Finite element modelling of damage induced by low-velocity impact on composite laminates

Abstract Progressive damage models based on continuum damage mechanics were used in combination with cohesive interface elements to predict the structural response and the failure mechanisms of composite laminates subjected to low-velocity impact. The potential of this simulation approach for correctly predicting the through-thickness distribution of internal damage was specifically examined in the study. The constitutive models for intralaminar and interlaminar damage modes were incorporated into the ABAQUS/Explicit FE code by user-defined VUMAT material subroutines. The results of numerical simulations were compared with experimental data obtained by drop-weight impact testing and stereoscopic X-radiography. The developed FE model provided a correct prediction of the structural impact response of laminated samples over the range of impact energies examined and successfully simulated the temporal sequence of the major damage mechanisms. A reasonably good agreement was also achieved between numerical predictions and experimental observations in terms of shapes, orientations and sizes of individual delaminations induced by impact at the different interfaces. Additional numerical analyses were also conducted to investigate the influence of simulated intralaminar damage modes on the prediction of interface delaminations. The analyses show that implementation of intralaminar damage modes may be required for accurate simulation of the three dimensional delamination pattern induced by impact.

[1]  Lorenzo Iannucci,et al.  Progressive failure modelling of woven carbon composite under impact , 2006 .

[2]  Lorenzo Iannucci,et al.  An energy based damage mechanics approach to modelling impact onto woven composite materials: Part II. Experimental and numerical results , 2007 .

[3]  P. Camanho,et al.  Numerical Simulation of Mixed-Mode Progressive Delamination in Composite Materials , 2003 .

[4]  Hiroshi Suemasu,et al.  Damage propagation in CFRP laminates subjected to low velocity impact and static indentation , 2007 .

[5]  Brian Falzon,et al.  Numerical analysis of intralaminar failure mechanisms in composite structures, Part II: Applications , 2011 .

[6]  Lorenzo Iannucci,et al.  Physically-based failure models and criteria for laminated fibre-reinforced composites with emphasis on fibre kinking: Part I: Development , 2006 .

[7]  Pedro P. Camanho,et al.  A continuum damage model for composite laminates: Part I - Constitutive model , 2007 .

[8]  Serge Abrate,et al.  Impact on Composite Structures , 1998 .

[9]  P.P. Camanho,et al.  A Three-dimensional Damage Model for Transversely Isotropic Composite Laminates , 2008 .

[10]  Raimund Rolfes,et al.  Modeling the inelastic deformation and fracture of polymer composites – Part I: Plasticity model , 2013 .

[11]  Constantinos Soutis,et al.  Prediction of the post-impact compressive strength of CFRP laminated composites , 1996 .

[12]  Raimund Rolfes,et al.  Modeling the inelastic deformation and fracture of polymer composites – Part II: Smeared crack model , 2013 .

[13]  Brian Falzon,et al.  Predicting low-velocity impact damage on a stiffened composite panel , 2010 .

[14]  Murray L. Scott,et al.  Review of delamination predictive methods for low speed impact of composite laminates , 2004 .

[15]  Pedro P. Camanho,et al.  A continuum damage model for composite laminates: Part II – Computational implementation and validation , 2007 .

[16]  Francesco Aymerich,et al.  Damage prediction in composite sandwich panels subjected to low-velocity impact , 2013 .

[17]  M.F.S.F. de Moura,et al.  Modelling the interaction between matrix cracking and delamination in carbon–epoxy laminates under low velocity impact , 2004 .

[18]  Dinh Chi Pham,et al.  Progressive Failure Analysis of Composites , 2008 .

[19]  René de Borst,et al.  Mesh-independent discrete numerical representations of cohesive-zone models , 2006 .

[20]  Zafer Gürdal,et al.  Low-velocity impact damage on dispersed stacking sequence laminates. Part II: Numerical simulations , 2009 .

[21]  H. Schürmann,et al.  FAILURE ANALYSIS OF FRP LAMINATES BY MEANS OF PHYSICALLY BASED PHENOMENOLOGICAL MODELS , 1998 .

[22]  Alberto Corigliano,et al.  Damage analysis of interlaminar fracture specimens , 1995 .

[23]  M R Wisnom,et al.  The role of delamination in failure of fibre-reinforced composites , 2012, Philosophical Transactions of the Royal Society A: Mathematical, Physical and Engineering Sciences.

[24]  Lorenzo Iannucci,et al.  An energy based damage mechanics approach to modelling impact onto woven composite materials-Part I: Numerical models , 2006 .

[25]  Michael R Wisnom,et al.  Modelling discrete failures in composites with interface elements , 2010 .

[26]  Francesco Aymerich,et al.  Simulation of multiple delaminations in impacted cross-ply laminates using a finite element model based on cohesive interface elements , 2009 .

[27]  Ping Zhu,et al.  Finite element analysis of low-velocity impact damage in composite laminated plates , 2006 .

[28]  Constantinos Soutis,et al.  Modelling damage evolution in composite laminates subjected to low velocity impact , 2012 .

[29]  Christophe Bouvet,et al.  Low velocity impact modelling in laminate composite panels with discrete interface elements , 2009 .

[30]  A. Amaro,et al.  Delamination Depth in Composites Laminates With Interface Elements and Ultrasound Analysis , 2011 .

[31]  Tong Earn Tay,et al.  Characterization and analysis of delamination fracture in composites: An overview of developments from 1990 to 2001 , 2003 .

[32]  Brian Falzon,et al.  A progressive failure model for composite laminates subjected to low velocity impact damage , 2008 .

[33]  Francesco Aymerich,et al.  Prediction of impact-induced delamination in cross-ply composite laminates using cohesive interface elements , 2008 .

[34]  Leif A. Carlsson,et al.  Experimental characterization of advanced composite materials , 1987 .

[35]  Brian Falzon,et al.  Numerical analysis of intralaminar failure mechanisms in composite structures, Part I: FE implementation , 2011 .

[36]  Pedro P. Camanho,et al.  Simulation of drop-weight impact and compression after impact tests on composite laminates , 2012 .

[37]  Christophe Bouvet,et al.  Discrete Impact Modeling of Inter- and Intra-laminar Failure in Composites , 2013 .

[38]  Venkata M. K. Akula,et al.  Review of Degradation Models for Progressive Failure Analysis of Fiber Reinforced Polymer Composites , 2009 .