Emulation of neutron irradiation effects with protons: validation of principle

Abstract This paper presents the results of the irradiation, characterization and irradiation assisted stress corrosion cracking (IASCC) behavior of proton- and neutron-irradiated samples of 304SS and 316SS from the same heats. The objective of the study was to determine whether proton irradiation does indeed emulate the full range of effects of in-reactor neutron irradiation: radiation-induced segregation (RIS), irradiated microstructure, radiation hardening and IASCC susceptibility. The work focused on commercial heats of 304 stainless steel (heat B) and 316 stainless steel (heat P). Irradiation with protons was conducted at 360 °C to doses between 0.3 and 5.0 dpa to approximate those by neutron irradiation at 275 °C over the same dose range. Characterization consisted of grain boundary microchemistry, dislocation loop microstructure, hardness as well as stress corrosion cracking (SCC) susceptibility of both un-irradiated and irradiated samples in oxygenated and de-oxygenated water environments at 288 °C. Overall, microchemistry, microstructure, hardening and SCC behavior of proton- and neutron-irradiated samples were in excellent agreement. RIS analysis showed that in both heats and for both irradiating particles, the pre-existing grain boundary Cr enrichment transformed into a `W' shaped profile at 1.0 dpa and then into a `V' shaped profile between 3.0 and 5.0 dpa. Grain boundary segregation of Cr, Ni, Si, and Mo all followed the same trends and agreed well in magnitude. The microstructure of both proton- and neutron-irradiated samples was dominated by small, faulted dislocation loops. Loop size distributions were nearly identical in both heats over a range of doses. Saturated loop size following neutron irradiation was about 30% larger than that following proton irradiation. Loop density increased with dose through 5.0 dpa for both particle irradiations and was a factor of 3 greater in neutron-irradiated samples vs. proton-irradiated samples. Grain boundary denuded zones were only observed in neutron-irradiated samples. No cavities were observed for either irradiating particle. For both irradiating particles, hardening increased with dose for both heats, showing a more rapid increase and approach to saturation for heat B. In normal oxygenated water chemistry (NWC) at 288 °C, stress corrosion cracking in the 304 alloy was first observed at about 1.0 dpa and increased with dose. The 316 alloy was remarkably resistant to IASCC for both particle types. In hydrogen treated, de-oxygenated water (HWC), proton-irradiated samples of the 304 alloy exhibited IG cracking at 1.0 dpa compared to about 3.0 dpa for neutron-irradiated samples, although differences in specimen geometry, test condition and test duration can account for this difference. Cracking in heat P in HWC occurred at about 5.0 dpa for both irradiating particles. Thus, in all aspects of radiation effects, including grain boundary microchemistry, dislocation loop microstructure, radiation hardening and SCC behavior, proton-irradiation results were in good agreement with neutron-irradiation results, providing validation of the premise that the totality of neutron-irradiation effects can be emulated by proton irradiation of appropriate energy.

[1]  S. Zinkle,et al.  Microstructural processes in irradiated materials , 1999 .

[2]  L. Mansur.  Theory and experimental background on dimensional changes in irradiated alloys , 1994 .

[3]  S. Ishino,et al.  Role of charged particle irradiations in the study of radiation damage correlation , 1990 .

[4]  F. Garner.  Impact of the injected interstitial on the correlation of charged particle and neutron-induced radiation damage , 1983 .

[5]  M. Kiritani.  Microstructure evolution during irradiation , 1994 .

[6]  A. Jenssen,et al.  Importance of molybdenum on irradiation-assisted stress corrosion cracking in austenitic stainless steels , 1998 .

[7]  G. Was,et al.  Irradiation-assisted stress-corrosion cracking in austenitic alloys , 1992 .

[8]  E. Kenik.  Radiation-induced segregation in irradiated Type 304 stainless steels , 1992 .

[9]  Gary S. Was,et al.  Irradiation assisted stress corrosion cracking of controlled purity 304L stainless steels , 1993 .

[10]  D. Mazey.  Fundamental aspects of high-energy ion-beam simulation techniques and their relevance to fusion materials studies , 1990 .

[11]  Stephen M. Bruemmer,et al.  Radiation-Induced Material Changes and Susceptibility to Intergranular Failure of Light-Water-Reactor Core Internals , 1999 .

[12]  E. Kenik,et al.  Microchemistry and microstructure of proton-irradiated austenitic alloys: toward an understanding of irradiation effects in LWR core components , 1999 .

[13]  F. Nolfi.  Phase transformations during irradiation , 1983 .

[14]  Steven J. Zinkle,et al.  Dose dependence of the microstructural evolution in neutron-irradiated austenitic stainless steel , 1993 .

[15]  P. J. Maziasz,et al.  Overview of microstructural evolution in neutron-irradiated austenitic stainless steels , 1993 .

[16]  L. Rehn.  Production of freely-migrating defects , 1990 .

[17]  Roger E. Stoller,et al.  Modeling of microstructure evolution in austenitic stainless steels irradiated under light water reactor condition , 2001 .

[18]  E. P. Simonen,et al.  Proceedings of the sixth international symposium on environmental degradation of materials in nuclear power systems - water reactors , 1993 .

[19]  J. Venables,et al.  Developments in Electron Microscopy and Analysis , 1977 .

[20]  Russel H. Jones,et al.  Stress-Corrosion Cracking. Materials Performance and Evaluation , 1992 .

[21]  G. Was,et al.  Microstructure evolution in austenitic Fe-Cr-Ni alloys irradiated with rotons: comparison with neutron-irradiated microstructures , 2001 .

[22]  H. R. Higgy,et al.  Effect of fast-neutron irradiation on mechanical properties of stainless steels: AISI types 304, 316 and 347 , 1975 .