Lighting applications like OLED or on silicon for electro-optical applications need a reproducible sealing process. The joining has to be strong, the permeability for gasses and humidity very low and the process itself has to be very localized not affecting any organic or electronic parts inside the sealed region. The actual sealing process using glue does not fulfil these industrial needs. A new joining process using ultra-fast laser radiation offers a very precise joining with geometry dimensions smaller than 50 μm. Ultra-fast laser radiation is absorbed by multi-photon absorption in the glass. Due to the very definite threshold for melting and ablation the process of localized heating can be controlled without cracking. Repeating the irradiation at times smaller than the heat diffusion time the temperature in the focus is increased by heat accumulation reaching melting of the glass. Mowing the substrate relatively to the laser beam generates a seal of re-solidified glass. Joining of glass is achieved by positioning the laser focus at the interface. A similar approach is used for glass-silicon joining. The investigations presented will demonstrate the joining geometry by microscopy of cross-sections achieved by welding two glass plates (Schott D263 and AF45) with focused IR femtosecond laser radiation (wavelength λ = 1045nm, repetition rate f = 1 MHz, pulse duration tp = 500 fs, focus diameter w0 = 4 μm, feeding velocity v= 1-10 mm/s). The strength of the welding seam is measured by tensile stress measurements and the gas and humidity is detected. A new diagnostic method for the on-line detection of the welding seam properties will be presented. Using a non-interferometric technique by quantitative phase microscopy the refractive index is measured during welding of glass in the time regime 0-2 μs. By calibration of the measured refractive index with a relation between refractive index and temperature a online-temperature detection can be achieved.
[1]
K. Itoh,et al.
Direct joining of glass substrates by 1 kHz femtosecond laser pulses
,
2007
.
[2]
J. Nishii,et al.
Space-selective laser joining of dissimilar transparent materials using femtosecond laser pulses
,
2006
.
[3]
Dirk Wortmann,et al.
Refractive index modification using fs-laser double pulses.
,
2007,
Optics express.
[4]
I. Miyamoto,et al.
Ultra-fast Diagnostics of Laser-induced Melting of Matter in ns to µs Time-scales
,
2006
.
[5]
K. Itoh,et al.
Laser micro-welding of transparent materials by a localized heat accumulation effect using a femtosecond fiber laser at 1558 nm.
,
2006,
Optics express.
[6]
J. Gottmann,et al.
Local Melting of Glass Material and Its Application to Direct Fusion Welding by Ps-laser Pulses
,
2007
.
[7]
J. Nishii,et al.
Welding of Transparent Materials Using Femtosecond Laser Pulses
,
2005
.
[8]
W. Kern.
The Evolution of Silicon Wafer Cleaning Technology
,
1990
.
[9]
E. Mazur,et al.
Bulk heating of transparent materials using a high-repetition-rate femtosecond laser
,
2003
.