The Study of Chemical and Thermal Influences of the Environment on the Degradation of Mechanical Properties of Carbon Composite with Epoxy Resin

The present research deals with the investigation of the influence of aqueous solutions of chemical substances in combination with temperature on the change of material properties of polymer composites based on epoxy resins reinforced with carbon fibers. The aim of the research was to investigate and evaluate the impact of degradation processes due to the influence of chemical environments of different temperatures and time of their action on changes in the material properties and macrostructure of carbon composite with epoxy resin. The chemical and thermal influence of the environment on the experimental material was evaluated by monitoring changes in mechanical properties, glass transition temperature, and material surface macrostructure. The achieved results show different behavior of the experimental composite material in different environments, while it was demonstrated that the degradation effect of chemical and thermal influences on changes in material properties increase with increasing temperature. Among the investigated environments (NaCl, NaOH, and H2SO4), exposure to 10% NaOH, and 15% H2SO4 had the greatest degradation influence on the polymer composite, and exposure to 20% NaCl had the smallest influence, which is also confirmed by invisible changes in material surface macrostructure and decrease of tensile strength by about 20%. Exposure to 10% NaOH resulted in significant surface roughening of the epoxy resin, white deposit creation on the surface, and a decrease of tensile strength by 35%. Opposite that, exposure to 15% H2SO4 resulted in the highlighting of the fiber yarns of the carbon fiber fabric, yellowing of the surface, surface pore occurrence, and a decrease of tensile strength by 35%.

[1]  F. Nový,et al.  Evaluation of tensile properties of carbon fiber reinforced polymers produced from commercial prepregs , 2022, Materials Today: Proceedings.

[2]  Chenggao Li,et al.  Long-term service evaluation of a pultruded carbon/glass hybrid rod exposed to elevated temperature, hydraulic pressure and fatigue load coupling , 2020 .

[3]  Sabu Thomas,et al.  Durability of an Epoxy Resin and Its Carbon Fiber- Reinforced Polymer Composite upon Immersion in Water, Acidic, and Alkaline Solutions , 2020, Polymers.

[4]  T. Liptáková,et al.  The physical – mechanical properties of low-density polyethylene films , 2020, IOP Conference Series: Materials Science and Engineering.

[5]  I. García-Moreno,et al.  Effect of Thermal Ageing on the Impact and Flexural Damage Behaviour of Carbon Fibre-Reinforced Epoxy Laminates , 2019, Polymers.

[6]  Durability and Life Prediction in Biocomposites, Fibre-Reinforced Composites and Hybrid Composites , 2019 .

[7]  N. Liou,et al.  Effects of high temperature and ultraviolet radiation on polymer composites , 2019, Durability and Life Prediction in Biocomposites, Fibre-Reinforced Composites and Hybrid Composites.

[8]  Ronald Sterkenburg,et al.  Investigating the effects of fluid intrusion on Nomex® honeycomb sandwich structures with carbon fiber facesheets , 2018, Composite Structures.

[9]  Gang Wu,et al.  Effect of sustained load and seawater and sea sand concrete environment on durability of basalt- and glass-fibre reinforced polymer (B/GFRP) bars , 2018, Corrosion Science.

[10]  G. Xian,et al.  Durability study of pultruded carbon fiber reinforced polymer plates subjected to water immersion , 2018 .

[11]  Y. J. Kim,et al.  Effects of Sulfuric Acid on Durability Characteristics of CFRP Composite Sheets , 2017 .

[12]  K. Kar Composite Materials: Processing, Applications, Characterizations , 2017 .

[13]  Luis A. Rodriguez Environmental Durability and Degradation of Fiber-Reinforced Bismaleimide/Quartz Composite for Aircraft Radome Applications , 2017 .

[14]  K. Kar,et al.  Polymer-Based Composite Structures: Processing and Applications , 2017 .

[15]  D. Harris,et al.  Charpy impact testing to assess the quality and durability of unidirectional CFRP rods , 2016 .

[16]  S. A. Grammatikos,et al.  On the response to hygrothermal aging of pultruded FRPs used in the civil engineering sector , 2016 .

[17]  Constantinos Soutis,et al.  Polymer Composites in the Aerospace Industry , 2014 .

[18]  H. Biscaia,et al.  On estimates of durability of FRP based on accelerated tests , 2014 .

[19]  P. Polák The Influence of Moisture Absorption into Uncured Resins. , 2014 .

[20]  J. Ferreira,et al.  Effect of corrosive solutions on composites laminates subjected to low velocity impact loading , 2014 .

[21]  M. Altan,et al.  Three‐dimensional anisotropic moisture absorption in quartz‐reinforced bismaleimide laminates , 2014 .

[22]  C. Louro,et al.  Effect of different acid solutions on glass/epoxy composites , 2013 .

[23]  M. A. Neto,et al.  Effects of alkaline and acid solutions on glass/epoxy composites , 2013 .

[24]  O. Almeida,et al.  Comparison of the impact resistance of carbon/epoxy and carbon/peek composite laminates , 2012 .

[25]  P. Hamelin,et al.  Ageing of carbon/epoxy and carbon/vinylester composites used in the reinforcement and/or the repair of civil engineering structures , 2012 .

[26]  Bahram M. Shahrooz,et al.  Environmental durability of externally bonded FRP materials intended for repair of concrete structures , 2011 .

[27]  K. Elleuch,et al.  The effect of time and aging temperature on structural and mechanical properties of pipeline coating , 2009 .

[28]  Alireza Nasiri Properties of FRP composite durability , 2008 .

[29]  Mukesh Limbachiya,et al.  Excellence in concrete construction through innovation , 2008 .

[30]  Young-Jun You,et al.  Durability of GFRP composite exposed to various environmental conditions , 2006 .

[31]  A. Hammami,et al.  Durability and environmental degradation of glass‐vinylester composites , 2004 .

[32]  M. Mahmoud,et al.  Effect of Strong Acids on Mechanical Properties of Glass/Polyester GRP Pipe at Normal and High Temperatures , 2003 .

[33]  Toshio Nakamura,et al.  Degradation of Carbon Fiber-Reinforced Epoxy Composites by Ultraviolet Radiation and Condensation , 2002 .

[34]  Levend Parnas,et al.  Design of fiber-reinforced composite pressure vessels under various loading conditions , 2002 .

[35]  J. P. Lucas,et al.  Hygrothermal effects of epoxy resin. Part II : Variations of glass transition temperature , 1999 .

[36]  R Delasi,et al.  Effect of Moisture on Epoxy Resins and Composites , 1978 .