Sequential interpenetrating polymer networks of novolac resin and poly(2-ethyl hexyl acrylate)—thermal, mechanical, and morphological study

Interpenetrating polymer networks (IPN) of novolac/poly (2- ethyl hexyl acrylate) (PEHA) have been prepared via in situ sequential technique of IPN formation. Full and semi-IPNs were prepared with different blend ratios (w/w) e.g., 90 : 10, 80 : 20, and 70 : 30 in which the major constituent was novolac resin. A gradual decrease in specific gravity and hardness values was observed with increase in PEHA incorporation. A steady decrease in crosslink density with increase in PEHA fraction in the IPNs was quite evident. The IPNs were characterized with respect to their mechanical properties, e.g., ultimate tensile strength, percentage elongation at break, modulus, and toughness. Thermal behavior was studied by differential scanning calorimetry and thermogravimetric analysis. A plasticizing influence of PEHA on the rigid, brittle, and hard matrix of crosslinked phenolic resin is evidenced from the mechanical and thermal properties. The two-phase surface morphology is revealed by scanning electron microscope. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012

[1]  S. Goswami,et al.  Synthesis and characterization of sequential interpenetrating polymer networks of novolac resin and poly(ethyl acrylate) , 2006 .

[2]  S. Goswami,et al.  Modification of novolac resin by interpenetrating network formation with poly(butyl acrylate) , 2005 .

[3]  Y. J. Kim,et al.  Comparative study of carbon dioxide and nitrogen atmospheric effects on the chemical structure changes during pyrolysis of phenol-formaldehyde spheres. , 2004, Journal of colloid and interface science.

[4]  B. Wunderlich,et al.  Calorimetric study of block-copolymers of poly(n-butyl acrylate) and gradient poly(n-butyl acrylate-co-methyl methacrylate) , 2002 .

[5]  C. Ma,et al.  Thermal degradation of phenolic resin/silica hybrid ceramers , 2000 .

[6]  T. Kyotani,et al.  Comparison of structural parameters of PF carbon from XRD and HRTEM techniques , 2000 .

[7]  D. Chakrabarty,et al.  Novolac resin–poly(ethyl methacrylate) interpenetrating polymer networks: Morphology and mechanical and thermal properties , 1998 .

[8]  G. Camino,et al.  Structure-charring relationship in phenol-formaldehyde type resins , 1997 .

[9]  D. J. Hourston,et al.  Poly(ether urethane)/poly(ethyl methacrylate) interpenetrating polymer networks: Morphology, phase continuity and mechanical properties as a function of composition , 1996 .

[10]  D. Chakraborty,et al.  Epoxy resin/poly(ethyl acrylate)—interpenetrating polymer networks: engineering properties and morphology , 1994 .

[11]  A. Basta,et al.  Kinetic Studies on the Pyrolytic Degradation of Phenolic Resin Paper Sheets Using DTA Technique. II. In Situ Formation of Phenol Lignin Formaldehyde in Bagasse Pulp , 1994 .

[12]  G. Meyer,et al.  Polydimethylsiloxane/poly(methyl methacrylate) interpenetrating polymer networks: 2. Synthesis and properties , 1992 .

[13]  H. Frisch.  Interpenetrating polymer networks , 1985 .

[14]  D. Klempner,et al.  Nomenclature of Interpenetrating Polymer Networks , 1973 .

[15]  D. A. Thomas,et al.  Interpenetrating Polymer Networks of Poly(ethyl acrylate) and Poly(styrene-co-methly methacrylate). I. Morphology via Electron Microscopy , 1972 .

[16]  Robert T. Conley,et al.  A study of the oxidative degradation of phenol-formaldehyde polycondensates using infrared spectroscopy†‡ , 1963 .