An exploration of binder jetting of copper

Purpose – The purpose of this paper is to explore the use of binder jetting to fabricate high-purity copper parts. The ability to fabricate geometrically complex copper shapes would have implications on the design and manufacture of components for thermal management systems and structural electronics. Design/methodology/approach – To explore the feasibility of processing copper via binder jetting, the authors followed an established material development process that encompasses powder selection and tuning process parameters in printing and thermal cycles. Specifically, the authors varied powder size and sintering cycles to explore their effects on densification. Findings – Three differently sized copper powders were successfully printed, followed by sintering in a reducing atmosphere. It was found that a 15-μm-diameter powder with a sintering cycle featuring a 1,080°C maximum temperature provides the most dense (85 per cent) and pure (97 per cent) final copper parts of the parameters tested. Research limi...

[1]  Michael J. Cima,et al.  Microstructural Elements of Components Derived from 3D Printing , 1992 .

[2]  K. Leong,et al.  Solid freeform fabrication of three-dimensional scaffolds for engineering replacement tissues and organs. , 2003, Biomaterials.

[3]  Joel W. Barlow,et al.  Metal Parts From Selective Laser Sintering of Metal-Polymer Powders , 1992 .

[4]  Mark A. Ganter,et al.  A review of process development steps for new material systems in three dimensional printing (3DP) , 2008 .

[5]  D. Hutmacher,et al.  Scaffold development using 3D printing with a starch-based polymer , 2002 .

[6]  Christopher B. Williams,et al.  Lightweight metal cellular structures via indirect 3D printing and casting , 2012 .

[7]  Injection moulding of oxide reduced copper powders , 2005 .

[8]  Mark A. Ganter,et al.  Development Process for Custom Three-Dimensional Printing (3DP) Material Systems , 2010 .

[9]  Joe Hiemenz,et al.  Electron beam melting , 2007 .

[10]  Ryan B. Wicker,et al.  Open-cellular copper structures fabricated by additive manufacturing using electron beam melting , 2011 .

[11]  R. Balluffi,et al.  The mechanism of sintering of copper , 1957 .

[12]  David W. Rosen,et al.  A Brief History of Additive Manufacturing and the 2009 Roadmap for Additive Manufacturing: Looking Back and Looking Ahead , 2009 .

[13]  S. Babu,et al.  Thermal transients during processing of materials by very high power ultrasonic additive manufacturing , 2011 .

[14]  Bee Yen Tay,et al.  Processing of polycaprolactone porous structure for scaffold development , 2007 .

[15]  L. Murr,et al.  Metal Fabrication by Additive Manufacturing Using Laser and Electron Beam Melting Technologies , 2012 .

[16]  K. Hayashi,et al.  Effects of Equilibrium Pressure of Gas Generated by Ruduction Reaction on Sintering Densification of MIM Fine Powders , 1993 .

[17]  Ryan B. Wicker,et al.  Novel precipitate–microstructural architecture developed in the fabrication of solid copper components by additive manufacturing using electron beam melting , 2011 .

[18]  Benjamin M. Wu,et al.  Scaffold fabrication by indirect three-dimensional printing. , 2005, Biomaterials.

[19]  Tushar Ramkrishna Mahale,et al.  Electron beam melting of advanced materials and structures. , 2009 .

[20]  Matt Short,et al.  Bonding characteristics during very high power ultrasonic additive manufacturing of copper , 2010 .

[21]  Christopher B. Williams,et al.  The Effects of 3D Printed Molds on Metal Castings , 2013 .

[22]  J. Suwanprateeb,et al.  Three-dimensional printing of porous polyethylene structure using water-based binders. , 2006, Journal of biomedical materials research. Part B, Applied biomaterials.

[23]  Michael J. Cima,et al.  Structural Ceramic Components by 3D Printing , 1993 .

[24]  O. Harrysson,et al.  Design and characterization of orthotropic re-entrant auxetic structures made via EBM using Ti 6 Al 4 V and pure copper , 2011 .