Libraries of methacrylic acid and oligo(ethylene glycol) methacrylate copolymers with LCST behavior

Homopolymers of methacrylic acid (MAA), monoethyleneglycol methyl ether methacrylate (MEOMA), diethyleneglycol methyl ether methacrylate (MEO2MA), oligo(ethyleneglycol) methyl ether methacrylate (OEGMA475 and OEGMA1100) and oligo(ethyleneglycol) ethyl ether methacrylate (OEGEMA246) were synthesized with various chain lengths via reversible addition fragmentation chain transfer (RAFT) polymerization. The homopolymers of MAA, MEOMA and OEGMA1100 did not show any cloud point (CP) in the range of 0–100 °C, whereas at a pH value of 7, the CPs were found to be 20.6, 93.7, and 20.0 °C for p(MEO2MA), p(OEGMA475) and p(OEGEMA246), respectively, with an initial monomer to initiator ratio of 50. Furthermore, statistical copolymer libraries of MAA with OEGMA475 and OEGMA1100 were prepared. The cloud points of the random copolymers of MAA and OEGMA475 were found to be in the range of 20–90 °C; surprisingly, even though the homopolymers of MAA and OEGMA1100 did not exhibit any LCST behavior, the copolymers of these monomers at certain molar ratios (up to 40% OEGMA1100) revealed a double responsive behavior for both temperature and pH. Finally, the cloud points were found to be in the range of 22–98 °C, measured at pH values of 2, 4, and 7, while no cloud point was detected at pH 10. © Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 7138–7147, 2008

[1]  J. Lutz,et al.  About the Phase Transitions in Aqueous Solutions of Thermoresponsive Copolymers and Hydrogels Based on 2-(2-methoxyethoxy)ethyl Methacrylate and Oligo(ethylene glycol) Methacrylate , 2007 .

[2]  D. Webster,et al.  Library synthesis and characterization of 3-aminopropyl-terminated poly(dimethylsiloxane)s and poly(ε-caprolactone)-b-poly(dimethylsiloxane)s , 2006 .

[3]  C. R. Becer,et al.  Optimization of the Nitroxide-Mediated Radical Polymerization Conditions for Styrene and tert-Butyl Acrylate in an Automated Parallel Synthesizer , 2006 .

[4]  D. Webster.  Combinatorial and High‐Throughput Methods in Macromolecular Materials Research and Development , 2008 .

[5]  U. Schubert,et al.  Automated parallel anionic polymerizations: Enhancing the possibilities of a widely used technique in polymer synthesis , 2005 .

[6]  D. Schmaljohann.  Thermo- and pH-responsive polymers in drug delivery. , 2006, Advanced drug delivery reviews.

[7]  S. Agarwal,et al.  Biocompatible, Thermoresponsive, and Biodegradable: Simple Preparation of “All-in-One” Biorelevant Polymers , 2007 .

[8]  Charles L. McCormick,et al.  Reversible addition–fragmentation chain transfer (RAFT) radical polymerization and the synthesis of water-soluble (co)polymers under homogeneous conditions in organic and aqueous media , 2007 .

[9]  S. Carlotti,et al.  Anionic Polymerizations of Oligo(ethylene glycol) Alkyl Ether Methacrylates: Effect of Side Chain Length and ω-Alkyl Group of Side Chain on Cloud Point in Water , 2008 .

[10]  J. Lutz,et al.  Polymerization of oligo(ethylene glycol) (meth)acrylates: Toward new generations of smart biocompatible materials , 2008 .

[11]  Jean-François Lutz,et al.  Point by point comparison of two thermosensitive polymers exhibiting a similar LCST: is the age of poly(NIPAM) over? , 2006, Journal of the American Chemical Society.

[12]  Ulrich S. Schubert,et al.  Application of a Parallel Synthetic Approach in Atom‐Transfer Radical Polymerization: Set‐Up and Feasibility Demonstration , 2003 .

[13]  C. R. Becer,et al.  Water uptake of hydrophilic polymers determined by a thermal gravimetric analyzer with a controlled humidity chamber , 2007 .

[14]  H. G. Schild.  Poly(N-isopropylacrylamide): experiment, theory and application , 1992 .

[15]  C. Hawker,et al.  Initiating Systems for Nitroxide-Mediated ``Living'' Free Radical Polymerizations: Synthesis and Evaluation , 1996 .

[16]  C. R. Becer,et al.  MALDI-TOF MS coupled with collision-induced dissociation (CID) measurements of poly(methyl methacrylate) , 2008 .

[17]  A. Cooper,et al.  Structure-LCST relationships for end-functionalized water-soluble polymers: an "accelerated" approach to phase behaviour studies. , 2007, Chemical communications.

[18]  U. Schubert,et al.  The fast and the curious: High‐throughput experimentation in synthetic polymer chemistry , 2003 .

[19]  M. Pitsikalis,et al.  Polymers with complex architecture by living anionic polymerization. , 2001, Chemical reviews.

[20]  Renzo M. Paulus,et al.  Tunable pH- and Temperature-Sensitive Copolymer Libraries by Reversible Addition−Fragmentation Chain Transfer Copolymerizations of Methacrylates , 2007 .

[21]  S. Aoshima,et al.  Synthesis of Stimuli-Responsive Polymers by Living Polymerization: Poly(N-Isopropylacrylamide) and Poly(Vinyl Ether)s , 2007 .

[22]  J. Hedrick,et al.  Structure—property relationships in perfectly alternating segmented polysulphone/poly(dimethylsiloxane) copolymers , 1988 .

[23]  Mar Michael Meier,et al.  Automated parallel investigations/optimizations of the reversible addition‐fragmentation chain transfer polymerization of methyl methacrylate , 2004 .

[24]  B. Sumerlin,et al.  Versatile Pathway to Functional Telechelics via RAFT Polymerization and Click Chemistry , 2007 .

[25]  Lei Tao,et al.  Design and synthesis of N-maleimido-functionalized hydrophilic polymers via copper-mediated living radical polymerization: a suitable alternative to PEGylation chemistry. , 2005, Journal of the American Chemical Society.

[26]  S. Armes,et al.  Facile Atom Transfer Radical Polymerization of Methoxy-Capped Oligo(ethylene glycol) Methacrylate in Aqueous Media at Ambient Temperature , 2000 .

[27]  J. Chiefari,et al.  Living free-radical polymerization by reversible addition - Fragmentation chain transfer: The RAFT process , 1998 .

[28]  N. Peppas,et al.  Preparation and Characterization of pH-Responsive Poly(methacrylic acid-g-ethylene glycol) Nanospheres , 2002 .

[29]  G. Mao,et al.  Dually responsive multiblock copolymers via reversible addition- fragmentation chain transfer polymerization: Synthesis of temperature- and redox-responsive copolymers of poly(N-isopropylacrylamide) and poly(2-(dimethylamino)ethyl methacrylate) , 2007 .

[30]  U. Schubert,et al.  High-throughput synthesis and screening of a library of random and gradient copoly(2-oxazoline)s. , 2006, Journal of combinatorial chemistry.

[31]  Baorui Liu,et al.  Thermo and pH Dual‐Responsive Nanoparticles for Anti‐Cancer Drug Delivery , 2007 .

[32]  M. Sawamoto,et al.  Polymerization of Methyl Methacrylate with the Carbon Tetrachloride/Dichlorotris- (triphenylphosphine)ruthenium(II)/Methylaluminum Bis(2,6-di-tert-butylphenoxide) Initiating System: Possibility of Living Radical Polymerization , 1995 .

[33]  K. Matyjaszewski,et al.  The effect of structure on the thermoresponsive nature of well‐defined poly(oligo(ethylene oxide) methacrylates) synthesized by ATRP , 2008 .

[34]  A. Mathur,et al.  Polymeric emulsifiers based on reversible formation of hydrophobic units , 1998, Nature.

[35]  C. R. Becer,et al.  Acetyl Halide Initiator Screening for the Cationic Ring‐Opening Polymerization of 2‐Ethyl‐2‐Oxazoline , 2008 .

[36]  H. D. H. Stöver,et al.  Cross-Linked Poly(methacrylic acid-co-poly(ethylene oxide) methyl ether methacrylate) Microspheres and Microgels Prepared by Precipitation Polymerization: A Morphology Study , 2002 .

[37]  Curtis W. Frank,et al.  A microfluidic actuator based on thermoresponsive hydrogels , 2003 .

[38]  Axel H. E. Müller,et al.  Thermosensitive water-soluble copolymers with doubly responsive reversibly interacting entities , 2007 .

[39]  T. Ishizone,et al.  Synthesis of Thermally Sensitive Water-Soluble Polymethacrylates by Living Anionic Polymerizations of Oligo(ethylene glycol) Methyl Ether Methacrylates , 2003 .

[40]  E. Gil,et al.  Stimuli-reponsive polymers and their bioconjugates , 2004 .

[41]  X. Kong,et al.  Thermoresponsive copolymers of methacrylic acid and poly(ethylene glycol) methyl ether methacrylate , 2005 .

[42]  H. D. H. Stöver,et al.  Well-Defined Amphiphilic Thermosensitive Copolymers Based on Poly(ethylene glycol monomethacrylate) and Methyl Methacrylate Prepared by Atom Transfer Radical Polymerization , 2004 .

[43]  Renzo M. Paulus,et al.  Synthesis and Structure-Property Relationships of Random and Block Copolymers: A Direct Comparison for Copoly(2-oxazoline)s , 2007 .

[44]  Graeme Moad,et al.  A more versatile route to block copolymers and other polymers of complex architecture by living radical polymerization : The RAFT process , 1999 .

[45]  Krzysztof Matyjaszewski,et al.  Controlled/"living" radical polymerization. atom transfer radical polymerization in the presence of transition-metal complexes , 1995 .

[46]  Yan Xia,et al.  End group effect on the thermal response of narrow-disperse poly (n -isopropylacrylamide) prepared by atom transfer radical polymerization , 2006 .

[47]  O. Webster.  Living Polymerization Methods , 1991, Science.

[48]  Elazer R. Edelman,et al.  Adv. Drug Delivery Rev. , 1997 .

[49]  René M. Rossi,et al.  Temperature-responsive polymers with LCST in the physiological range and their applications in textiles , 2007 .

[50]  D. Neugebauer.  Graft copolymers with poly(ethylene oxide) segments , 2007 .

[51]  R. Hoogenboom.  Poly(2‐oxazoline)s: Alive and Kicking , 2007 .