Experimental investigation of the degradation mechanism of silicone rubber exposed to heat and gamma rays

Cable-grade silicone rubber was aged thermally or by combining heat and gamma-ray radiation, and resultant changes in chemical, thermal, mechanical and electrical properties were examined. The experimental results obtained in these analyses are clearly consistent with the mechanism that silicone rubber is degraded by forming cross-linked structures via formation of abundant siloxane bonds. With further progress of degradation, decomposition becomes dominant. Reflecting these mechanisms, mechanical properties deteriorate dramatically by losing elasticity. Both the real and imaginary parts of complex permittivity decrease, which is a contrastive difference from typical ageing behaviour of organic insulating polymers. In addition, both the elongation at break and indenter modulus are good indicators of degradation of silicone rubber.

[1]  Masaki Sugimoto,et al.  Degradation mechanisms of silicone rubber (SiR) by accelerated ageing for cables of nuclear power plant , 2014, IEEE Transactions on Dielectrics and Electrical Insulation.

[2]  Xinxiang Zhang,et al.  One-step sol–gel preparation of PDMS–silica ORMOSILs as environment-resistant and crack-free thick antireflective coatings , 2012 .

[3]  T. Seguchi,et al.  Mechanism of antioxidant interaction on polymer oxidation by thermal and radiation ageing , 2012 .

[4]  T. Ohshima,et al.  Degradation mechanisms of cable insulation materials during radiation–thermal ageing in radiation environment☆ , 2011 .

[5]  Y. Ohki,et al.  Diagnosis of surface degradation of flame-retardant ethylene propylene diene copolymer by scanning probe microscopy , 2016 .

[6]  Yoshimichi Ohki,et al.  Location feasibility of degradation in cable through Fourier transform analysis of broadband impedance spectra , 2012 .

[7]  Toshinori Kajiwara,et al.  Engineering ethics education on the basis of continuous education to improve communication ability , 2013 .

[8]  J. E. Mark,et al.  Characterization of PDMS model junctions and networks by solution and solid-state silicon-29 NMR spectroscopy , 1986 .

[9]  R. Harris,et al.  29Si nuclear magnetic resonance studies of oligomeric and polymeric siloxanes: 4. Chemical shift effects of end-groups , 1978 .

[10]  D. Fabiani,et al.  Dielectric spectroscopy as a condition monitoring technique for cable insulation based on crosslinked polyethylene , 2015 .

[11]  Javier Tamayo,et al.  Effects of elastic and inelastic interactions on phase contrast images in tapping-mode scanning force microscopy , 1997 .

[12]  Shiyu He,et al.  Damage effects and mechanisms of proton irradiation on methyl silicone rubber , 2003 .

[13]  Takayuki Yamada,et al.  Precise location of the excessive temperature points in polymer insulated cables , 2013, IEEE Transactions on Dielectrics and Electrical Insulation.

[14]  T. Seguchi,et al.  Degradation distribution in insulation materials of cables by accelerated thermal and radiation ageing , 2013, IEEE Transactions on Dielectrics and Electrical Insulation.

[15]  Lawrence E. Nielsen,et al.  Cross-Linking–Effect on Physical Properties of Polymers , 1969 .

[16]  Yuan Hu,et al.  Non-isothermal crystallization kinetics of silane crosslinked polyethylene , 2005 .

[17]  Adam Quintana,et al.  Gamma irradiation and oxidative degradation of a silica-filled silicone elastomer , 2015 .

[18]  G. Seytre,et al.  Irradiation effects on the relaxation behaviour of EPDM elastomers , 2004 .

[19]  Y. Ohki,et al.  Estimation of Talc Contents in Ethylene-Propylene-Diene Copolymer by Terahertz Absorption Spectroscopy , 2016 .

[20]  R. Arhart.  The chemistry of ethylene propylene insulation. II , 1993, IEEE Electrical Insulation Magazine.

[21]  A. Miller,et al.  Radiation Chemistry of Polydimethylsiloxane.1 I. Crosslinking and Gas Yields , 1960 .

[22]  Yoshimichi Ohki,et al.  Effects of the structure and insulation material of a cable on the ability of a location method by FDR , 2016, IEEE Transactions on Dielectrics and Electrical Insulation.