Scattering-controlled femtosecond-laser induced nanostructuring of TiO2 thin films

The formation of laser induced periodic surface structures (LIPSS) is to a large extent of self-organizing nature and in its early stages essentially influenced by optical scattering. The evolution of related mechanisms, however, has still to be studied in detail and strongly depends on materials and laser parameters. Excitation with highly intense ultrashort pulses leads to the creation of nanoripple structures with periods far below the fundamental wavelength because of opening multiphoton excitation channels. Because of the drastically reduced spatial scale of such laser induced periodic nanostructures (LIPNS), a particular influence of scattering is expected in this special case. Here we report on first investigations of femtosecond-laser induced nanostructuring of sputtered titanium dioxide (TiO2) layers in comparison to bulk material. The crucial role of the optical film quality for the morphology of the resulting LIPNS was worked out. Typical periods of nanoripples were found to be within the range of 80-180 nm for an excitation wavelength of 800 nm. Unlike our previously reported results on bulk TiO2, LIPNS in thin films appeared preferentially at low pulse numbers (N=5-20). This observation was explained by a higher number of scattering centers caused by the thin film structure and interfaces. The basic assumptions are further supported by supplementary experiments with polished and unpolished surfaces of bulk TiO2 single crystals.

[1]  B. Kumar,et al.  Submicrometre periodic surface structures in InP induced by nanosecond UV laser pulses , 2008 .

[2]  M. Maeda,et al.  Contact angle and biocompatibility of sol‐gel prepared TiO2 thin films for their use as semiconductor‐based cell‐viability sensors , 2008 .

[3]  Huijun Zhao,et al.  Novel TiO2 thin film with non-UV activated superwetting and antifogging behaviours , 2007 .

[4]  Wolfgang Kautek,et al.  Ablation experiments on polyimide with femtosecond laser pulses , 1999 .

[5]  Jeff F. Young,et al.  Laser-induced periodic surface structure. II. Experiments on Ge, Si, Al, and brass , 1983 .

[6]  Chunlei Guo,et al.  Effects of nanostructure-covered femtosecond laser-induced periodic surface structures on optical absorptance of metals , 2007 .

[7]  Heinz Sturm,et al.  Chemical, morphological and accumulation phenomena in ultrashort-pulse laser ablation of TiN in air , 2000 .

[8]  Annett Rechtenbach,et al.  The influence of pressure on the structure and the self-cleaning properties of sputter deposited TiO2 layers , 2010 .

[9]  H. Petek,et al.  Ultrafast interfacial proton-coupled electron transfer. , 2010, Chemical reviews.

[10]  H. Fu,et al.  Superhydrophilic anatase TiO2 film with the micro- and nanometer-scale hierarchical surface structure , 2008 .

[11]  A. Rosenfeld,et al.  Femtosecond-laser-induced quasiperiodic nanostructures on TiO2 surfaces , 2009 .

[12]  Feng Li,et al.  Amorphous TiO2 nanotube arrays for low-temperature oxygen sensors , 2008, Nanotechnology.

[13]  R. Taylor,et al.  Applications of femtosecond laser induced self‐organized planar nanocracks inside fused silica glass , 2008 .

[14]  Winnie Y. Y. Wong,et al.  Pulsed laser processings of polymer and ceramic surfaces. , 1997 .

[15]  Ruediger Grunwald,et al.  Extended-area nanostructuring of TiO2 with femtosecond laser pulses at 400 nm using a line focus , 2010, Nanotechnology.

[16]  Masaaki Sakakura,et al.  Application of femtosecond-laser induced nanostructures in optical memory. , 2007, Journal of nanoscience and nanotechnology.

[17]  R. Amal,et al.  Effect of film thickness and agglomerate size on the superwetting and fog-free characteristics of TiO2 films , 2009 .

[18]  K. Nguyen,et al.  Corrosion behavior and biocompatibility of nanostructured TiO2 film on Ti6Al4V. , 2007, Journal of biomedical materials research. Part A.

[19]  M. Grätzel,et al.  A low-cost, high-efficiency solar cell based on dye-sensitized colloidal TiO2 films , 1991, Nature.

[20]  Mengyan Shen,et al.  High-density regular arrays of nanometer-scale rods formed on silicon surfaces via femtosecond laser irradiation in water. , 2008, Nano letters.