Raman scattering from hydrogenated microcrystalline and amorphous silicon

Raman scattering measurements on hydrogenated microcrystalline silicon prepared in a hydrogen plasma at deposition temperatures between approximately=65 and 400 degrees C are presented and discussed. The shifts of the crystalline (c) and 'amorphous-like' (a) components of the spectra to lower frequencies with decreasing crystallite size have been correlated with the lattice expansion and the finite dimensions of the crystallites in these films. The roles of hydrogen and of the compressive stress in the samples have been investigated by annealing experiments and a deposition of the samples under negative bias of the substrate, respectively. These results point to a probable mechanism of the crystalline-amorphous transition in silicon. The data presented allow an assignment of the amorphous-like feature in the Raman spectra to surface-like modes at grain boundaries of the crystallites. Strong arguments are given that suggest that the 480 cm-1 peak in the Raman spectra of X-ray amorphous silicon is of the same origin and is hence associated with some shearing modes of Si clusters rather than a broadened density of states. Results on the depolarisation ratio of Raman scattering in the microcrystalline and X-ray amorphous films are also presented and discussed.

[1]  R. Cowley,et al.  The thermodynamic and optical properties of germanium, silicon, diamond and gallium arsenide , 1966 .

[2]  Zafar Iqbal,et al.  Raman scattering from small particle size polycrystalline silicon , 1981 .

[3]  J. E. Smith,et al.  Vibrational properties of amorphous Si and Ge , 1975 .

[4]  B. Weinstein,et al.  Raman scattering and phonon dispersion in Si and GaP at very high pressure , 1975 .

[5]  P. Temple,et al.  Multiphonon Raman Spectrum of Silicon , 1973 .

[6]  A. Ushirokawa,et al.  Observation of the amorphous‐to‐crystalline transition in silicon by Raman scattering , 1981 .

[7]  M. Cardona,et al.  Raman scattering in pure and hydrogenated amorphous germanium and silicon , 1979 .

[8]  M. Balkanski,et al.  Effect of dimensions on the vibrational frequencies of thin slabs of silicon , 1980 .

[9]  S. Yamasaki,et al.  Electrical and Structural Properties of Phosphorous-Doped Glow-Discharge Si:F:H and Si:H Films , 1980 .

[10]  J. E. Smith,et al.  Raman Spectra of Amorphous Si and Related Tetrahedrally Bonded Semiconductors , 1971 .

[11]  S. Solin,et al.  Temperature Dependence of the Raman Spectrum and the Depolarization Spectrum of Amorphous As 2 S 3 , 1973 .

[12]  Zafar Iqbal,et al.  Lattice dilatation of small silicon crystallites - implications for amorphous silicon , 1981 .

[13]  Z. Iqbal,et al.  Properties of polycrystalline silicon prepared by chemical transport in hydrogen plasma at temperatures between 80 and 400 degrees C , 1981 .

[14]  S. Vepřek,et al.  The preparation of thin layers of Ge and Si by chemical hydrogen plasma transport , 1968 .

[15]  W. Spear,et al.  Electronic properties of substitutionally doped amorphous Si and Ge , 1976 .

[16]  Z. Iqbal,et al.  Polycrystalline silicon films deposited in a glow discharge at temperatures below 250 °C , 1980 .