Thickness dependence of exchange anisotropy in NiFe/IrMn bilayers studied by Planar Hall Effect

Abstract Planar Hall Effect (PHE) in NiFe( t )/IrMn(10.0 nm) thin film structures has been experimentally investigated as a function of NiFe thickness in the range from 3 to 20 nm, under the applied magnetic field perpendicular to the easy axis. The PHE voltage change and its field sensitivity increase with NiFe thickness, but the field interval of two voltage maxima decreases with the thickness. There are good agreements between measured and calculated PHE voltage profiles, where the parameters of exchange-biased and effective anisotropy fields have been characterized to decrease with NiFe thickness. However, an anisotropic resistivity change increases as the NiFe thickness increases. These analyses suggest that PHE is the effective method, inferred to single domain, to determine the electrical and magnetic parameters in magnetic devices.

[1]  K. V. Rao,et al.  Determination of exchange anisotropy by means of ac susceptometry in Co/CoO bilayers , 1997 .

[2]  U. Gradmann.  Magnetic surface anisotropies , 1986 .

[3]  B. Diény,et al.  Large anomalous enhancement of perpendicular exchange bias by introduction of a nonmagnetic spacer between the ferromagnetic and antiferromagnetic layers , 2003 .

[4]  Dong Young Kim,et al.  Thickness dependence of planar Hall resistance and field sensitivity in NiO(30 nm)/NiFe(t) bilayers , 2000 .

[5]  E. Dahlberg,et al.  Use of the anisotropic magnetoresistance to measure exchange anisotropy in Co/CoO bilayers , 1996 .

[6]  X. Hong,et al.  Giant planar Hall effect in colossal magnetoresistive La0.84Sr0.16MnO3 thin films , 2004, cond-mat/0404291.

[7]  Jeffrey R. Childress,et al.  Magnetic sensors for nanotesla detection using planar Hall effect , 1996 .

[8]  R. Miranda,et al.  Origin of the asymmetric magnetization reversal behavior in exchange-biased systems: competing anisotropies. , 2005, Physical review letters.

[9]  Robert C. O'Handley,et al.  Giant surface magnetostriction in polycrystalline Ni and NiFe films , 1994 .

[10]  B. Diény,et al.  Tailoring perpendicular exchange bias in [Pt/Co]-IrMn multilayers , 2005 .

[12]  G. Bayreuther,et al.  Magnetocrystalline volume and interface anisotropies in epitaxial films: Universal relation and Néel’s model (invited) , 2003 .

[13]  W. N. Wang,et al.  Investigation of exchange bias in FeMnC/FeMn bilayers , 2002 .

[14]  Tieying Yang,et al.  Exchange coupling and thermostability in NiFe/NiMn bilayers , 1999 .

[15]  D. Mapps,et al.  Exchange anisotropy in NiFe/FeMn bilayers studied by planar Hall effect , 2002 .