Hot‐Pressing of Si3N4 with Y2O3 and Li2O as Additives

The rates of densification and phase transformation undergone by α-Si3N4 during hot-pressing in the presence of Y2O3, Y2O3−2SiO2, and Li20−2Si02 as additives were studied. Although these systems behave less simply than MgO-doped Si3N4, the data can be interpreted during the early stages of hot-pressing as resulting from a solution-diffusion-reprecipitation mechanism, where the diffusion step is rate controlling and where the reprecipitation step invariably results in the formation of the β-Si3N4 phase.