Effect of activation on the carbon fibers from phenol–formaldehyde resins for electrochemical supercapacitors

Activated carbon fibers (ACF) are prepared from phenol–formaldehyde resin fibers through chemical activation and physical activation methods. The chemical activation process consisted of KOH, whereas the physical activation was performed by activation in CO2. The characteristics of the electrochemical supercapacitors with carbon fibers without activation (CF), carbon fibers activated by CO2 (ACF-CO2), and carbon fibers activated by KOH (ACF-KOH) have been compared. The activated carbon fibers from phenol–formaldehyde resins present a broader potential range in aqueous electrolytes than activated carbon and other carbon fibers. Activation does not produce any important change in the shape of starting fibers. However, activation leads to surface roughness and larger surface areas as well as an adapted pore size distribution. The higher surface areas of fibers treated by KOH exhibited higher specific capacitances (214 and 116 F g−1 in aqueous and organic electrolytes, respectively) and good rate capability. Results of this study suggest that the activated carbon fiber prepared by chemical activation is a suitable electrode material for high performance electrochemical supercapacitors.

[1]  Morinobu Endo,et al.  Self‐Sustained Thin Webs Consisting of Porous Carbon Nanofibers for Supercapacitors via the Electrospinning of Polyacrylonitrile Solutions Containing Zinc Chloride , 2007 .

[2]  Feng Wu,et al.  Mesoporous activated carbon fiber as electrode material for high-performance electrochemical double layer capacitors with ionic liquid electrolyte , 2010 .

[3]  M. Ue.  Mobility and Ionic Association of Lithium and Quaternary Ammonium Salts in Propylene Carbonate and γ‐Butyrolactone , 1994 .

[4]  Hsisheng Teng,et al.  The performance of electric double layer capacitors using particulate porous carbons derived from PAN fiber and phenol-formaldehyde resin , 2006 .

[5]  Lang Liu,et al.  Influence of KOH followed by oxidation pretreatment on the electrochemical performance of phenolic based activated carbon fibers , 2007 .

[6]  J. Horng,et al.  Effects of thermal treatments on the supercapacitive performances of PAN-based carbon fiber electrodes , 2009 .

[7]  A. Wokaun,et al.  Evolution of BET internal surface area in glassy carbon powder during thermal oxidation , 2002 .

[8]  Lian Gao,et al.  Characterization of a manganese dioxide/carbon nanotube composite fabricated using an in situ coating method , 2007 .

[9]  Jui-Hsiang Lin,et al.  Various Treated Conditions to Prepare Porous Activated Carbon Fiber for Application in Supercapacitor Electrodes , 2009 .

[10]  H. Mikawa,et al.  Application of Activated Carbon Fiber Fabrics to Electrodes of Rechargeable Battery and Organic Electrolyte Capacitor , 1984 .

[11]  A. Hollenkamp,et al.  Carbon properties and their role in supercapacitors , 2006 .

[12]  Changhou Liu,et al.  Effect of pre-carbonization of petroleum cokes on chemical activation process with KOH , 2005 .

[13]  B. Conway.  Electrochemical Supercapacitors: Scientific Fundamentals and Technological Applications , 1999 .

[14]  Jing-tang Zheng,et al.  Microstructure and chemical analysis of PAN-based activated carbon fibers prepared by different activation methods , 2002 .

[15]  Maria Angeles Lillo-Rodenas,et al.  Understanding chemical reactions between carbons and NaOH and KOH: An insight into the chemical activation mechanism , 2003 .

[16]  J. Amarilla,et al.  Amorphous Carbon Nanofibers and Their Activated Carbon Nanofibers as Supercapacitor Electrodes , 2010 .

[17]  J. Besenhard,et al.  Nomex-derived activated carbon fibers as electrode materials in carbon based supercapacitors , 2006 .

[18]  Seong-Ho Yoon,et al.  KOH Activation of Needle Coke to Develop Activated Carbons for High-Performance EDLC , 2006 .

[19]  R. D. Levie,et al.  On porous electrodes in electrolyte solutions: I. Capacitance effects☆ , 1963 .

[20]  J. Bernhard,et al.  Role of functional groups on the microwave attenuation and electric resistivity of activated carbon fiber cloth , 2009 .

[21]  Lang Liu,et al.  Capacitance Limits of Activated Carbon Fiber Electrodes in Aqueous Electrolyte , 2008 .

[22]  Yong Jung Kim,et al.  Structural features necessary to obtain a high specific capacitance in electric double layer capacitors , 2004 .