Influence of thermo-oxidative aging on the impact property of conventional and graphene-based carbon fabric composites

The effects of reinforced structure (three-dimensional braided preform and laminated plain woven fabric) and graphene nanoplatelet-reinforced hierarchical interface on the impact properties of carbon fabric composites after thermo-oxidative aging were investigated. The results indicated that the impact properties decreased with increasing aging time due to the degradation of the matrix and fiber–matrix interface. After exposure to 140℃ for 1200 h, the peak impact force and impact strength retention rates of 3D-braided graphene nanoplatelet-coated carbon fiber-reinforced composite were 13% and 8% higher than those of the laminated composite, respectively. One of the reasons was the graphene nanoplatelet-reinforced gradient interphase may provide an effective shield against interface oxidation, transfer the localized thermal stress, and restrict the movement of the different phase of the materials at the composites interface. Another reason was the integrated structure of the 3D-braided composite can make the fiber bear impact force together although the resin was damaged and the adhesive force between fiber bundles and resin decreased after thermo-oxidative aging. This synergetic reinforcing effect of 3D-braided structure and graphene nanoplatelet-reinforced hierarchical interface provides an easy and effective way to design and improve the thermo-oxidative stability of carbon fiber-reinforced composites.

[1]  O. Akhavan,et al.  Toward single-DNA electrochemical biosensing by graphene nanowalls. , 2012, ACS nano.

[2]  Yudong Huang,et al.  Formation of a carbon fiber/polyhedral oligomeric silsesquioxane/carbon nanotube hybrid reinforcement and its effect on the interfacial properties of carbon fiber/epoxy composites , 2011 .

[3]  R. Polanský,et al.  Influence of thermal treatment on the glass transition temperature of thermosetting epoxy laminate , 2009 .

[4]  Huang Wu,et al.  Graphene nanoplatelet paper as a light-weight composite with excellent electrical and thermal conductivity and good gas barrier properties , 2012 .

[5]  Liping Yu,et al.  Interfacial microstructure and properties of carbon fiber composites modified with graphene oxide. , 2012, ACS applied materials & interfaces.

[6]  Wei Fan,et al.  Rapid evaluation of thermal aging of a carbon fiber laminated epoxy composite , 2014 .

[7]  Xiaobo Liu,et al.  Dramatic mechanical and thermal increments of thermoplastic composites by multi-scale synergetic reinforcement: Carbon fiber and graphene nanoplatelet , 2013 .

[8]  G. Tandon,et al.  Anisotropic oxidation and weight loss in PMR-15 composites , 2007 .

[9]  K. Bowles,et al.  The Effects of Fiber Surface Modification and Thermal Aging on Composite Toughness and its Measurement , 1997 .

[10]  A. Ashori,et al.  Mechanical performance of epoxy/carbon fiber laminated composites , 2014 .

[11]  Samit Roy,et al.  The changes in flexural properties and microstructures of carbon fiber bismaleimide composite after exposure to a high temperature , 2014 .

[12]  M. Gigliotti,et al.  The effect of thermo-oxidation on matrix cracking of cross-ply [0/90]S composite laminates , 2013 .

[13]  Luigi Sorrentino,et al.  Drop-weight impact behaviour of woven hybrid basalt–carbon/epoxy composites , 2014 .

[14]  S. Stankovich,et al.  Preparation and characterization of graphene oxide paper , 2007, Nature.

[15]  M. Taha,et al.  Low-velocity impact of thin woven carbon fabric composites incorporating multi-walled carbon nanotubes , 2012 .

[16]  D. Heider,et al.  Thermal conductivities of three-dimensionally woven fabric composites , 2008 .

[17]  D. Fang,et al.  Effect of temperature on bending properties and failure mechanism of three-dimensional braided composite , 2012 .

[18]  H. Sturm,et al.  The scanning force microscope as a tool for the detection of local mechanical properties within the interphase of fibre reinforced polymers , 1998 .

[19]  Xuekun Sun,et al.  Mechanical properties of three-dimensional braided composites , 2004 .

[20]  K. Bowles,et al.  Thermo-Oxidative Stability and Fiber Surface Modification Effects on the Inplane Shear Properties of Graphite/PMR-15 Composites , 1997 .

[21]  W. Lu,et al.  Improved synthesis of graphene oxide. , 2010, ACS nano.

[22]  Richard E. Martin,et al.  Experimental and FEM study of thermal cycling induced microcracking in carbon/epoxy triaxial braided composites , 2013 .

[23]  Lei Chen,et al.  A design of gradient interphase reinforced by silanized graphene oxide and its effect on carbon fiber/epoxy interface , 2014 .

[24]  N. Koratkar,et al.  Dramatic increase in fatigue life in hierarchical graphene composites. , 2010, ACS applied materials & interfaces.

[25]  G. Tandon,et al.  Influence of laminate lay-up on oxidation and damage growth: Isothermal aging , 2011 .