The Study on Sintering Capabilities of High Purity Metal Vanadium Powder

High purity metal vanadium powder was milled by high energy ball milling, and the grain size and morphology of vanadium powder was observed by electron probe, and the stress-strain curve was measured by CMT5305 universal testing machine for research of the mechanical property. In order to investigate the effect of sintering process on the property of product, the vanadium powder was sintered by the hot pressing sintering process and the cold isostatic pressing with vacuum sintering process respectively. The experimental results show that for the cold isostatic pressing with vacuum sintering process, the density of raw compact increases with the increase of pressing pressure. When the pressure increases to 280 MPa, the density and relative density of raw compact are 3.99 g·cm-3 and 66.94% respectively, the density and relative density of product after sintering are 5.28 g·cm-3 and 88.59% respectively. With the pressure increasing from 80 MPa to 200 MPa, the compressive strength increases significantly from 0.4 MPa to 6.0 MPa, the pressure increases to 280 MPa, the compressive strength slowly increases to 7.4 MPa. For the hot pressing sintering process, the relative density of product is higher than that of cold isostatic pressing with vacuum sintering process, and the density and relative density reach to 5.51 g·cm-3 and 92.91% respectively under 280 MPa pressure.