Blue emission from Tm-doped GaN electroluminescent devices

Blue emission has been obtained at room temperature from Tm-doped GaN electroluminescent devices. The GaN was grown by molecular beam epitaxy on Si(111) substrates using solid sources (for Ga and Tm) and a plasma source for N2. Indium–tin–oxide was deposited on the GaN layer and patterned to provide both the bias (small area) and ground (large area) transparent electrodes. Strong blue light emission under the bias electrode was observable with the naked eye at room temperature. The visible emission spectrum consists of a main contribution in the blue region at 477 nm corresponding to the Tm transition from the 1G4 to the 3H6 ground state. A strong near-infrared peak was also observed at 802 nm. The relative blue emission efficiency was found to increase linearly with bias voltage and current beyond certain turn-on levels.

[1]  Ian G. Brown,et al.  Visible cathodoluminescence of GaN doped with Dy, Er, and Tm , 1999 .

[2]  J. Kossanyi,et al.  Rare earth-doped polycrystalline zinc oxide electroluminescent ceramics , 1996 .

[3]  P. N. Yocom,et al.  Cathodoluminescence Efficiency of Tm+3 in Zinc Sulfide , 1971 .

[4]  M. Schubert,et al.  Optical phonons and free-carrier effects in MOVPE grown AlxGa1−xN measured by Infrared Ellipsometry , 1999 .

[5]  H. Poignant,et al.  Blue upconversion fluorozirconate fibre laser , 1990 .

[6]  F. Pellé,et al.  Excited state absorption mechanisms of red to UV and blue conversion luminescence in Tm3+ doped fluorophosphate glass , 1995 .

[7]  L. Esterowitz.  Diode pumped holmium, thulium and erbium lasers between 2 and 3 micrometers operating cw at room temperature , 1990 .

[8]  Andrew J. Steckl,et al.  Red light emission by photoluminescence and electroluminescence from Pr-doped GaN on Si substrates , 1999 .

[9]  A. Steckl,et al.  VISIBLE AND INFRARED RARE-EARTH-ACTIVATED ELECTROLUMINESCENCE FROM INDIUM TIN OXIDE SCHOTTKY DIODES TO GAN:ER ON SI , 1999 .

[10]  Robert A. Satten,et al.  Spectra and energy levels of rare earth ions in crystals , 1968 .

[11]  C. K. Jayasankar,et al.  Optical properties of Tm3+ ions in zinc borosulphate glasses and comparative energy level analyses of Tm3+ ions in various glasses , 1994 .

[12]  Gerald B. Stringfellow,et al.  High brightness light emitting diodes , 1997 .

[13]  A. Steckl,et al.  Green electroluminescence from Er-doped GaN Schottky barrier diodes , 1998 .

[14]  Andrew J. Steckl,et al.  Green emission from Er-doped GaN grown by molecular beam epitaxy on Si substrates , 1998 .

[15]  Andrew J. Steckl,et al.  Visible emission from Er-doped GaN grown by solid source molecular beam epitaxy , 1998 .