Experimental Characterization of a Direct Metal Deposited Cobalt-Based Alloy on Tool Steel for Component Repair

Casting dies made of tool steel are subject to impact, abrasion, and cyclic thermo-mechanical loading that can result in damage such as wear, corrosion, and cracking. To repair these defects, materials enveloping the defects need to be machined off and then refilled. In this study, V-shaped defects with varied sidewall inclination angles were prepared on H13 tool steel substrates and refilled with a cobalt-based alloy using direct metal deposition process (DMD) for superior hardness and wear resistance. The microstructure of rebuilt samples was characterized using an optical microscope (OM) and scanning electron microscope (SEM). Elemental distribution from the substrate to deposits was analyzed using energy-dispersive spectrometry (EDS). The mechanical properties of repaired samples were evaluated by tensile testing and microhardness measurement. A fracture mechanism in tensile testing was analyzed by observing the fracture surface. The experimental result reveals that V-shaped defects with sidewall beyond certain angles can be successfully remanufactured. The deposits were fully dense and free of defects. The microstructure and tensile testing confirm the solid bonding along the interface. The tensile testing shows the average ultimate tensile strength (UTS) of the repaired samples is approximately 620 MPa, where samples fractured at the deposits region. The hardness measurement reveals the hardness of deposits is around 800 HV, which is much higher than the hardness of the substrate.

[1]  Yong-qiang Yang,et al.  Microstructure evolution of laser clad layers of W–C–Co alloy powders , 2000 .

[2]  Neil Hopkinson,et al.  Rapid prototyping for direct manufacture , 2001 .

[3]  K. Osakada,et al.  Rapid Manufacturing of Metal Components by Laser Forming , 2006 .

[4]  W. Wang,et al.  Component repair using laser direct metal deposition , 2007 .

[5]  E. Toyserkani,et al.  Cladding of WC–12 Co on low carbon steel using a pulsed Nd:YAG laser , 2007 .

[6]  J. Hosson,et al.  Thick Co-based coating on cast iron by side laser cladding: Analysis of processing conditions and coating properties , 2007 .

[7]  Frank W. Liou,et al.  Applications of a hybrid manufacturing process for fabrication of metallic structures , 2007 .

[8]  J. C. Alvarez,et al.  Laser cladding of tungsten carbides (Spherotene®) hardfacing alloys for the mining and mineral industry , 2009 .

[9]  J. Mazumder,et al.  Laser aided direct metal deposition of Inconel 625 superalloy: Microstructural evolution and thermal stability , 2009 .

[10]  B. Laget,et al.  Potential of direct metal deposition technology for manufacturing thick functionally graded coatings and parts for reactors components , 2009 .

[11]  B. Graf,et al.  Laser Metal Deposition as Repair Technology for Stainless Steel and Titanium Alloys , 2012 .

[12]  L. Xue,et al.  Laser Cladding of CPM Tool Steels on Hardened H13 Hot-Work Steel for Low-Cost High-Performance Automotive Tooling , 2012 .

[13]  M. Shukla,et al.  Scanning velocity influence on microstructure, microhardness and wear resistance performance of laser deposited Ti6Al4V/TiC composite , 2013 .

[14]  S. Wang,et al.  Characterization of stainless steel parts by Laser Metal Deposition Shaping , 2014 .

[15]  A. Mertens,et al.  Laser cladding as repair technology for Ti–6Al–4V alloy: Influence of building strategy on microstructure and hardness , 2015 .

[16]  N. Janssen,et al.  Additive Manufacturing of High-Entropy Alloys by Laser Processing , 2016 .

[17]  Yaoyu Ding,et al.  Feasibility Study on 3-D Printing of Metallic Structural Materials with Robotized Laser-Based Metal Additive Manufacturing , 2016 .

[18]  B. Graf,et al.  Laser Metal Deposition as Repair Technology for a Gas Turbine Burner Made of Inconel 718 , 2016 .

[19]  F. Liou,et al.  A Smooth Toolpath Generation Method for Laser Metal Deposition , 2016 .

[20]  F. Liou,et al.  Metallic Components Repair Strategies using the Hybrid Manufacturing Process , 2017 .

[21]  F. Weng,et al.  Effect of process parameters on the microstructure evolution and wear property of the laser cladding coatings on Ti-6Al-4V alloy , 2017 .

[22]  F. Liou,et al.  Effect of optimizing particle size on directed energy deposition of Functionally Graded Material with blown Pre-Mixed Multi-Powder , 2017 .

[23]  Pengfei Li,et al.  Joining of Sip/6063Al composite using additive manufacturing-based laser melting deposition , 2017 .

[24]  F. Liou,et al.  Directed energy depositing a new Fe-Cr-Ni alloy with gradually changing composition with elemental powder mixes and particle size’ effect in fabrication process , 2018 .

[25]  P. Suresh Babu,et al.  Thermally-Sprayed WC-Based Cermet Coatings for Corrosion Resistance Applications , 2018, JOM.

[26]  Wei Li,et al.  Damage reconstruction from tri-dexel data for laser-aided repairing of metallic components , 2018 .

[27]  Wei Li,et al.  Damage detection and reconstruction algorithm in repairing compressor blade by direct metal deposition , 2018 .

[28]  Modeling analysis of argon gas flow rate’s effect on pre-mixed powder separation in laser metal deposition process and experimental validation , 2018 .

[29]  F. Liou,et al.  Additive manufacturing of a new Fe-Cr-Ni alloy with gradually changing compositions with elemental powder mixes and thermodynamic calculation , 2018 .

[30]  Yang Tong,et al.  Additive Manufacturing of High-Entropy Alloys: A Review , 2018, Entropy.

[31]  F. Liou,et al.  Evaluation of component repair using direct metal deposition from scanned data , 2018 .

[32]  F. Liou,et al.  Modeling of worn surface geometry for engine blade repair using Laser-aided Direct Metal Deposition process , 2018 .