Effect of Processing Techniques on the Microstructure and Mechanical Performance of High-Density Polyethylene

The versatility of high-density polyethylene (HDPE) makes it one of the most used polymers for vast applications ranging from food packaging to human implants. However, there still is confusion regarding the proper selection of processing techniques to produce HDPE specimens for high-end applications. Herein, we compare the processing of HDPE by two relevant techniques: compression and injection molding. The fabricated samples were studied using uniaxial tensile testing to determine their mechanical performance. Furthermore, the microstructure of samples was analyzed using different characterization techniques. Compression-molded specimens recorded a higher degree of crystallinity (DC) using two different characterization techniques such as differential scanning calorimetry (DSC) and X-ray diffraction (XRD). With this information, critical processing factors were determined, and a general structure–property relationship was established. It was demonstrated that having a higher DC resulted in higher yield strength and Young’s modulus. Furthermore, premature failure was observed in the injection-molded specimens, resulting in lower mechanical performance. This premature failure was caused due to flow marks observed using scanning electron microscopy (SEM). Therefore, it is concluded that compression molding produces superior samples compared to injection molding.

[1]  Amir Hussain Idrisi,et al.  Impact of Prolonged Exposure of Eleven Years to Hot Seawater on the Degradation of a Thermoset Composite , 2021, Polymers.

[2]  Amir Hussain Idrisi,et al.  Investigation on the Durability of E-Glass/Epoxy Composite Exposed to Seawater at Elevated Temperature , 2021, Polymers.

[3]  J. Velasco-Hernández,et al.  Electro-magnetically modulated self-propulsion of swimming sperms via cervical canal , 2021, Biomechanics and Modeling in Mechanobiology.

[4]  S. Abdelsalam,et al.  Thermal transport of radiative Williamson fluid over stretchable curved surface , 2021, Thermal Science and Engineering Progress.

[5]  M. M. Bhatti,et al.  Thermodynamic entropy of a magnetized Ree‐Eyring particle‐fluid motion with irreversibility process: A mathematical paradigm , 2020, ZAMM - Journal of Applied Mathematics and Mechanics / Zeitschrift für Angewandte Mathematik und Mechanik.

[6]  M. Khalid,et al.  Effect of radiation on the mechanical, morphological and thermal properties of HDPE/rPTFE blends , 2020 .

[7]  I. Barsoum,et al.  Impact Strengthening of Laminated Kevlar/Epoxy Composites by Nanoparticle Reinforcement , 2020, Polymers.

[8]  S. Abdelsalam,et al.  Leveraging elasticity to uncover the role of Rabinowitsch suspension through a wavelike conduit , 2020, Mathematics.

[9]  Nizamudeen Cherupurakal,et al.  Study on the thermal stability of stabilized and unstabilized low-density polyethylene films , 2020, Polymer Bulletin.

[10]  A. Fatemi,et al.  Tensile Behavior of High-Density Polyethylene Including the Effects of Processing Technique, Thickness, Temperature, and Strain Rate , 2020, Polymers.

[11]  S. Ramadas,et al.  Crystallisation behaviour of composites of HDPE and MWCNTs: The effect of nanotube dispersion, orientation and polymer deformation , 2020 .

[12]  A. Mourad,et al.  Upcycling of HDPE Waste using Additive Manufacturing: Feasibility and Challenges , 2020, 2020 Advances in Science and Engineering Technology International Conferences (ASET).

[13]  S. Abdelsalam,et al.  THE INTEGRATED THERMAL EFFECT IN CONJUNCTION WITH SLIP CONDITIONS ON PERISTALTICALLY INDUCED PARTICLE-FLUID TRANSPORT IN A CATHETERIZED PIPE , 2020 .

[14]  Dinu Thomas Thekkuden,et al.  Mechanical Performance Assessment of Internally-Defected Materials Manufactured Using Additive Manufacturing Technology , 2019, Journal of Manufacturing and Materials Processing.

[15]  Amir Hussain Idrisi,et al.  Long-term durability of thermoset composites in seawater environment , 2019, Composites Part B: Engineering.

[16]  A. Mourad,et al.  Impact of co-mixing technique and surface modification of ZnO nanoparticles using stearic acid on their dispersion into HDPE to produce HDPE/ZnO nanocomposites , 2019, Polymers and Polymer Composites.

[17]  S. Somiya,et al.  Estimating the creep behavior of glass-fiber-reinforced polyamide considering the effects of crystallinity and fiber volume fraction , 2018, Mechanics of Advanced Materials and Modern Processes.

[18]  M. Haque,et al.  Effect of TiO2 Nanofiller Concentration on the Mechanical, Thermal and Biological Properties of HDPE/TiO2 Nanocomposites , 2018, Journal of Materials Engineering and Performance.

[19]  A. S. Luyt,et al.  Thermal and mechanical properties of PP/HDPE/wood powder and MAPP/HDPE/wood powder polymer blend composites , 2017 .

[20]  Hifsa Pervez,et al.  On the Injection Molding Processing Parameters of HDPE-TiO2 Nanocomposites , 2017, Materials.

[21]  V. Lorenzo,et al.  Photodegradation characterization and heterogeneity evaluation of the exposed and unexposed faces of stabilized and unstabilized LDPE films , 2016 .

[22]  A. Mourad,et al.  Durability of mono-layer versus tri-layers LDPE films used as greenhouse cover: Comparative study , 2016 .

[23]  Hifsa Pervez,et al.  Optimization of Injection Molding Parameters for HDPE/TiO2 Nanocomposites Fabrication with Multiple Performance Characteristics Using the Taguchi Method and Grey Relational Analysis , 2016, Materials.

[24]  M. Paoli,et al.  Curaua fiber reinforced high-density polyethylene composites: effect of impact modifier and fiber loading , 2016 .

[25]  Chuntai Liu,et al.  Enhancing oriented crystals in injection-molded HDPE through introduction of pre-shear , 2015 .

[26]  I. Krupa,et al.  Thermal and mechanical characterization of injection moulded high density polyethylene/paraffin wax blends as phase change materials , 2014 .

[27]  A. Mourad,et al.  NanoTiO2-Enriched Biocompatible Polymeric Powder Coatings: Adhesion, Thermal and Biological Characterizations , 2014 .

[28]  A. Mourad,et al.  On use of trilayer low density polyethylene greenhouse cover as substitute for monolayer cover , 2014 .

[29]  B. Tisserat,et al.  Properties of High Density Polyethylene – Paulownia Wood Flour Composites via Injection Molding , 2013 .

[30]  M. Ouali,et al.  Analysis of Thermal Ageing Effect (Hold Time - Crystallinity Rate - Mechanical Property) on High Density Polyethylene (HDPE) , 2013 .

[31]  Abdel-Hamid I. Mourad,et al.  Degradation assessment of LDPE multilayer films used as a greenhouse cover: Natural and artificial aging impacts , 2012 .

[32]  A. Mourad,et al.  Ageing Effect on the Properties of Tri-Layer Polyethylene Film Used as Greenhouse Roof , 2011 .

[33]  A. Mourad.  Thermo-mechanical characteristics of thermally aged polyethylene/polypropylene blends , 2010 .

[34]  A. Mourad,et al.  Impact of some environmental conditions on the tensile, creep-recovery, relaxation, melting and crystallinity behaviour of UHMWPE-GUR 410-medical grade , 2009 .

[35]  A. Mourad,et al.  Characterisation of thermally treated and untreated polyethylene–polypropylene blends using DSC, TGA and IR techniques , 2009 .

[36]  B. Basu,et al.  HDPE-Al2O3-HAp composites for biomedical applications: processing and characterizations. , 2009, Journal of biomedical materials research. Part B, Applied biomaterials.

[37]  Huilin Li,et al.  Morphology and mechanical properties of injection‐molded ultrahigh molecular weight polyethylene/polypropylene blends and comparison with compression molding , 2008 .

[38]  B. Blümich,et al.  The effect of temperature and annealing on the phase composition, molecular mobility and the thickness of domains in high-density polyethylene , 2007 .

[39]  Christopher Y. Li,et al.  Morphology and Crystallization Behavior of HDPE/CNT Nanocomposite , 2006 .

[40]  D. J. Lee.  Comparison of Mechanical Properties of Compression and Injection Molded PEEK/Carbon Fiber Reinforced Composites , 2006 .

[41]  G. Zhong,et al.  Injection molding-induced morphology of thermoplastic polymer blends , 2005 .

[42]  A. Błędzki,et al.  Wood Fiber Reinforced Polypropylene Composites: Compression and Injection Molding Process , 2004 .

[43]  D. Barton,et al.  Ultra high molecular weight polyethylene deformation and fracture behaviour as a function of high strain rate and triaxial state of stress , 2013 .

[44]  John Lambros,et al.  Strain rate effects on the thermomechanical behavior of polymers , 2001 .

[45]  H. E. Kadi,et al.  Injection and compression molding of polystyrene/high‐density polyethylene blends—phase morphology and tensile behavior , 1997 .

[46]  S. K. Maiti,et al.  Influence of state of stress on mixed mode stable crack growth through D16AT aluminium alloy , 1995 .

[47]  James L White,et al.  Phase morphology of injection‐molded blends of nylon‐6 and polyethylene and comparison with compression molding , 1991 .

[48]  D. Uhlmann,et al.  Ductile–brittle transition in polymers , 1984 .

[49]  S. Aggarwal,et al.  Determination of crystallinity in polyethylene by X‐ray diffractometer , 1955 .