Influence of defects on fatigue crack propagation in laser hybrid welded eccentric fillet joint

Fatigue cracking of laser hybrid welded eccentric fillet joints has been studied for stainless steel. Two-dimensional linear elastic fracture mechanics analysis was carried out for this joint geometry for four point bending load. The numerical simulations explain for the experimental observations why the crack propagates from the lower weld toe and why the crack gradually bends towards the root. Lack of fusion turned out to be uncritical for the initiation of cracks due to its compressive stress conditions. The linear elastic fracture mechanics analysis has demonstrated in good qualitative agreement with fatigue test results that lack of fusion slightly (<10%) reduces the fatigue life by accelerating the crack propagation. For the geometrical conditions studied here improved understanding of the crack propagation was obtained and in turn illustrated. The elaborated design curves turned out to be above the standard recommendations.

[1]  H. W. Kerr,et al.  Fatigue crack initiation from defects at weld toes in steel , 1989 .

[2]  C. M. Sonsino,et al.  Fatigue crack initiation and growth in AlMg4.5Mn butt weldments , 2001 .

[3]  Gregory J. Hancock,et al.  Fracture toughness of G550 sheet steels subjected to tension , 2001 .

[4]  Ali Fatemi,et al.  Cumulative fatigue damage and life prediction theories: a survey of the state of the art for homogeneous materials , 1998 .

[5]  Fatigue behavior of butt welded joints containing inclined lack-of-penetration. , 2001 .

[6]  T. R. Gurney.  Cumulative Damage of Welded Joints , 2006 .

[7]  J. M. Alegre,et al.  A finite element simulation methodology of the fatigue behaviour of punched and drilled plate components , 2004 .

[8]  Y. Verreman,et al.  SHORT CRACK GROWTH AND COALESCENCE ALONG THE TOE OF A MANUAL FILLET WELD , 1991 .

[9]  G. Degallaix,et al.  MICROSTRUCTURAL EFFECTS ON SHORT FATIGUE CRACK INITIATION AND PROPAGATION IN HIGH STRENGTH STEEL BUTT WELDED JOINTS , 1998 .

[10]  G. Sih.  Strain-energy-density factor applied to mixed mode crack problems , 1974 .

[11]  Kevin Z. Truman,et al.  An evaluation of fracture mechanics quarter-point displacement techniques used for computing stress intensity factors , 1999 .

[12]  S. Atluri,et al.  CALCULATION OF FRACTURE MECHANICS PARAMETERS FOR AN ARBITRARY THREE-DIMENSIONAL CRACK, BY THE ‘EQUIVALENT DOMAIN INTEGRAL’ METHOD , 1987 .

[13]  G. Rihar,et al.  Lack of Fusion Characterisation of Indications , 2006 .

[14]  Gerd Heber,et al.  Three-dimensional, parallel, finite element simulation of fatigue crack growth in a spiral bevel pinion gear , 2005 .

[15]  A study of fatigue crack growth and crack closure in mechanical heterogeneous welded joints , 1996 .

[16]  F. Erdogan,et al.  On the Crack Extension in Plates Under Plane Loading and Transverse Shear , 1963 .

[17]  Paul A. Wawrzynek,et al.  Quasi-automatic simulation of crack propagation for 2D LEFM problems , 1996 .

[18]  Paris,et al.  FRACTURE MECHANICS AND FATIGUE: A HISTORICAL PERSPECTIVE , 2008 .

[19]  Liuhe Li,et al.  Influence of weld mis-matching on fatigue crack growth behaviors of electron beam welded joints , 2002 .

[20]  A. F. Hobbacher,et al.  Fatigue design of welded joints and components , 1996 .

[21]  Zuheir Barsoum,et al.  Residual Stress Analysis and Fatigue Assessment of Welded Steel Structures , 2008 .

[22]  I. Raju.  Calculation of strain-energy release rates with higher order and singular finite elements , 1987 .

[23]  C. Q. Lee,et al.  Effect of weld geometry on the fatigue life of non-load-carrying fillet welded cruciform joints , 2009 .

[24]  Ji Hyun Kim,et al.  Fracture behavior of heat-affected zone in low alloy steels , 2001 .

[25]  M. German,et al.  Crack extension modeling with singular quadratic isoparametric elements , 1976 .

[26]  Hans-Åke Häggblad,et al.  The influence of surface geometry and topography on the fatigue cracking behaviour of laser hybrid welded eccentric fillet joints , 2010 .

[27]  Ahmad Kamal Ariffin,et al.  Finite element simulation of stress intensity factors in elastic-plastic crack growth , 2006 .

[28]  M. Kanninen,et al.  A finite element calculation of stress intensity factors by a modified crack closure integral , 1977 .

[29]  Hussain,et al.  Strain Energy Release Rate for a Crack Under Combined Mode I and Mode II , 1974 .

[30]  Hans Albert Richard,et al.  Fatigue crack propagation in the frame of a hydraulic press , 2008, CP 2013.

[31]  Johan Martinsson.  Fatigue Assessment of a Welded Component in a Construction Machinery Based on Different Methods , 2002 .

[32]  K. Nilsson,et al.  Influence of joint geometry and fit-up gaps on hybrid laser-metal active gas (MAG) welding , 2006 .

[33]  J. F. Porter,et al.  Fatigue crack initiation and growth in A517 submerged arc welds under variable amplitude loading , 2000 .