Use of calcium sulfoaluminate cements for setting control of 3D-printing mortars

Abstract Printing cementitious structures in 3D (3D Printing) requires the use of a mortar which setting is rigorously controlled. In this paper, a mix made out of two types of cement, ordinary Portland cement (OPC) and Calcium Sulfo-aluminate cement (CSA), was adopted to control the printability of a mortar. The latter was formulated in order to be extrudable, buildable and to reach a compressive strength comparable to that of a traditional mortar. Finally, a printable mix made out of 7% CSA and 93% OPC was developed. The cement paste of the developed mix was tested using isothermal calorimetry to study the impact of CSA on the heat of hydration of the mix. The mortar is first checked for the two characteristics of printability (extrudability and buildability) by a manual home-made device. Then, an estimation of the rheological properties of the mortar using a penetration test was done. Afterwards, the strength of the mortar was tested and a compressive strength of 88 MPa was found after 28 days for non-printed specimens and 79 MPa for printed specimens.

[1]  Barry Berman,et al.  3D printing: the new industrial revolution , 2012, IEEE Engineering Management Review.

[2]  André Lecomte,et al.  Hydration of ordinary Portland cement and calcium sulfoaluminate cement blends , 2015 .

[3]  Clément Gosselin,et al.  Large-scale 3D printing of ultra-high performance concrete – a new processing route for architects and builders , 2016 .

[4]  Robert J. Flatt,et al.  Yield Stress During Setting of Cement Pastes From Penetration Tests , 2009 .

[5]  W. Hergeth,et al.  Change in reaction kinetics of a Portland cement caused by a superplasticizer — Calculation of heat flow curves from XRD data , 2012 .

[6]  F. Piller,et al.  Economic implications of 3D printing: Market structure models in light of additive manufacturing revisited , 2015 .

[7]  Georges Aouad,et al.  Numerical and experimental studies of aggregate blocking in mortar extrusion , 2017 .

[8]  J. Ambroise,et al.  Improving the mechanical performance of high-grade slag cement by the addition of Portland cement and sulfoaluminate cement , 2012 .

[9]  Roman Putanowicz,et al.  3D printing of buildings and building components as the future of sustainable construction , 2016 .

[10]  T. T. Le,et al.  Mix design and fresh properties for high-performance printing concrete , 2012 .

[11]  Jian fei Chen,et al.  Mechanical Properties of Structures 3D-Printed With Cementitious Powders , 2015, 3D Concrete Printing Technology.

[12]  A. Gibb,et al.  Hardened properties of high-performance printing concrete , 2012 .

[13]  G. Saoût,et al.  Hydration of Portland cement with additions of calcium sulfoaluminates , 2013 .

[14]  Robert Bogue,et al.  3D printing: the dawn of a new era in manufacturing? , 2013 .

[15]  Paulo J.M. Monteiro,et al.  Early age hydration of calcium sulfoaluminate (synthetic ye'elimite, ) in the presence of gypsum and varying amounts of calcium hydroxide , 2013 .

[16]  G. F. Barbosa,et al.  Design for Manufacturing and Assembly methodology applied to aircrafts design and manufacturing , 2013 .

[17]  L. Santoro,et al.  Long-term behaviour of hydraulic binders based on calcium sulfoaluminate and calcium sulfosilicate , 1995 .

[18]  S. Berger.  Etude des potentialités des ciments sulfo-alumineux bélitiques pour le conditionnement du zinc De l'hydratation à la durabilité , 2009 .

[19]  Xiaodong Wu,et al.  Compatibility between a polycarboxylate superplasticizer and the belite-rich sulfoaluminate cement: Setting time and the hydration properties , 2014 .

[20]  Samuel M. Allen,et al.  Three-dimensional printing of metal parts for tooling and other applications , 2000 .

[21]  R. Černý,et al.  Application of large-volume calorimetry for monitoring the early-stage hydration heat development in cement-based composites as a function of w/c , 2012 .

[22]  Jan H. Kietzmann,et al.  Disruptions, decisions, and destinations: enter the age of 3-D printing and additive manufacturing , 2015, IEEE Engineering Management Review.

[23]  Nicolas Roussel,et al.  Digital Concrete: Opportunities and Challenges , 2016 .

[24]  Paramita Mondal,et al.  Physico-chemical interaction between mineral admixtures and OPC–calcium sulfoaluminate (CSA) cements and its influence on early-age expansion , 2016 .

[25]  Xiangyu Wang,et al.  A critical review of the use of 3-D printing in the construction industry , 2016 .