Determining the Low-Temperature Fracture Toughness of Asphalt Mixtures

There has been a sustained effort in applying fracture mechanics concepts to crack formation and propagation in bituminous pavement materials. Adequate fracture resistance is an essential requirement for asphalt pavements built in the northern part of the United States and Canada, for which the prevailing failure mode is cracking due to low-temperature shrinkage stresses. The current Superpave® specifications address this issue mainly through the use of strength tests on unnotched (smooth boundary) specimens. However, recent studies have shown the limitations of this approach and have suggested that fracture mechanics concepts, based on tests performed on notched samples, should be used instead. Research in progress at the University of Minnesota investigates the use of fracture mechanics principles to determine the low-temperature fracture properties of asphalt mixtures. A testing protocol is presented that makes it possible to obtain multiple measurements of fracture toughness as a function of crack propagation based on the compliance method to measure crack length. An increase in fracture toughness with crack length is observed, which is consistent with the behavior displayed by other brittle materials. The plateau of the curves may be representative of the asphalt concrete resistance to fracture, because the initial values can be significantly influenced by the presence of the inelastic zone at the crack tip.

[1]  S. Timoshenko,et al.  Theory of elasticity , 1975 .

[2]  Simon A M Hesp,et al.  Canadian Technical Asphalt Association Proceedings 2001 46 th Annual Meeting, Toronto, Ontario Fracture Energy and Critical Crack Tip Opening Displacement: Fracture Mechanics- Based Failure Criteria for Low-Temperature Grading of Asphalt Binders , 2001 .

[3]  Reynaldo Roque,et al.  Evaluation of Laboratory-Measured Crack Growth Rate for Asphalt Mixtures , 2001 .

[4]  David Martin,et al.  Low-temperature rheological and fracture properties of polymer-modified bitumens , 2000 .

[5]  Nolan K. Lee,et al.  Low temperature fracture of polyethylene-modified asphalt binders and asphalt concrete mixes , 1995 .

[6]  Joseph F Labuz,et al.  EXPERIMENTAL ANALYSIS OF CRACK PROPAGATION IN GRANITE , 1985 .

[7]  Albert S. Kobayashi,et al.  Fracture Mechanics Applied to Brittle Materials , 1979 .

[8]  R. A. Schmidt,et al.  Fracture-toughness testing of limestone , 1976 .

[9]  A. Molenaar,et al.  FRACTURE TOUGHNESS OF ASPHALT IN THE SEMI-CIRCULAR BEND TEST , 2000 .

[10]  Shongtao Dai,et al.  CRACKING OF ASPHALT CONCRETE AT LOW TEMPERATURES , 1994 .

[11]  Raj Dongré,et al.  DEVELOPMENT OF FRACTURE CRITERION FOR ASPHALT MIXES AT LOW TEMPERATURES , 1989 .

[12]  Michael S Mamlouk,et al.  Evaluation of crack propagation properties of asphalt mixtures , 1997 .

[13]  David A. Anderson,et al.  Low-Temperature Thermal Cracking of Asphalt Binders as Ranked by Strength and Fracture Properties , 2000 .

[14]  Reynaldo Roque,et al.  DETERMINATION OF CRACK GROWTH RATE PARAMETER OF ASPHALT MIXTURES USING THE SUPERPAVE IDT , 1999 .

[15]  Simon A M Hesp,et al.  LOW-TEMPERATURE FRACTURE TOUGHNESS OF POLYETHYLENE-MODIFIED ASPHALT BINDERS , 1994 .

[16]  T. Lutz,et al.  K Ic and J Ic of Westerly Granite—Effects of Thickness and In-Plane Dimensions , 1979 .