Life Prediction Methodology for Composite Structures. Part I—Constant Amplitude and Two-Stress Level Fatigue

A strength-based wearout model is presented for predicting the residual strength and life of composite structures subjected to constant amplitude or two-stress level fatigue loadings. It is assumed that the structure undergoes proportional loading, that its residual strength is a monotonically decreasing function of the number of loading cycles, and that both the life distribution due to continuous constant amplitude cycling and the residual strength distribution after an arbitrary load history may be represented by two parameter Weibull functions. The model also incorporates a "cycle mix factor" to account for the degradation of strength and life that may be associated with frequent changes in the stress amplitude of the loading. Experimental results from two-stress level, uniaxially loaded laminates are used to evaluate the model's predictive capability for sequencing effects, as in a low-high or high-low test, and for cycle mix effects, as in a low-high-low-high repeating test. Good correlation between theory and experiment is obtained for all loadings and laminates studied.

[1]  R. Kim,et al.  Fatigue Behavior of Composite Laminate , 1976 .

[2]  Robert Croman,et al.  Residual Strength in Fatigue Based on the Strength-Life Equal Rank Assumption , 1978 .

[3]  Lj Broutman,et al.  A New Theory to Predict Cumulative Fatigue Damage in Fiberglass Reinforced Plastics , 1972 .

[4]  Anoush Poursartip,et al.  The fatigue damage mechanics of a carbon fibre composite laminate: II—life prediction , 1986 .

[5]  H. Whitworth,et al.  Cumulative Damage in Composites , 1990 .

[6]  Douglas L. Jones,et al.  Load Sequence Effects on Graphite/Epoxy [±35] 2s Laminates , 1983 .

[7]  TK O'Brien,et al.  Long-Term Behavior of Composites , 1983 .

[8]  M. Ashby,et al.  The fatigue damage mechanics of a carbon fibre composite laminate: I—development of the model , 1986 .

[9]  W. Hwang,et al.  Cumulative Damage Models and Multi-Stress Fatigue Life Prediction , 1986 .

[10]  Ramesh Talreja,et al.  Estimation of Weibull Parameters for Composite Material Strength and Fatigue Life Data , 1981 .

[11]  J. N. Yang,et al.  Effect of Load Sequence on the Statistical Fatigue of Composites , 1980 .

[12]  J.N. Yang,et al.  Residual Strength Degradation Model and Theory of Periodic Proof Tests for Graphite/Epoxy Laminates* , 1977 .

[13]  J. N. Yang,et al.  Fatigue and Residual Strength Degradation for Graphite/Epoxy Composites Under Tension-Compression Cyclic Loadings , 1978 .

[14]  H. Hahn,et al.  Proof Testing of Composite Materials , 1975 .

[15]  W. Hwang,et al.  Fatigue of Composite Materials—Damage Model and Life Prediction , 1989 .

[16]  J. Halpin,et al.  Kinetic fracture models and structural reliability , 1972 .

[17]  W. Hwang,et al.  Fatigue of Composites—Fatigue Modulus Concept and Life Prediction , 1986 .

[18]  Pc Chou,et al.  Degradation and Sudden-Death Models of Fatigue of Graphite/Epoxy Composites , 1979 .

[19]  J. N. Yang,et al.  Load sequence effects on the fatigue of unnotched composite materials , 1981 .

[20]  Shanyi Du,et al.  An Exploratory Study Into the Fatigue of Composites Under Spectrum Loading , 1983 .

[21]  Douglas L. Jones,et al.  A Stiffness-Based Statistical Model for Predicting the Fatigue Life of Graphite/Epoxy Laminates , 1989 .

[22]  K. Reifsnider,et al.  Fatigue Damage Evaluation through Stiffness Measurements in Boron-Epoxy Laminates , 1981 .

[23]  Kn Lauraitis,et al.  Fatigue of Fibrous Composite Materials , 1981 .

[24]  H. Whitworth,et al.  Modeling Stiffness Reduction of Graphite/Epoxy Composite Laminates , 1987 .

[25]  Barry D. Davidson,et al.  Life Prediction Methodology for Composite Structures. Part II—Spectrum Fatigue , 1997 .

[26]  H. Hoersch,et al.  Composite Materials: Fatigue and Fracture , 1986 .

[27]  J. N. Yang,et al.  Prediction of fatigue life for matrix-dominated composite laminates , 1993 .

[28]  E. W. C. Wilkins,et al.  Cumulative damage in fatigue , 1956 .

[29]  S. V. Kulkarni,et al.  Fatigue of notched fiber composite laminates - Analytical and experimental evaluation , 1977 .