Fabrication of porous biodegradable polymer scaffolds using a solvent merging/particulate leaching method.

This study developed a solvent merging/particulate leaching method for preparing three-dimensional porous scaffolds. Poly(L-lactic-co-glycolic acid) (PLGA) and sodium chloride particles were dry-mixed and cast into a special mold, through which a liquid could pass due to a pressure difference. An organic solvent was then poured into the mold to dissolve and merge the PLGA particles under negative pressure. A nonsolvent was conducted into the PLGA/salt composite to solidify and precipitate the merged PLGA matrix. Finally, a large amount of water was passed through the mold to leach out the salt particles so as to create a porous structure. The results revealed that a highly porous three-dimensional scaffold (>85 vol %) with a well interconnected porous structure could be achieved by this process. Porosity and the pore size of the scaffold were controlled using the ratio and the particle size of the added salt particles. A larger-volume scaffold was produced using a larger mold. This work provides a continuous and simple procedure for fabricating a bulk three-dimensional porous scaffold for tissue engineering.

[1]  D. Hutmacher,et al.  Scaffolds in tissue engineering bone and cartilage. , 2000, Biomaterials.

[2]  William E Lee,et al.  Ceramic Microstructures: Property control by processing , 1994 .

[3]  R Langer,et al.  Laminated three-dimensional biodegradable foams for use in tissue engineering. , 1993, Biomaterials.

[4]  Kevin E. Healy,et al.  A novel method to fabricate bioabsorbable scaffolds , 1995 .

[5]  Robert Langer,et al.  Preparation and characterization of poly(l-lactic acid) foams , 1994 .

[6]  T. Park,et al.  Porous biodegradable polymeric scaffolds prepared by thermally induced phase separation. , 1999, Journal of biomedical materials research.

[7]  David J. Mooney,et al.  Synthesis and Properties of Biodegradable Polymers Used as Synthetic Matrices for Tissue Engineering , 1997 .

[8]  J. Feijen,et al.  Phase transitions during membrane formation of polylactides. I. A morphological study of membranes obtained from the system polylactide-chloroform-methanol , 1996 .

[9]  Antonios G. Mikos,et al.  Pore Morphology Effects on the Fibrovascular Tissue Growth in Porous Polymer Substrates , 1994, Cell transplantation.

[10]  M J Yaszemski,et al.  Three-dimensional culture of rat calvarial osteoblasts in porous biodegradable polymers. , 1998, Biomaterials.

[11]  T. Park,et al.  A novel fabrication method of macroporous biodegradable polymer scaffolds using gas foaming salt as a porogen additive. , 2000, Journal of biomedical materials research.

[12]  C. M. Agrawal,et al.  Sterilization, toxicity, biocompatibility and clinical applications of polylactic acid/polyglycolic acid copolymers. , 1996, Biomaterials.

[13]  Michael Jarcho,et al.  Calcium phosphate ceramics as hard tissue prosthetics. , 1981, Clinical orthopaedics and related research.

[14]  L G Griffith,et al.  Integration of surface modification and 3D fabrication techniques to prepare patterned poly(L-lactide) substrates allowing regionally selective cell adhesion. , 1998, Journal of biomaterials science. Polymer edition.

[15]  Larry L. Hench,et al.  Biomaterials : an interfacial approach , 1982 .

[16]  M J Yaszemski,et al.  Ectopic bone formation by marrow stromal osteoblast transplantation using poly(DL-lactic-co-glycolic acid) foams implanted into the rat mesentery. , 1997, Journal of biomedical materials research.

[17]  R Langer,et al.  Novel approach to fabricate porous sponges of poly(D,L-lactic-co-glycolic acid) without the use of organic solvents. , 1996, Biomaterials.

[18]  A. Mikos,et al.  Effect of osteoblastic culture conditions on the structure of poly(DL-lactic-co-glycolic acid) foam scaffolds. , 1999, Tissue engineering.

[19]  V. Maquet,et al.  Polylactide macroporous biodegradable implants for cell transplantation. II. Preparation of polylactide foams by liquid-liquid phase separation. , 1996, Journal of biomedical materials research.

[20]  John M. Powers,et al.  Hydroxyapatite fiber reinforced poly(α-hydroxy ester) foams for bone regeneration , 1998 .

[21]  Suzana P. Nunes,et al.  Porous poly(l-lactide) films obtained by immersion precipitation process: morphology, phase separation and culture of VERO cells , 1999 .

[22]  J. Vacanti,et al.  Tissue engineering : Frontiers in biotechnology , 1993 .

[23]  D E Ingber,et al.  Preparation of poly(glycolic acid) bonded fiber structures for cell attachment and transplantation. , 1993, Journal of biomedical materials research.

[24]  K. Leong,et al.  Poly(L-lactic acid) foams with cell seeding and controlled-release capacity. , 1996, Journal of biomedical materials research.

[25]  Y. Ikada,et al.  In vitro and in vivo comparison of bulk and surface hydrolysis in absorbable polymer scaffolds for tissue engineering. , 1999, Journal of biomedical materials research.

[26]  A morphological study of membranes obtained from the systems polylactide-dioxane-methanol, polylactide-dioxane-water and polylactide-N-methyl pyrrolidone-water , 1996 .

[27]  R Langer,et al.  Neocartilage formation in vitro and in vivo using cells cultured on synthetic biodegradable polymers. , 1993, Journal of biomedical materials research.

[28]  R Langer,et al.  Macroporous polymer foams by hydrocarbon templating. , 2000, Proceedings of the National Academy of Sciences of the United States of America.