Influence of alkaline (Na, K) vapors on carbon and mineral behavior in blast furnace cokes

Abstract A series of adsorption–alkalization experiments were conducted in a muffle furnace on two types of blast furnace cokes at 1300 °C in the presence of alkali vapors. Coke textures were found to peel off layer by layer after the alkalization process by potassium vapor, and macro fissures were observed for K/Coke ratios higher than 3/100. This phenomenon was not observed in the coke samples alkalized by sodium vapor. A number of additional potassium-bearing and sodium-bearing phases were detected with scanning electron microscope and energy dispersive spectrometer after the alkalization process. The formation of kalsilite or potassium aluminum silicate (KAlSiO 4 ) and sodium alumina silicates (Na 6 Al 4 Si 4 O 17 ) was confirmed through X-ray diffraction, however the formation of intercalation compounds that were expected to form in the alkalized coke samples could not be confirmed. The catalytic effect of sodium and potassium-bearing minerals appeared to be quite similar; the degradation of coke strength by sodium was however found to be stronger than that caused by potassium. The severe degradation of coke quality caused by alkali vapors was attributed to their strong influence on the coke carbon matrix, coke minerals, as well as their catalytic effect on the carbon gasification reaction.

[1]  M. Dresselhaus,et al.  Raman spectra and staging of intercalated graphite fibers , 1983 .

[2]  V. Sahajwalla,et al.  Degradation Behaviour of a High CSR Coke in an Experimental Blast Furnace: Effect of Carbon Structure and Alkali Reactions , 2005 .

[3]  V. Sahajwalla,et al.  The evolution of structural order, microstructure and mineral matter of metallurgical coke in a blast furnace: A review , 2014 .

[4]  R. Asher.  A LAMELLAR COMPOUND OF SODIUM AND GRAPHITE , 1959 .

[5]  K. Abendroth.  Advanced Pulverized Coal Injection Technology And Blast Furnace Operation , 2016 .

[6]  Q. Meng,et al.  Effect of Annealing on Properties of Carbonaceous Materials. Part III: Macro and Microstrengths , 2013, Metallurgical and Materials Transactions B.

[7]  R. Sakurovs,et al.  Quantification of mineral matter in commercial cokes and their parent coals , 2007 .

[8]  M. Tokuda,et al.  Preparation and characterization of sodium-graphite intercalation compounds , 2002 .

[9]  P. Zulli,et al.  Effects of Annealing on Microstructure and Microstrength of Metallurgical Coke , 2014, Metallurgical and Materials Transactions B.

[10]  K. Thomas,et al.  The interactions of carbons with potassium , 1993 .

[11]  P. Trucano,et al.  Structure of graphite by neutron diffraction , 1975, Nature.

[12]  V. Sahajwalla,et al.  Mineralogy and reactivity of cokes in a working blast furnace , 2014 .

[13]  T. Baird,et al.  Microstructural analysis of metallurgical cokes and intercalated species , 1986 .

[14]  V. Sahajwalla,et al.  Coke graphitization and degradation across the tuyere regions in a blast furnace , 2013 .

[15]  Jianliang Zhang,et al.  Gasification of Graphite and Coke in Carbon–Carbon Dioxide–Sodium or Potassium Carbonate Systems , 2014 .

[16]  F. Kapteijn,et al.  Formation of intercalate-like structures by heat treatment of K2CO3-carbon in an inert atmosphere , 1983 .

[17]  K. Carr.  Intercalation and oxidation effects on graphite of a mixture of sulphuric and nitric acids , 1970 .

[18]  Stanislav S. Gornostayev,et al.  An Example of Alkalization of SiO2 in a Blast Furnace Coke , 2007 .

[19]  M. Tribus,et al.  Monoclinic structure and nonstoichiometry of 'KAlSiO4-O1'. , 2013, Acta crystallographica. Section C, Crystal structure communications.

[20]  T. Terai,et al.  Sorption behavior of hydrogen gas and tritiated hydrogen gas on potassium-carbon intercalation compounds , 1984 .

[21]  Zhao Hong-bo.  New cognition on coke degradation by potassium and sodium in alkali enriched regions and quantificational control model for BF , 2012 .

[22]  W. Ruland,et al.  Interstitial compounds of potassium with carbon fibers , 1972 .

[23]  Y. L. Page,et al.  Refinement of the crystal structure of low-quartz , 1976 .

[24]  R. Dippenaar,et al.  The influence of potassium on the reactivity and strength of coke, with special reference to the role of coke ash , 1986 .

[25]  Dieter Senk,et al.  Effect of coke reactivity and nut coke on blast furnace operation , 2009 .

[26]  V. Sahajwalla,et al.  The Evolution of Structural Order as a Measure of Thermal History of Coke in the Blast Furnace , 2014, Metallurgical and Materials Transactions B.

[27]  Kuniyoshi Ishii,et al.  Advanced pulverized coal injection technology and blast furnace operation , 2000 .

[28]  V. Sahajwalla,et al.  Coke Mineral Transformations in the Experimental Blast Furnace , 2008 .

[29]  V. Sahajwalla,et al.  Characterization of the origin and distribution of the minerals and phases in metallurgical cokes , 2007 .

[30]  J. H. Haberman,et al.  On the mechanism of catalysis of the Boudouard reaction by alkali-metal compounds , 1982 .

[31]  F. Salzano,et al.  Thermodynamic Properties of the Potassium–Graphite Lamellar Compounds from Solid‐State emf Measurements , 1968 .

[32]  H. Jüntgen,et al.  Investigations on the alkali-catalysed steam gasification of coal: Kinetics and interactions of alkali catalyst with carbon☆ , 1983 .

[33]  M. Carpenter,et al.  X-ray study of the trigonal → hexagonal phase transition in metamorphic kalsilite , 1999 .

[34]  R. Kandiyoti,et al.  Study on the effect of heat treatment and gasification on the carbon structure of coal chars and metallurgical cokes using fourier transform Raman spectroscopy , 2009 .

[35]  Michiharu Hatano,et al.  Investigation of Quenched No. 2 Blast Furnace at Kokura Works , 1976 .

[36]  Q. Meng,et al.  Effect of Annealing on Properties of Carbonaceous Materials. Part II: Porosity and Pore Geometry , 2013, Metallurgical and Materials Transactions B.