Microstructure and Mechanical Properties of Medium-Carbon Si-Rich Steel Processed by Austempering after Intercritical Annealing

In the present paper, the medium-C Si-rich steel with a quenched martensite microstructure was heated to intercritical annealing temperatures at 750 °C, 760 °C and 770 °C after warm rolling deformation to obtain ferrite with varying volume fractions. Subsequently, bainite/ferrite multiphase microstructures were attained via austempering near Ms temperature. The microstructures of the test steel after different heat treatments were characterized by scanning electron microscopy, transmission electron microscopy and electron backscatter diffraction, and corresponding tensile and impact properties were tested. The results showed that, with the increase of intercritical annealing temperature, the austenite content increased, which limited the growth of ferrite grains, and the grain size decreased from ~1.6 μm to ~1.4 μm. In addition, the degree of ferrite recrystallization was almost complete. At the same intercritical annealing temperature, compared with austempering above Ms, prior athermal martensite (PAM) was obtained after austempering below Ms, which effectively refined the size of bainite ferrite lath. Moreover, with the increase of intercritical annealing temperature, the bainite content of the test steel increased after austempering, resulting in the increase of yield strength, tensile strength and impact energy. In contrast, while the decrease in ferrite content led to a significant decrease in uniform elongation. At constant intercritical annealing temperature, the tensile strength decreased slightly, and the impact property improved after austempering above Ms.

[1]  L. Wang,et al.  Microstructure and Mechanical Properties of Low- and Medium-Carbon Si-Rich Low-Alloy Steels Processed by Austemping after Intercritical Annealing , 2022, Materials.

[2]  Fucheng Zhang,et al.  Introducing ultrafine ferrite in low-temperature bainitic steel through a novel process for simultaneously improving strength and toughness , 2021, Journal of Materials Research and Technology.

[3]  Fucheng Zhang,et al.  Strain-hardening behavior and mechanisms of a lamellar-structured low-alloy TRIP steel , 2021, Materials Science and Engineering: A.

[4]  Fucheng Zhang,et al.  Simultaneously Improved Strength and Impact Toughness by Introducing Ultrafine Ferrite in Low-Temperature Bainitic Steel , 2021 .

[5]  Xiang Wang,et al.  Transformation kinetics of carbide-free bainitic steels during isothermal holding above and below MS , 2020 .

[6]  Y. Mazaheri,et al.  Correlation of ferrite and martensite micromechanical behavior with mechanical properties of ultrafine grained dual phase steels , 2019, Materials Science and Engineering: A.

[7]  Y. Mazaheri,et al.  High strength-elongation balance in ultrafine grained ferrite-martensite dual phase steels developed by thermomechanical processing , 2019, Materials Science and Engineering: A.

[8]  Fucheng Zhang,et al.  Effects of austempering temperature on bainitic microstructure and mechanical properties of a high-C high-Si steel , 2019, Materials Science and Engineering: A.

[9]  J. Sietsma,et al.  Influence of the prior athermal martensite on the mechanical response of advanced bainitic steel , 2018, Materials Science and Engineering: A.

[10]  B. M. Gurumurthy,et al.  Effect of preheat treatment structure On mechanical characterization of aisi 4340 ferrite bainite dual phase steel , 2018 .

[11]  Yanhui Wang,et al.  Extremely high strength achievement in medium-C nanobainite steel , 2018, Scripta Materialia.

[12]  Ahmed A. Saleh,et al.  Strain-induced ferrite formation and its effect on mechanical properties of a dual phase steel produced using laboratory simulated strip casting , 2017 .

[13]  Fucheng Zhang,et al.  Below-Ms austempering to obtain refined bainitic structure and enhanced mechanical properties in low-C high-Si/Al steels , 2016 .

[14]  A. Kermanpur,et al.  A novel route for development of ultrahigh strength dual phase steels , 2014 .

[15]  O. Bouaziz,et al.  The influence of microstructure and composition on the plastic behaviour of dual-phase steels , 2014 .

[16]  J. D. Boyd,et al.  Development and characterisation of model TRIP steel microstructures , 2013 .

[17]  J. D. Boyd,et al.  Effect of microstructure on retained austenite stability and work hardening of TRIP steels , 2011 .

[18]  R. Bakhtiari,et al.  The effect of bainite morphology on the mechanical properties of a high bainite dual phase (HBDP) steel , 2009 .

[19]  N. Saeidi,et al.  Comparison of mechanical properties of martensite/ferrite and bainite/ferrite dual phase 4340 steels , 2009 .

[20]  Francisca García Caballero,et al.  Ultra-high-strength Bainitic Steels , 2005 .

[21]  H. Bhadeshia,et al.  Mechanical Properties of Low-Temperature Bainite , 2005 .

[22]  W. Poole,et al.  Austenite formation during intercritical annealing , 2004 .

[23]  D. Matlock,et al.  Quantitative measurement of deformation-induced martensite in 304 stainless steel by X-ray diffraction , 2004 .

[24]  H. Bhadeshia,et al.  Very strong bainite , 2004 .

[25]  H. Bhadeshia,et al.  Acceleration of Low-temperature Bainite , 2003 .

[26]  H. Bhadeshia,et al.  Development of Hard Bainite , 2003 .

[27]  E. Werner,et al.  An unexpected feature of the stress–strain diagram of dual-phase steel , 2002 .

[28]  Francisca García Caballero,et al.  Very strong low temperature bainite , 2002 .

[29]  O. Bouaziz,et al.  Physical modelling of microstructure and mechanical properties of dual-phase steel , 2001 .

[30]  R. Priestner,et al.  Influence of ferrite-martensite microstructural morphology on tensile properties of dual-phase steel , 1996, Journal of Materials Science.

[31]  H. Bhadeshia,et al.  Austenite films in bainitic microstructures , 1995 .

[32]  Zhonghao Jiang,et al.  Effects of microstructural variables on the deformation behaviour of dual-phase steel , 1995 .

[33]  Fucheng Zhang,et al.  Roles of pre-formed martensite in below-Ms bainite formation, microstructure, strain partitioning and impact absorption energies of low-carbon bainitic steel , 2022 .