Single and multiple shot near-infrared femtosecond laser pulse ablation thresholds of copper

The single-shot ablation threshold and incubation coefficient of copper were investigated using an amplified near-infrared, femtosecond Ti:sapphire laser. To date, the near-infrared femtosecond ablation threshold of copper has been reported in the range of several hundred millijoules per cm2 based primarily on multiple shot ablation studies. A careful study of the single shot ablation threshold for copper was carried out yielding an incident single-shot ablation threshold of (1.06±0.12) J/cm2 for a clean copper foil surface. This was determined by measuring the diameters of the ablation spots as a function of the laser pulse energy using scanning electron microscopy for spatially Gaussian laser spots. When multiple shots were taken on the same spot, a reduction in ablation threshold was observed, consistent with a multiple shot incubation coefficient of 0.76±0.02. Similar experiments on 250 nm and 500 nm copper thin films sputtered on a silicon substrate demonstrated that scaling the threshold values with the absorbance of energy at the surface yields a consistent absorbed fluence threshold for copper of (59±10) mJ/cm2. This absorbed threshold value is consistent with the expected value from a two-temperature model for the heating of copper with an electron-lattice coupling constant of g=1017 Wm-3 K-1. Single-shot rippling of the surface in the threshold ablation intensity regime was also observed for the foil target but not for the smooth thin film target.

[1]  Yongfeng Lu,et al.  Audible acoustic wave real-time monitoring in laser processing of microelectronic materials , 1997, Other Conferences.

[2]  C. Li,et al.  Micromachining with femtosecond 250-nm laser pulses , 2000 .

[3]  J. Liu.  Simple technique for measurements of pulsed Gaussian-beam spot sizes. , 1982, Optics letters.

[4]  J. Güdde,et al.  Electron and lattice dynamics following optical excitation of metals , 2000 .

[5]  R. Fedosejevs,et al.  Absorption of subpicosecond ultraviolet laser pulses in high-density plasma , 1990 .

[6]  Michael F. Becker,et al.  Laser-induced damage on single-crystal metal surfaces , 1988 .

[7]  Salvatore Amoruso,et al.  Thermal and nonthermal ion emission during high-fluence femtosecond laser ablation of metallic targets , 2000 .

[8]  S. Amoruso,et al.  Double-peak distribution of electron and ion emission profile during femtosecond laser ablation of metals , 2002 .

[9]  Ferenc Krausz,et al.  Photoablation with sub-10 fs laser pulses , 2000 .

[10]  Boris N. Chichkov,et al.  Precise laser ablation with ultrashort pulses , 1997 .

[11]  Minoru Obara,et al.  Ablation characteristics of Au, Ag, and Cu metals using a femtosecond Ti:sapphire laser , 1999 .

[12]  Brunel,et al.  Thermal response of metals to ultrashort-pulse laser excitation. , 1988, Physical review letters.

[13]  J. Forsyth,et al.  Bright-field microscopy of semitransparent objects. , 1988, Journal of the Optical Society of America. A, Optics and image science.

[14]  Norris,et al.  Time-resolved observation of electron-phonon relaxation in copper. , 1987, Physical review letters.

[15]  Jeff F. Young,et al.  Laser-induced periodic surface structure. II. Experiments on Ge, Si, Al, and brass , 1983 .

[16]  M. Hong,et al.  Electric signal detection at the early stage of laser ablation in air , 1999 .

[17]  Juergen Jandeleit,et al.  Picosecond laser ablation of thin copper films , 1996 .

[18]  M. Stuke,et al.  Sub-picosecond UV laser ablation of metals , 1995 .

[19]  Boris N. Chichkov,et al.  Ablation of metals by ultrashort laser pulses , 1997 .

[20]  J. Meyer-ter-Vehn,et al.  Hydrodynamic simulation of subpicosecond laser interaction with solid-density matter , 2000, Physical review. E, Statistical physics, plasmas, fluids, and related interdisciplinary topics.