Acrylated hyperbranched polymer photoresist for ultra-thick and low-stress high aspect ratio micropatterns

Different photocurable acrylates, including two hyperbranched monomers, are compared with an epoxy negative-tone photoresist (SU-8) with respect to their suitability for the fabrication of ultra-thick polymer microstructures in a photolithographic process. To this end, a resolution pattern was used and key parameters, such as the maximum attainable thickness and aspect ratio, the minimum resolution and the processing time were determined. Compared to SU-8, all acrylate materials allowed the fabrication of thicker layers with a fast single layer fabrication procedure. Microstructures with thicknesses of up to 850 µm, an aspect ratio of up to 7.7, a 5.5-fold reduction in internal stress and a 6-fold reduction in processing time compared to SU-8 were demonstrated using an acrylated hyperbranched polyether. The specific development process of the hyperbranched polymer combined with channel design moreover enabled us to produce a high-performance valve for micro-battery devices.

[1]  C Gärtner,et al.  Polymer microfabrication methods for microfluidic analytical applications , 2000, Electrophoresis.

[2]  B. Löchel,et al.  Magnetically driven microstructures fabricated with multilayer electroplating , 1995 .

[3]  V. Michaud,et al.  Internal stress control in epoxy resins and their composites by material and process tailoring , 2002 .

[4]  Peter Vettiger,et al.  High-aspect-ratio, ultrathick, negative-tone near-UV photoresist and its applications for MEMS , 1998 .

[5]  Yves Leterrier,et al.  Time-intensity transformation and internal stress in UV-curable hyperbranched acrylates , 2007 .

[6]  G. Stoney.  The Tension of Metallic Films Deposited by Electrolysis , 1909 .

[7]  Fan-Gang Tseng,et al.  High aspect ratio ultrathick micro-stencil by JSR THB-430N negative UV photoresist , 2002 .

[8]  J. Månson,et al.  Structural and residual stress analysis of UV curable hyperbranched acrylates , 2005 .

[9]  Isabelle Chartier,et al.  Thick SU-8 photolithography for BioMEMS , 2003, SPIE MOEMS-MEMS.

[10]  N. Fabre,et al.  Potentialities of a new positive photoresist for the realization of thick moulds , 1999 .

[11]  A fast low-temperature micromolding process for hydrophilic microfluidic devices using UV-curable acrylated hyperbranched polymers , 2007 .

[12]  Wanjun Wang,et al.  Study on the postbaking process and the effects on UV lithography of high aspect ratio SU-8 microstructures , 2004 .

[13]  H. Becker,et al.  Polymer microfluidic devices. , 2002, Talanta.

[14]  Wanjun Wang,et al.  Using megasonic development of SU-8 to yield ultra-high aspect ratio microstructures with UV lithography , 2004 .

[15]  Kou Huiguang,et al.  Hyperbranched Acrylated Aromatic Polyester Used as a Modifier in UV-Curable Epoxy Acrylate Resins , 2010 .

[16]  Ren-Haw Chen,et al.  Development behaviours and microstructure quality of downward-development in deep x-ray lithography , 2001 .

[17]  J. Månson,et al.  A review of dendritic hyperbranched polymer as modifiers in epoxy composites , 2001 .

[18]  Y. Inoue,et al.  Mechanics of adhesive joints: Part III. Evaluation of residual stresses , 1958 .

[19]  R. Mülhaupt,et al.  Hyperbranched polyesters and their application in dental composites: monomers for low shrinking composites , 2001 .

[20]  N. D. Rooij,et al.  High aspect ratio UV photolithography for electroplated structures , 1999 .

[21]  Sunghwan Chang,et al.  Design, fabrication, and characterization of electrical and fluidic interconnections for a multi-chip microelectrofluidic bench , 2005, 18th IEEE International Conference on Micro Electro Mechanical Systems, 2005. MEMS 2005..

[22]  Gabi Gruetzner,et al.  Challenges of processing thick and ultrathick photoresist films , 2003, SPIE Advanced Lithography.