Based on stochastic crack growth model, the effects of material variations on aircraft inspection schedules are investigated in this paper. Fatigue tests are performed to obtain the log standard deviation of fatigue lives due to material variations. The test materials are 7475-T7351, 7050-T7451, 2024-T851 and 2124-T851. The effects of material variation on inspection schedule are significant. For a large material variation, the inspection schedule should be shortened for conservative consideration. The effects of sample size on the material variation under 50% and 95% confidence levels are investigated numerically. The results of this study provide a guideline to allocate resources of fleet planning more realistically by compromising between the cost (or time) of fatigue experiments and aircraft inspections.

[1]  J. N. Yang,et al.  Aircraft fleet maintenance based on structural reliability analysis , 1994 .

[2]  S. D. Manning,et al.  A simple second order approximation for stochastic crack growth analysis , 1996 .

[3]  Jin Xing,et al.  A simple log normal random process approach of the fatigue crack growth considering the distribution of initial crack size and loading condition , 1997 .

[4]  P. Bowen,et al.  On predicting small fatigue crack growth and fatigue life from long crack data in 2024 aluminium alloy , 2003 .

[5]  Wen-Fang Wu,et al.  A study of stochastic fatigue crack growth modeling through experimental data , 2003 .

[6]  Wen-Fang Wu,et al.  Probabilistic models of fatigue crack propagation and their experimental verification , 2004 .

[7]  Statistical analysis of high cycle fatigue crack growth: center crack in aluminum panel , 1996 .

[8]  L. Min,et al.  Large sample size experimental investigation on the statistical nature of fatigue crack initiation and growth , 1996 .

[9]  A. Ray,et al.  Stochastic modeling of fatigue crack propagation , 1998 .

[10]  Asok Ray,et al.  A stochastic model of fatigue crack propagation under variable-amplitude loading , 1999 .

[11]  G. C. Salivar,et al.  Statistical modeling of fatigue-crack growth in a nickel-base superalloy , 1983 .

[12]  James W. Provan,et al.  Probabilistic fracture mechanics and reliability , 1987 .

[13]  J. N. Yang,et al.  Fatigue reliability of gas turbine engine components under scheduledinspection maintenance , 1985 .

[14]  S. D. Manning,et al.  Stochastic crack growth analysis methodologies for metallic structures , 1990 .

[15]  J. N. Yang,et al.  Statistical Crack Propagation in Fastener Holes Under Spectrum Loading , 1983 .