Durability of cementitious binder derived from industrial wastes

The durability of cementitious binder hydrated at 27°C and 50°C under high humidity was examined by alternate wetting and drying, as well as heating and cooling, cycles at temperatures ranging from 27°C to 60°C and by performance in water. The results show that cementitious binder hardened at 50°C possesses higher water resistance and lower porosity than the binder hardened at 27°C. A decrease in the strength of the cementitious binder was observed with an increase in temperature and in the wetting and drying and heating and cooling cycles. The maximum decrease in strength occurred at 60°C. The cementitious binder cured at 27°C showed a much smaller decrease in strength with a rise in temperature and in weathering cycles. The changes in strength of the cementitious binder were monitored by differential thermal analysis and microscopy.RésuméOn a examiné la durabilité des matériaux liants hydratés à 27°C et à 50°C sous haute humidité, au moyen de cycles alternés d'humidification/dessiccation, ainsi que des cycles de chauffage/refroidissement, à des températures allant de 27°C à 60°C. Leur performance dans l'eau a également été évaluée. Les résultats montrent qu'un liant durci à 50°C possède une meilleure résistance à l'eau et une plus faible porosité qu'un liant durci à 27°C. Une chute de la résistance du liant a été observée avec l'accroissement de la température et des cycles humidification/dessiccation et chauffage/refroidissement. La perte de résistance maximale a été atteinte à 60°C. Le liant durci à 27°C montre une plus faible perte de résistance avec l'accroissement de la température et les cycles de vieillissement. Les changements de la résistance du liant ont été contrôlés par des analyses thermiques différentielles et microscopiques.