Key results from irradiation and post-irradiation examination of AGR-1 UCO TRISO fuel

Abstract The AGR-1 irradiation experiment was performed as the first test of tristructural isotropic (TRISO) fuel in the US Advanced Gas Reactor Fuel Development and Qualification Program. The experiment consisted of 72 right cylinder fuel compacts containing approximately 3 × 105 coated fuel particles with uranium oxide/uranium carbide (UCO) fuel kernels. The fuel was irradiated in the Advanced Test Reactor for a total of 620 effective full power days. Fuel burnup ranged from 11.3 to 19.6% fissions per initial metal atom and time-average, volume-average irradiation temperatures of the individual compacts ranged from 955 to 1136 °C. This paper focuses on key results from the irradiation and post-irradiation examination, which revealed a robust fuel with excellent performance characteristics under the conditions tested and have significantly improved the understanding of UCO coated particle fuel irradiation behavior. The fuel exhibited zero TRISO coating failures (failure of all three dense coating layers) during irradiation and post-irradiation safety testing at temperatures up to 1700 °C. Advanced PIE methods have allowed particles with SiC coating failure that were discovered to be present in a very-low population to be isolated and meticulously examined, which has elucidated the specific causes of SiC failure in these specimens. The level of fission product release from the fuel during irradiation and post-irradiation safety testing has been studied in detail. Results indicated very low release of krypton and cesium through intact SiC and modest release of europium and strontium, while also confirming the potential for significant silver release through the coatings depending on irradiation conditions. Focused study of fission products within the coating layers of irradiated particles down to nanometer length scales has provided new insights into fission product transport through the coating layers and the role various fission products may have on coating integrity. The broader implications of these results and the application of lessons learned from AGR-1 to fuel fabrication and post-irradiation examination for subsequent fuel irradiation experiments as part of the US fuel program are also discussed.

[1]  B. Collin.  AGR-1 Irradiation Test Final As-Run Report, Rev. 3 , 2015 .

[2]  B. Collin,et al.  AGR-1 Irradiation Test Final As-Run Report , 2012 .

[3]  J. Riesterer,et al.  Electron microscopic evaluation and fission product identification of irradiated TRISO coated particles from the AGR-1 experiment: A preliminary review , 2014 .

[4]  John D. Hunn,et al.  Fabrication and Comparison of Fuels for Advanced Gas Reactor Irradiation Tests , 2010 .

[5]  D. Petti,et al.  Comparison of silver, cesium, and strontium release predictions using PARFUME with results from the AGR-1 irradiation experiment , 2015 .

[6]  T. Lillo,et al.  Identification of silver and palladium in irradiated TRISO coated particles of the AGR-1 experiment , 2014 .

[7]  H. O. Mosca,et al.  Point defects in thorium nitride: A first-principles study , 2016 .

[8]  D. Keiser,et al.  Advantages and Disadvantages of using a Focused Ion Beam to Prepare TEM Samples From Irradiated U-10Mo Monolithic Nuclear Fuel , 2012 .

[9]  Kazuo Minato,et al.  Fission product behavior in Triso-coated UO2 fuel particles , 1994 .

[10]  S. Blaine Grover,et al.  Completion of the First NGNP Advanced Gas Reactor Fuel Irradiation Experiment, AGR-1, in the Advanced Test Reactor , 2010 .

[11]  John D. Hunn,et al.  Detection and analysis of particles with failed SiC in AGR-1 fuel compacts , 2016 .

[12]  John D. Hunn,et al.  Initial results from safety testing of US AGR-2 irradiation test fuel , 2017 .

[13]  P. Demkowicz,et al.  First high temperature safety tests of AGR-1 TRISO fuel with the Fuel Accident Condition Simulator (FACS) furnace , 2015 .

[15]  J. Hunn,et al.  SiC layer microstructure in AGR-1 and AGR-2 TRISO fuel particles and the influence of its variation on the effective diffusion of key fission products , 2016 .

[16]  T. Lillo,et al.  Influence of SiC grain boundary character on fission product transport in irradiated TRISO fuel , 2016 .

[17]  John D. Hunn,et al.  PIE on Safety-Tested Loose Particles from Irradiated Compact 4-4-2 , 2016 .

[18]  Kazuo Minato,et al.  Fission product palladium-silicon carbide interaction in htgr fuel particles , 1990 .

[19]  John D. Hunn,et al.  Initial examination of fuel compacts and TRISO particles from the US AGR-2 irradiation test , 2017 .

[20]  G. Jellison,et al.  Increase in pyrolytic carbon optical anisotropy and density during processing of coated particle fuel due to heat treatment , 2008 .

[21]  T. Lillo,et al.  Silicon carbide grain boundary distributions, irradiation conditions, and silver retention in irradiated AGR-1 TRISO fuel particles , 2017 .

[22]  H. Nabielek,et al.  Silver Release from Coated Particle Fuel , 1977 .

[23]  Detlev Stöver,et al.  Diffusion of Silver and Cesium in Silicon-Carbide Coatings of Fuel Particles for High-Temperature Gas-Cooled Reactors , 1983 .

[24]  John Saurwein,et al.  The DOE advanced gas reactor fuel development and qualification program , 2005 .

[25]  J. Harp,et al.  Analysis of Fission Products on the AGR-1 Capsule Components , 2013 .

[26]  H. Nabielek,et al.  COATED PARTICLE FUEL FOR HIGH TEMPERATURE GAS COOLED REACTORS , 2007 .

[27]  Timothy D. Burchell,et al.  A novel approach to fabricating fuel compacts for the next generation nuclear plant (NGNP) , 2008 .

[28]  T. Lillo,et al.  Associations of Pd, U and Ag in the SiC layer of neutron-irradiated TRISO fuel , 2015 .

[29]  John D. Hunn,et al.  Irradiation performance of AGR-1 high temperature reactor fuel , 2016 .