Corrosion fatigue crack growth behavior of pipeline steel under underload-type variable amplitude loading schemes
暂无分享,去创建一个
Greg Van Boven | Richard Kania | Hao Zhang | Mengshan Yu | Jenny Been | Jiaxi Zhao | R. L. Eadie | Jiaxi Zhao | Weixing Chen | G. V. Boven | Xiao Xing | Weixing Chen | Hao Zhang | R. Kania | R. Eadie | Mengshan Yu | J. Been | R. Eadie | Xiao Xing | G. Boven
[1] T. Anderson,et al. Fracture mechanics - Fundamentals and applications , 2017 .
[2] Weixing Chen,et al. Underload‐induced crack growth behaviour of minor cycles of pipeline steel in near‐neutral pH environment , 2015 .
[3] Weixing Chen,et al. Development and Validation of Load-Interaction Based Models for Crack Growth Prediction , 2014 .
[4] Weixing Chen,et al. Correlating Corrosion Field Data With Experimental Findings for the Development of Pipeline Mitigation Strategies , 2014 .
[5] Weixing Chen,et al. Depressurization-Induced Crack Growth Enhancement for Pipeline Steels Exposed to Near-Neutral pH Environments , 2014 .
[6] Weixing Chen,et al. Transgranular crack growth in the pipeline steels exposed to near-neutral pH soil aqueous solutions: Discontinuous crack growth mechanism , 2014 .
[7] M. Nakamura,et al. Hydrogen-enhanced lattice defect formation and hydrogen embrittlement of cyclically prestressed tempered martensitic steel , 2013 .
[8] W. Curtin,et al. Atomic mechanism and prediction of hydrogen embrittlement in iron. , 2013, Nature materials.
[9] Weixing Chen,et al. Effects of grain boundary and boundary inclination on hydrogen diffusion in a-iron , 2011 .
[10] W. Curtin,et al. A nanoscale mechanism of hydrogen embrittlement in metals , 2011 .
[11] Weixing Chen,et al. Transgranular crack growth in the pipeline steels exposed to near-neutral pH soil aqueous solutions: The role of hydrogen , 2009 .
[12] S. Matsumoto,et al. Atomistic simulations of hydrogen embrittlement , 2009 .
[13] Weixing Chen,et al. Crack Growth Behavior of Pipeline Steel in Near-Neutral pH Soil Environments , 2007 .
[14] J. L. Otegui,et al. Failures by SCC in buried pipelines , 2002 .
[15] Weixing Chen,et al. Environmental aspects of near-neutral pH stress corrosion cracking of pipeline steel , 2002 .
[16] Weixing Chen,et al. A study on the pre-cyclic-load-induced burst of creep deformation of a pipeline steel under subsequent static load , 2002 .
[17] S. Lambert,et al. Mechanical Factors Affecting Stress Corrosion Crack Growth Rates in Buried Pipelines , 2000 .
[18] Weixing Chen,et al. Hydrogen Permeation Behavior of X-70 Pipeline Steel in a Near-Neutral pH Soil Environment , 2000 .
[19] M. Skorupa,et al. Load interaction effects during fatigue crack growth under variable amplitude loading—a literature review. Part II: qualitative interpretation , 1999 .
[20] P. Ferreira,et al. Hydrogen effects on the character of dislocations in high-purity aluminum , 1999 .
[21] M. Skorupa. Load interaction effects during fatigue crack growth under variable amplitude loading : A literature review. Part I : Empirical trends , 1998 .
[22] T. Ahmed,et al. Cyclic Crack Growth Rates of X-60 Pipeline Steel in a Neutral Dilute Solution , 1997 .
[23] Petros Athanasios Sofronis,et al. Hydrogen-enhanced localized plasticity—a mechanism for hydrogen-related fracture , 1993 .
[24] J. Jones,et al. Effects of temperature and frequency on fatigue crack growth in 18% Cr ferritic stainless steel , 1993 .
[25] B Delanty,et al. MAJOR FIELD STUDY COMPARES PIPELINE SCC WITH COATINGS , 1992 .
[26] T. Sudarshan,et al. Mechanisms of fatigue crack initiation in metals: role of aqueous environments , 1988 .
[27] Weixing Chen,et al. Crack propagation of pipeline steel exposed to a near-neutral pH environment under variable pressure fluctuations , 2016 .
[28] Huajian Gao,et al. Continuum and atomistic models of strongly coupled diffusion, stress, and solute concentration , 2011 .
[29] R. Eadie,et al. Prediction of Environmentally Assisted Cracking on Gas and Liquid Pipelines , 2006 .
[30] Robert Sutherby,et al. Characterizing Pressure Fluctuations on Buried Pipelines in Terms Relevant to Stress Corrosion Cracking , 2002 .
[31] Z. Gasem. Frequency-dependent environmental fatigue crack propagation in the 7XXX alloy/aqueous chloride system , 1999 .
[32] J. Lankford,et al. Fatigue crack growth in metals and alloys: mechanisms and micromechanics , 1992 .