The effect of milling and sintering techniques on mechanical properties of Cu–graphite metal matrix composite prepared by powder metallurgy route

Abstract When copper is used as electrical sliding contacts, a large contact force is desirable to maintain effective current transfer, whilst on other hand it is advisable to have as small as contact force as possible in order to reduce the wear of the sliding components. In the present investigation Cu–graphite metal matrix composites (MMCs) were prepared by conventional powder metallurgy route using conventional and spark plasma sintering (SPS) techniques. It has been found that addition of graphite into copper does not result in much improvement on the hardness due to the soft nature of graphite. However, 90% and 97% of relative density have been obtained for conventional sintered and SPS samples respectively. Maximum Vickers hardness of around 100 has been achieved for Cu–1 vol.% graphite MMC when it is fabricated by SPS due to the combined effect of pressure and spark plasma effect. However, a hardness value of 65 has been obtained for the same composite when it is fabricated by conventional sintering at 900 °C for 1 h. It has been found that density and hardness of MMCs decreases up to 20 h of milling due to flake formation and increase in size and after that these values increases as particle shape changes to irregular and size reduction takes place.

[1]  W. Xu,et al.  Effect of electrical current on tribological property of Cu matrix composite reinforced by carbon nanotubes , 2011 .

[2]  R. Othman,et al.  Mechanical alloying and sintering of nanostructured tungsten carbide-reinforced copper composite and its characterization , 2011 .

[3]  S. C. Jain,et al.  Dry sliding wear behavior of hot forged and annealed Cu–Cr–graphite in-situ composites , 2011 .

[4]  S. Aravindan,et al.  Microwave sintering of copper–graphite composites , 2009 .

[5]  J. Lim,et al.  Manufacturing Processes and Properties of Copper—Graphite Composites Produced by High Frequency Induction Heating Sintering , 2007 .

[6]  K. N. Sood,et al.  Development of pitch-based carbon–copper composites , 2010 .

[7]  B. Kieback,et al.  Friction and wear of copper–graphite composites made with Cu-coated and uncoated graphite powders , 2002 .

[8]  Lei Liu,et al.  Investigation on wear and corrosion behavior of Cu–graphite composites prepared by electroforming , 2007 .

[9]  A. Yeoh,et al.  Dimensional responses of copper-graphite powder composites to sintering , 1997 .

[10]  J. Hao,et al.  Tribological properties of solid lubricants (graphite, h-BN) for Cu-based P/M friction composites , 2008 .

[11]  R. Menéndez,et al.  Preparation of pitch-based carbon–copper composites for electrical applications , 2004 .

[12]  M. Z. Abdullah,et al.  Development and performance analysis of novel cast copper–SiC–Gr hybrid composites , 2009 .

[13]  Zheng-fei Hu,et al.  Sliding wear behavior of copper–graphite composite material for use in maglev transportation system , 2008 .

[14]  R. Luo,et al.  Effect of the ratio of graphite/pitch coke on the mechanical and tribological properties of copper–carbon composites , 2010 .

[15]  Yanchun Zhou,et al.  Highly conductive and strengthened copper matrix composite reinforced by Zr2Al3C4 particulates , 2009 .

[16]  E. Rocha-Rangel,et al.  Effect of metallic addition on mechanical properties in an aluminum–graphite composite synthesized by means of mechanical milling , 2010 .

[17]  Hani Henein,et al.  Comparative processing-structure-property studies of Al-Cu matrix composites reinforced with TiC particulates , 2011 .

[18]  B. M. Girish,et al.  Mechanical properties of cast ZA-27/graphite particulate composites , 1995 .