Dynamic compressive loading influences degradation behavior of PEG‐PLA hydrogels

Biodegradable hydrogels are attractive 3D environments for cell and tissue growth. In cartilage tissue engineering, mechanical stimulation has been shown to be an important regulator in promoting cartilage development. However, the impact of mechanical loading on the gel degradation kinetics has not been studied. In this study, we examined hydrolytically labile gels synthesized from poly(lactic acid)‐b‐poly(ethylene glycol)‐b‐poly‐(lactic acid) dimethacrylate macromers, which have been used for cartilage tissue engineering. The gels were subject to physiological loading conditions in order to examine the effects of loading on hydrogel degradation. Initially, hydrogels were formed with two different cross‐linking densities and subject to a dynamic compressive strain of 15% at 0.3, 1, or 3 Hz. Degradation behavior was assessed by mass loss, equilibrium swelling and compressive modulus as a function of degradation time. From equilibrium swelling, the pseudo‐first‐order reaction rate constants were determined as an indication of degradation kinetics. The application of dynamic loading significantly enhanced the degradation time for the low cross‐linked gels (P < 0.01) while frequency showed no statistical differences in degradation rates or bulk erosion profiles. In the higher cross‐linked gels, a 3 Hz dynamic strain significantly increased the degradation kinetics resulting in an overall faster degradation time by 6 days compared to gels subject to the 0.3 and 1 Hz loads (P < 0.0001). The bioreactor set‐up also influenced overall degradation behavior where the use of impermeable versus permeable platens resulted in significantly lower degradation rate constants for both cross‐linked gels (P < 0.001). The compressive modulus exponentially decreased with degradation time under dynamic loading. Together, our findings indicate that both loading regime and the bioreactor setup influence degradation and should be considered when designing and tuning a biodegradable hydrogel where mechanical stimulation is employed. Biotechnol. Bioeng. 2009; 102: 948–959. © 2008 Wiley Periodicals, Inc.

[1]  David J. Mooney,et al.  Controlled growth factor release from synthetic extracellular matrices , 2000, Nature.

[2]  Stephanie J Bryant,et al.  In situ forming degradable networks and their application in tissue engineering and drug delivery. , 2002, Journal of controlled release : official journal of the Controlled Release Society.

[3]  Stephanie J Bryant,et al.  Manipulations in hydrogel chemistry control photoencapsulated chondrocyte behavior and their extracellular matrix production. , 2003, Journal of biomedical materials research. Part A.

[4]  Stephanie J Bryant,et al.  Encapsulating chondrocytes in degrading PEG hydrogels with high modulus: Engineering gel structural changes to facilitate cartilaginous tissue production , 2004, Biotechnology and bioengineering.

[5]  Seonghun Park,et al.  Cartilage interstitial fluid load support in unconfined compression. , 2003, Journal of biomechanics.

[6]  Michael J. Solomon,et al.  Inertial effects on polymer chain scission in planar elongational cross-slot flow , 2004 .

[7]  Albert C. Chen,et al.  Static and dynamic compression modulate matrix metabolism in tissue engineered cartilage , 2002, Journal of orthopaedic research : official publication of the Orthopaedic Research Society.

[8]  Kristi S. Anseth,et al.  Predicting Controlled-Release Behavior of Degradable PLA-b-PEG-b-PLA Hydrogels , 2001 .

[9]  H J Mankin,et al.  Articular cartilage repair and transplantation. , 1998, Arthritis and rheumatism.

[10]  Kristi S Anseth,et al.  Manipulations in hydrogel degradation behavior enhance osteoblast function and mineralized tissue formation. , 2006, Tissue engineering.

[11]  S. Goldstein,et al.  Functional tissue engineering: the role of biomechanics in articular cartilage repair. , 2001, Clinical orthopaedics and related research.

[12]  T M Quinn,et al.  Static compression is associated with decreased diffusivity of dextrans in cartilage explants. , 2000, Archives of biochemistry and biophysics.

[13]  C. Oomens,et al.  An integrated finite-element approach to mechanics, transport and biosynthesis in tissue engineering. , 2004, Journal of biomechanical engineering.

[14]  J. Meister,et al.  Static compression of articular cartilage can reduce solute diffusivity and partitioning: implications for the chondrocyte biological response. , 2001, Journal of biomechanics.

[15]  Moonsoo Jin,et al.  Effects of dynamic compressive loading on chondrocyte biosynthesis in self-assembling peptide scaffolds. , 2004, Journal of biomechanics.

[16]  Kristi S. Anseth,et al.  Verification of scaling laws for degrading PLA‐b‐PEG‐b‐PLA hydrogels , 2001 .

[17]  A. Güner,et al.  Degradation of PLA, PLGA homo‐ and copolymers in the presence of serum albumin: a spectroscopic investigation , 2000 .

[18]  A. Maroudas,et al.  Biophysical chemistry of cartilaginous tissues with special reference to solute and fluid transport. , 1975, Biorheology.

[19]  A. Grodzinsky,et al.  Contributions of fluid convection and electrical migration to transport in cartilage: relevance to loading. , 1996, Archives of biochemistry and biophysics.

[20]  G A Ateshian,et al.  Functional tissue engineering of articular cartilage through dynamic loading of chondrocyte-seeded agarose gels. , 2000, Journal of biomechanical engineering.

[21]  Walter Herzog,et al.  An improved solution for the contact of two biphasic cartilage layers , 1997 .

[22]  A. Metters,et al.  A Statistical Kinetic Model for the Bulk Degradation of PLA-b-PEG-b-PLA Hydrogel Networks , 2000 .

[23]  T. Quinn,et al.  Dynamic compression augments interstitial transport of a glucose-like solute in articular cartilage. , 2006, Biophysical journal.

[24]  E. Schacht,et al.  Encapsulation of osteoblast seeded microcarriers into injectable, photopolymerizable three-dimensional scaffolds based on d,l-lactide and epsilon-caprolactone. , 2005, Biomacromolecules.

[25]  S J Bryant,et al.  Cytocompatibility of UV and visible light photoinitiating systems on cultured NIH/3T3 fibroblasts in vitro , 2000, Journal of biomaterials science. Polymer edition.

[26]  S. Bryant,et al.  Crosslinking Density Influences Chondrocyte Metabolism in Dynamically Loaded Photocrosslinked Poly(ethylene glycol) Hydrogels , 2004, Annals of Biomedical Engineering.

[27]  P. Martens,et al.  Tailoring the degradation of hydrogels formed from multivinyl poly(ethylene glycol) and poly(vinyl alcohol) macromers for cartilage tissue engineering. , 2003, Biomacromolecules.

[28]  Christopher J Hunter,et al.  Dynamic compression of chondrocyte-seeded fibrin gels: effects on matrix accumulation and mechanical stiffness. , 2004, Osteoarthritis and cartilage.

[29]  Kristi S. Anseth,et al.  Fundamental studies of a novel, biodegradable PEG-b-PLA hydrogel , 2000 .

[30]  S J Bryant,et al.  Static and dynamic compressive strains influence nitric oxide production and chondrocyte bioactivity when encapsulated in PEG hydrogels of different crosslinking densities. , 2008, Osteoarthritis and cartilage.

[31]  Kristi S Anseth,et al.  Three-dimensional growth and function of neural tissue in degradable polyethylene glycol hydrogels. , 2006, Biomaterials.

[32]  Kristi S. Anseth,et al.  Exogenously triggered, enzymatic degradation of photopolymerized hydrogels with polycaprolactone subunits: experimental observation and modeling of mass loss behavior. , 2006, Biomacromolecules.

[33]  D L Bader,et al.  Compressive strains at physiological frequencies influence the metabolism of chondrocytes seeded in agarose , 1997, Journal of orthopaedic research : official publication of the Orthopaedic Research Society.

[34]  Stephanie J Bryant,et al.  Controlling the spatial distribution of ECM components in degradable PEG hydrogels for tissue engineering cartilage. , 2003, Journal of biomedical materials research. Part A.

[35]  Jeffrey A. Hubbell,et al.  Bioerodible hydrogels based on photopolymerized poly(ethylene glycol)-co-poly(.alpha.-hydroxy acid) diacrylate macromers , 1993 .

[36]  S. Waldman,et al.  Long-term intermittent compressive stimulation improves the composition and mechanical properties of tissue-engineered cartilage. , 2004, Tissue engineering.

[37]  K. Anseth,et al.  Controlling cartilaginous matrix evolution in hydrogels with degradation triggered by exogenous addition of an enzyme. , 2007, Tissue engineering.

[38]  Jason A Burdick,et al.  Review: photopolymerizable and degradable biomaterials for tissue engineering applications. , 2007, Tissue engineering.

[39]  P. Netti,et al.  Effect of dynamic loading on solute transport in soft gels implication for drug delivery , 2008 .

[40]  C. M. Agrawal,et al.  Effects of fluid flow on the in vitro degradation kinetics of biodegradable scaffolds for tissue engineering. , 2000, Biomaterials.

[41]  Farshid Guilak,et al.  Functional Tissue Engineering , 2002, Annals of the New York Academy of Sciences.