Failure mechanisms in composite panels subjected to underwater impulsive loads

This work examines the performance of composite panels when subjected to underwater impulsive loads. The scaled fluid-structure experimental methodology developed by Espinosa and co-workers was emp ...

[1]  Vikram Deshpande,et al.  One-dimensional response of sandwich plates to underwater shock loading , 2005 .

[2]  Zhenyu Xue,et al.  A comparative study of impulse-resistant metal sandwich plates , 2004 .

[3]  Adnan H. Nayfeh,et al.  Wave propagation in layered anisotropic media : with applications to composites , 1995 .

[4]  Zhenyu Xue,et al.  Metal sandwich plates optimized for pressure impulses , 2005, International Journal of Mechanical Sciences.

[5]  Zhenyu Xue,et al.  Preliminary assessment of sandwich plates subject to blast loads , 2003 .

[6]  Zvi Hashin,et al.  Analysis of cracked laminates: a variational approach , 1985 .

[7]  Sg Lim,et al.  Effect of transverse cracks on the thermomechanical properties of cross-ply laminated composites , 1989 .

[8]  P. Soden,et al.  Recommendations for designers and researchers resulting from the world-wide failure exercise , 2004 .

[9]  Reza Vaziri,et al.  Computational Modeling of Damage Development in Composite Laminates Subjected to Transverse Dynamic Loading , 2009 .

[10]  S. Dwivedi,et al.  Modeling impact induced delamination of woven fiber reinforced composites with contact/cohesive laws , 2000 .

[11]  K. Narasimhan,et al.  Deformation and fracture behaviour of plate specimens subjected to underwater explosion—a review , 2006 .

[12]  Z. Hashin.  Failure Criteria for Unidirectional Fiber Composites , 1980 .

[13]  P. Soden,et al.  Chapter 2.2 – Biaxial test results for strength and deformation of a range of E-glass and carbon fibre reinforced composite laminates: Failure exercise benchmark data , 2004 .

[14]  PERFORMANCE AND FAILURE OF METAL SANDWICH PLATES SUBJECTED TO SHOCK LOADING , 2007 .

[15]  D. Hall.  Examination of the effects of underwater blasts on sandwich composite structures , 1989 .

[16]  N. Fleck,et al.  The dynamic response of composite sandwich beams to transverse impact , 2007 .

[17]  Z. Hashin.  Analysis of stiffness reduction of cracked cross-ply laminates , 1986 .

[18]  Arun Shukla,et al.  Dynamic response and damage evolution in composite materials subjected to underwater explosive loading: An experimental and computational study , 2010 .

[19]  Maurizio Porfiri,et al.  A review of research on impulsive loading of marine composites , 2009 .

[20]  Douglas T. Queheillalt,et al.  DEFORMATION AND FRACTURE MODES OF SANDWICH STRUCTURES SUBJECTED TO UNDERWATER IMPULSIVE LOADS , 2007 .

[21]  Z. Hashin,et al.  A Fatigue Failure Criterion for Fiber Reinforced Materials , 1973 .

[22]  Adrian P. Mouritz,et al.  Review of advanced composite structures for naval ships and submarines , 2001 .

[23]  Pierre Ladevèze,et al.  An enhanced mesomodel for laminates based on micromechanics , 2002 .

[24]  Pierre Ladevèze,et al.  A Computational Damage Micromodel of Laminated Composites , 2005 .

[25]  Isaac M Daniel,et al.  Low velocity impact behavior of composite sandwich panels , 2005 .

[26]  David R Hayhurst,et al.  The response of metallic sandwich panels to water blast , 2007 .

[27]  R. Rajendran,et al.  Performance evaluation of HSLA steel subjected to underwater explosion , 2001 .

[28]  S. Jeelani,et al.  Low-velocity impact response of sandwich composites with nanophased foam core and biaxial (±45°) braided face sheets , 2009 .

[29]  Ramesh Talreja,et al.  A synergistic damage mechanics approach for composite laminates with matrix cracks in multiple orientations , 2009 .

[30]  J. B. Martin,et al.  Deformation of thin plates subjected to impulsive loading—a review Part II: Experimental studies , 1989 .

[31]  P. D. Soden,et al.  A COMPARISON OF THE PREDICTIVE CAPABILITIES OF CURRENT FAILURE THEORIES FOR COMPOSITE LAMINATES , 1998 .

[32]  Sarah E. Mouring,et al.  Modelling impact damage in marine composite panels , 2009 .

[33]  Srinivasan Arjun Tekalur,et al.  Ballistic Resistance of 2D and 3D Woven Sandwich Composites , 2007 .

[34]  Vikram Deshpande,et al.  Underwater blast loading of sandwich beams: Regimes of behaviour , 2009 .

[35]  G. Nurick,et al.  The deformation and tearing of thin square plates subjected to impulsive loads—An experimental study , 1996 .

[36]  P. D. Soden,et al.  Biaxial test results for strength and deformation of a range of E-glass and carbon fibre reinforced composite laminates: failure exercise benchmark data , 2002 .

[37]  Isaac M Daniel,et al.  Engineering Mechanics of Composite Materials , 1994 .

[38]  Michelle S. Hoo Fatt,et al.  Analytical Modeling of Composite Sandwich Panels under Blast Loads , 2009 .

[39]  Horacio Dante Espinosa,et al.  Deformation and Failure Modes of I-Core Sandwich Structures Subjected to Underwater Impulsive Loads , 2009 .

[40]  H. Schürmann,et al.  FAILURE ANALYSIS OF FRP LAMINATES BY MEANS OF PHYSICALLY BASED PHENOMENOLOGICAL MODELS , 1998 .

[41]  Performance of composite panels subjected to impulsive loading , 2009 .

[42]  P. D. Soden,et al.  A COMPARISON OF THE PREDICTIVE CAPABILITIES OF CURRENT FAILURE THEORIES FOR COMPOSITE LAMINATES, JUDGED AGAINST EXPERIMENTAL EVIDENCE , 2002 .

[43]  S. Jeelani,et al.  Processing of nanoclay filled sandwich composites and their response to low-velocity impact loading , 2008 .

[44]  M. Z. Shah Khan,et al.  Non-destructive detection of fatigue damage in thick composites by pulse-echo ultrasonics , 2000 .

[45]  A. Evans,et al.  The mechanics of matrix cracking in brittle-matrix fiber composites , 1985 .

[46]  Serge Abrate,et al.  Matrix cracking in laminated composites: A review , 1991 .

[47]  P. Soden,et al.  Recommendations for designers and researchers resulting from the world-wide failure exercise , 2003 .

[48]  Arun Shukla,et al.  Mechanical behavior and damage evolution in E-glass vinyl ester and carbon composites subjected to static and blast loads , 2008 .

[49]  Brian Hayman,et al.  Damage tolerance assessment of composite sandwich panels with localised damage , 2005 .

[50]  G. Nurick,et al.  The deformation and tearing of thin circular plates subjected to impulsive loads , 1990 .

[51]  Horacio Dante Espinosa,et al.  A Novel Fluid Structure Interaction Experiment to Investigate Deformation of Structural Elements Subjected to Impulsive Loading , 2006 .

[52]  Vikram Deshpande,et al.  Dynamic compression of metallic sandwich structures during planar impulsive loading in water , 2010 .