Detection of fibre fracture and ply fragmentation in thin-ply UD carbon/glass hybrid laminates using acoustic emission

This paper investigates the link between acoustic emission (AE) events and the corresponding damage modes in thin-ply UD carbon/glass hybrid laminates under tensile loading. A novel configuration was investigated which has not previously been studied by AE, where the laminates were fabricated by embedding thin carbon plies between standard thickness translucent glass plies to produce progressive fragmentation of the carbon layer and delamination of the carbon/glass interface. A criterion based on amplitude and energy of the AE event values was established to identify the fragmentation failure mode. Since the glass layer was translucent, it was possible to quantitatively correlate the observed fragmentation during the tests and the AE events with high amplitude and energy values. This new method can be used as a simple and advanced tool to identify fibre fracture as well as estimate the number and sequence of damage events that are not visible e.g. in hybrid laminates with thick or non-transparent layers as well as when the damage is too small to be visually detected.

[1]  M. Ahmadi,et al.  Monitoring the initiation and growth of delamination in composite materials using acoustic emission under quasi-static three-point bending test , 2011 .

[2]  S. Ramakrishna,et al.  Influence of electrospun Nylon 6,6 nanofibrous mats on the interlaminar properties of Gr–epoxy composite laminates , 2012 .

[3]  L. Gorbatikh,et al.  Stress concentrations in hybrid unidirectional fibre-reinforced composites with random fibre packings , 2012 .

[4]  J. Summerscales,et al.  Carbon fibre and glass fibre hybrid reinforced plastics , 1978 .

[5]  Mohamad Fotouhi,et al.  Acoustic emission-based study to characterize the initiation of delamination in composite materials , 2016 .

[6]  Thomas Monnier,et al.  Non-destructive evaluation of damage and failure of fibre reinforced polymer composites using ultrasonic waves and acoustic emission , 2001 .

[7]  J. Aveston,et al.  Synergistic fibre strengthening in hybrid composites , 1976 .

[8]  G. Chollon,et al.  Microstructure and mechanical properties of coal tar pitch-based 2D-C/C composites with a filler addition , 2001 .

[9]  M. Pharaoh,et al.  Identification of failure modes in glass/polypropylene composites by means of the primary frequency content of the acoustic emission event , 2004 .

[10]  Rhys Pullin,et al.  Classification of acoustic emission data from buckling test of carbon fibre panel using unsupervised clustering techniques , 2015 .

[11]  Ramin Khamedi,et al.  Damage Classification of Sandwich Composites Using Acoustic Emission Technique and k-means Genetic Algorithm , 2014 .

[12]  Michael R Wisnom,et al.  Damage analysis of pseudo-ductile thin-ply UD hybrid composites - A new analytical method , 2015 .

[13]  Michael R Wisnom,et al.  Design and characterisation of advanced pseudo-ductile unidirectional thin-ply carbon/epoxy-glass/epoxy hybrid composites , 2016 .

[14]  M. Wisnom,et al.  Parametric study of failure mechanisms and optimal configurations of pseudo-ductile thin-ply UD hybrid composites , 2015 .

[15]  L. Gorbatikh,et al.  Hybrid effects in thin ply carbon/glass unidirectional laminates: Accurate experimental determination and prediction , 2016 .

[16]  Nak-Sam Choi,et al.  Analysis of fracture process in single-edge-notched laminated composites based on the high amplitude acoustic emission events , 2007 .

[17]  M. G. Bader,et al.  The strength of hybrid glass/carbon fibre composites , 1981 .

[18]  Stepan Vladimirovitch Lomov,et al.  Correlation of acoustic emission with optically observed damage in a glass/epoxy woven laminate under tensile loading , 2015 .

[19]  Nathalie Godin,et al.  Clustering of acoustic emission signals collected during tensile tests on unidirectional glass/polyester composite using supervised and unsupervised classifiers , 2004 .

[20]  Michael R Wisnom,et al.  Demonstration of pseudo-ductility in high performance glass-epoxy composites by hybridisation with thin-ply carbon prepreg , 2013 .

[21]  H. Heidary,et al.  Residual tensile strength monitoring of drilled composite materials by acoustic emission , 2012 .

[22]  Nathalie Godin,et al.  Integration of the Kohonen's self-organising map and k-means algorithm for the segmentation of the AE data collected during tensile tests on cross-ply composites , 2005 .

[23]  G. Minak,et al.  Investigation of the damage mechanisms for mode I delamination growth in foam core sandwich composites using acoustic emission , 2015 .

[24]  Carlo Santulli,et al.  Failure modes characterization of impacted carbon fibre reinforced plastics laminates under compression loading using acoustic emission , 2014 .

[25]  M. Benzeggagh,et al.  Initiation and growth of delamination in glass/epoxy composites subjected to static and dynamic loading by acoustic emission monitoring , 1999 .

[26]  Jonathan D Fuller,et al.  Combining fibre rotation and fragmentation to achieve pseudo-ductile CFRP laminates , 2016 .

[27]  Yentl Swolfs,et al.  Fibre hybridisation in polymer composites: a review , 2014 .

[28]  Mohamad Fotouhi,et al.  Investigation of the mixed-mode delamination in polymer-matrix composites using acoustic emission technique , 2014 .

[29]  M. Benzeggagh,et al.  On the use of acoustic emission to investigate damage mechanisms in glass-fibre-reinforced polypropylene , 1994 .

[30]  Andrea Zucchelli,et al.  Low-velocity impact on carbon/epoxy tubes subjected to torque - Experimental results, analytical models and FEM analysis , 2010 .

[31]  Mohamad Fotouhi,et al.  Acoustic emission-based damage classification of glass/polyester composites using harmony search k-means algorithm , 2012 .

[32]  B. Harris,et al.  Hybrid carbon and glass fibre composites , 1974 .

[33]  G. Chollon,et al.  Microstructural and mechanical properties of filler-added coal-tar pitch-based C/C composites: the damage and fracture process in correlation with AE waveform parameters , 2000 .

[34]  M. Ahmadi,et al.  Analysis of the damage mechanisms in mixed-mode delamination of laminated composites using acoustic emission data clustering , 2017 .

[35]  H. Dhakal,et al.  Effect of temperature and hybridisation on the low velocity impact behavior of hemp-basalt/epoxy composites , 2015 .

[36]  I. Verpoest,et al.  A comparative study of tensile properties of non-crimp 3D orthogonal weave and multi-layer plain weave E-glass composites. Part 1: Materials, methods and principal results , 2009 .

[37]  Jürgen Bohse,et al.  Acoustic emission characteristics of micro-failure processes in polymer blends and composites , 2000 .

[38]  M. Wisnom,et al.  Numerical modelling of the damage modes in UD thin carbon/glass hybrid laminates , 2014 .