Effect of pretreatment on electrochemical etching behavior of Al foil in HCl–H2SO4

Abstract The aluminum foil for high voltage aluminum electrolytic capacitor was immersed in 0.5 mol/L H 3 PO 4 or 0.125 mol/L NaOH solution at 40 °C for different time and then DC electro-etched in 1 mol/L HCl+2.5 mol/L H 2 SO 4 electrolyte at 80 °C. The pitting potential and self corrosion potential of Al foil were measured with polarization curves (PC). The potentiostatic current—time curve was recorded and the surface and cross section images of etched Al foil were observed with SEM. The electrochemical impedance spectroscopy (EIS) of etched Al foil and potential transient curves (PTC) during initial etching stage were measured. The results show the chemical pretreatments can activate Al foil surface, facilitate the absorption, diffusion and migration of Cl − onto the Al foil during etching, and improve the initiation rate of meta-stable pits and density of stable pits and tunnels, leading to much increase in the real surface area and special capacitance of etched Al foil.

[1]  R. Newman,et al.  Metastable Pitting and the Critical Pitting Temperature , 1998 .

[2]  H. Isaacs.  The localized breakdown and repair of passive surfaces during pitting , 1989 .

[3]  Mengye Wang,et al.  Al2O3-TiO2 composite oxide films on etched aluminum foil fabricated by electrodeposition and anodization , 2011 .

[4]  E. Mccafferty.  Sequence of steps in the pitting of aluminum by chloride ions , 2003 .

[5]  Youlong Xu,et al.  Formation of Al2O3–BaTiO3 nanocomposite oxide films on etched aluminum foil by sol–gel coating and anodizing , 2008 .

[6]  Jong-Ho Lee,et al.  Etching characteristics of high-purity aluminum in hydrochloric acid solutions , 2007 .

[7]  K. Nishio,et al.  Fabrication of site-controlled tunnel pits with high aspect ratios by electrochemical etching of Al using masking film , 2007 .

[8]  R. Alkire,et al.  Growth Rates of Aluminum Etch Tunnels , 1988 .

[9]  X. Shao,et al.  Effect of citric acid on microstructure and electrochemical characteristics of high voltage anodized alumina film formed on etched Al Foils , 2011 .

[10]  C. Ban,et al.  Controlling limiting length of tunnels on Al foil electroetched in HCl-H2SO4 solution , 2009 .

[11]  K. Nishio,et al.  Optimization of Etching Conditions for Site-Controlled Tunnel Pits with High Aspect Ratios in Al Foil , 2010 .

[12]  P. Pistorius,et al.  Surface Roughness and the Metastable Pitting of Stainless Steel in Chloride Solutions , 1995 .

[13]  Jiyoung Kim,et al.  Effects of pretreatment on the aluminium etch pit formation , 2009 .

[14]  H. Feng,et al.  Effect of trace Sn on corrosion behaviors of high voltage anode aluminum foil , 2008 .