Polystyrene foams. I. Processing‐structure relationships

In this study, processing-structure relationships in expanded polystyrene (EPS) made using near-critical carbon dioxide as a physical blowing agent were investigated. In order to investigate the relationship between structure and properties of EPS it was necessary to be able to make samples with a wide range of controlled structures. For this reason, a systematic investigation of the relationship between processing conditions and structure was performed based on a statistical experimental design. Regression analysis was conducted on the data and expressions were developed to quantify the relationships between structural parameters and processing conditions. The samples were saturated with carbon dioxide at relatively high pressure and ambient temperature and the saturated specimens were expanded at elevated temperatures. The importance of the individual processing parameters was determined. Statistical analysis of data showed that foaming time was the most important factor determining foam density, whereas saturation pressure was the most important factor determining cell size and cell density. By controlling the foaming conditions, EPS samples having the same densities and different cell sizes were produced. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 1412–1420, 2003

[1]  D. R. Lloyd,et al.  Microporous membrane formation via thermally-induced phase separation. II: Liquid-liquid phase separation , 1991 .

[2]  R. Pekala,et al.  Organic aerogels from the polycondensation of resorcinol with formaldehyde , 1989 .

[3]  Chul B. Park,et al.  An extrusion system for the processing of microcellular polymer sheets: Shaping and cell growth control , 1996 .

[4]  T. J. McCarthy,et al.  Preparation and Characterization of Microcellular Polystyrene Foams Processed in Supercritical Carbon Dioxide , 1998 .

[5]  M. Ohshima,et al.  Polymeric Foaming Simulation for Extrusion Processes , 2001 .

[6]  Saeed Doroudiani,et al.  Sorption and diffusion of carbon dioxide in wood‐fiber/polystyrene composites , 2002 .

[7]  A. Lele,et al.  Morphology of polymers precipitated from a supercritical solvent , 1992 .

[8]  J. Torkelson,et al.  The roles of phase separation mechanism and coarsening in the formation of poly(methyl methacrylate) asymmetric membranes , 1990 .

[9]  Alan N. Gent,et al.  Nucleation and Growth of Gas Bubbles in Elastomers , 1969 .

[10]  J. E. Mark,et al.  Microcellular foams from polyethersulfone and polyphenylsulfone. Preparation and mechanical properties , 2002 .

[11]  D. J. Dixon,et al.  Microcellular microspheres and microballoons by precipitation with a vapour-liquid compressed fluid antisolvent , 1994 .

[12]  R. Bodmeier,et al.  Preparation of Biodegradable Poly(±)lactide Microparticles Using a Spray‐Drying Technique , 1988, The Journal of pharmacy and pharmacology.

[13]  J. Aubert,et al.  Low-density, microcellular polystyrene foams , 1985 .

[14]  Sumarno,et al.  Production of polystyrene microcellular foam plastics and a comparison of late- and quick-heating † , 2000 .

[15]  Michael E. Paulaitis,et al.  GLASS TRANSITIONS IN POLYMER/CO2 MIXTURES AT ELEVATED PRESSURES , 1991 .

[16]  D. Willoughby,et al.  The local modulation of vascular permeability by endothelial cell derived products , 1988, The Journal of pharmacy and pharmacology.

[17]  Chul B. Park,et al.  Filamentary extrusion of microcellular polymers using a rapid decompressive element , 1996 .

[18]  D. Baird,et al.  Impact toughening of polycarbonate by microcellular foaming , 1994 .

[19]  N. Suh,et al.  A process for making microcellular thermoplastic parts , 1990 .

[20]  Dean W. Matson,et al.  Rapid expansion of supercritical fluid solutions: solute formation of powders, thin films, and fibers , 1987 .

[21]  Jean W. Tom,et al.  Particle formation with supercritical fluids—a review , 1991 .

[22]  J. S. Furno,et al.  COMPOSITIONAL QUENCHING: A PROCESS FOR FORMING POLYMER-IN-POLYMER MICRODISPERSIONS AND COCONTINUOUS NETWORKS , 1988 .

[23]  R. Landel,et al.  The Temperature Dependence of Relaxation Mechanisms in Amorphous Polymers and Other Glass-Forming Liquids , 1955 .

[24]  K. Khemani.  Extruded Polyester Foams , 1997 .

[25]  Y. Kawashima,et al.  Preparation of multiple unit hollow microspheres (microballoons) with acrylic resin containing tranilast and their drug release characteristics (in vitro) and floating behavior (in vivo) , 1991 .

[26]  J. W. Barlow,et al.  Plasticization of glassy polymers by CO2 , 1985 .

[27]  I. Sanchez,et al.  Glass transition behavior including retrograde vitrification of polymers with compressed fluid diluents , 1992 .