus von hexagonalen Selen-Einkristallen
,
1964,
August 1.
[9]
A. V. van Valkenburg,et al.
High Pressure Microscopy of the Silver and Cuprous Halides
,
1964,
Journal of research of the National Bureau of Standards. Section A, Physics and chemistry.
[10]
H. G. Drickamer,et al.
Effect of Pressure on the Resistance of Iodine and Selenium
,
1961
.
[11]
H. G. Drickamer,et al.
Effect of Pressure on the Absorption Edges of Certain Elements
,
1959
.