Dendrimer crosslinked collagen as a corneal tissue engineering scaffold: mechanical properties and corneal epithelial cell interactions.

Generation 2 polypropyleneimine octaamine dendrimers were used to generate highly crosslinked collagen with mechanical properties that would make it appropriate for use as a corneal tissue-engineering scaffold. Crosslinking of a highly concentrated collagen solution (2-4%) was effected using the water-soluble carbodiimide 1-ethyl-3-(3-dimethyl aminopropyl) carbodiimide hydrochloride (EDC). The multifunctional dendrimers were introduced as novel multifunctional crosslinkers after the activation of the carboxylic acid groups of glutamic and aspartic acid residues in collagen. Glutaraldehyde, a common collagen crosslinker, was used as comparison, as was EDC, itself an alternative crosslinker, which forms "zero-length or self-crosslinking". The mechanical properties resultant gels were determined. Young's modulus of the dendrimer crosslinked gels was significantly higher than that observed with the other crosslinkers, increasing to 5 MPa compared with 0.1 MPa for the EDC crosslinked gels. Transmission electron microscopy (TEM) analysis of the gels demonstrated the presence of fibrils in the thermally gelled collagen controls; no fibrils were observed in the dendrimer crosslinked gels. As a result, the optical transparency of the dendrimer crosslinked collagen was significantly better than that of the collagen thermal gels. The EDC and glutaraldehyde crosslinked gels were generally less transparent than those crosslinked with the dendrimers. Glucose permeation results demonstrated that the dendrimer crosslinked collagen had higher glucose permeability than natural human cornea. Dendrimer crosslinked collagen gels supported human corneal epithelial cell growth and adhesion, with no cell toxicity. In comparison, some potentially cytotoxic effects were observed with glutaraldehyde crosslinked collagen. Overall, the dendrimer crosslinked collagen gels showed promising properties that suggest that these might be suitable scaffolds for corneal tissue engineering and potentially other tissue engineering applications.

[1]  A. Jayakrishnan,et al.  Glutaraldehyde as a fixative in bioprostheses and drug delivery matrices. , 1996, Biomaterials.

[2]  A. Huc,et al.  Evaluation of different chemical methods for cros-linking collagen gel, films and sponges , 1996 .

[3]  H. Sheardown,et al.  Glucose permeable poly (dimethyl siloxane) poly (N-isopropyl acrylamide) interpenetrating networks as ophthalmic biomaterials. , 2005, Biomaterials.

[4]  G. Smolin,et al.  The Cornea: Scientific foundations and clinical practice , 1983 .

[5]  H. Sheardown,et al.  Crosslinking of collagen with dendrimers. , 2005, Journal of biomedical materials research. Part A.

[6]  C. W. Lin,et al.  Diffusion characteristics of collagen film. , 2001, Journal of controlled release : official journal of the Controlled Release Society.

[7]  S. Boyce,et al.  Structure of a collagen-GAG dermal skin substitute optimized for cultured human epidermal keratinocytes. , 1988, Journal of biomedical materials research.

[8]  A. I. Schneider,et al.  Constructing an in vitro cornea from cultures of the three specific corneal cell types , 1999, In Vitro Cellular & Developmental Biology - Animal.

[9]  A. C. Jayasuriya,et al.  Piezoelectric and mechanical properties in bovine cornea. , 2003, Journal of biomedical materials research. Part A.

[10]  E. Khor.  Methods for the treatment of collagenous tissues for bioprostheses. , 1997, Biomaterials.

[11]  E. J. Miller,et al.  Effect of physical crosslinking methods on collagen-fiber durability in proteolytic solutions. , 1996, Journal of biomedical materials research.

[12]  M. Moore,et al.  Shrinkage temperature versus protein extraction as a measure of stabilization of photooxidized tissue. , 1996, Journal of biomedical materials research.

[13]  M. Grant,et al.  Investigation into the biological stability of collagen/chondroitin-6-sulphate gels and their contraction by fibroblasts and keratinocytes: the effect of crosslinking agents and diamines. , 1999, Biomaterials.

[14]  A. C. Jayasuriya,et al.  A study of piezoelectric and mechanical anisotropies of the human cornea. , 2003, Biosensors & bioelectronics.

[15]  K. Tsubota,et al.  Collagen-Poly(N-Isopropylacrylamide)–Based Membranes for Corneal Stroma Scaffolds , 2003, Cornea.

[16]  A. Grodzinsky,et al.  The effects of cross-linking of collagen-glycosaminoglycan scaffolds on compressive stiffness, chondrocyte-mediated contraction, proliferation and biosynthesis. , 2001, Biomaterials.

[17]  B. Boyan,et al.  Stabilization of pericardial tissue by dye-mediated photooxidation. , 1994, Journal of biomedical materials research.

[18]  R. Guignard,et al.  Reconstructed Human Cornea Produced in vitro by Tissue Engineering , 1999, Pathobiology.

[19]  Jia-cong Shen,et al.  Enhanced biological stability of collagen porous scaffolds by using amino acids as novel cross-linking bridges. , 2004, Biomaterials.

[20]  J. Feijen,et al.  Cross-linking of dermal sheep collagen using a water-soluble carbodiimide. , 1996, Biomaterials.

[21]  H. Sheardown,et al.  Recruitment of multiple cell lines by collagen-synthetic copolymer matrices in corneal regeneration. , 2005, Biomaterials.

[22]  M. Srinivasan,et al.  Corneal blindness: a global perspective. , 2001, Bulletin of the World Health Organization.

[23]  G. Whitesides,et al.  Enzyme immobilization by condensation copolymerization into crosslinked polyacrylamide gels , 1980 .

[24]  T V Chirila,et al.  An overview of the development of artificial corneas with porous skirts and the use of PHEMA for such an application. , 2001, Biomaterials.

[25]  J. Krachmer,et al.  Clinical types of corneal transplant rejection. Their manifestations, frequency, preoperative correlates, and treatment. , 1981, Archives of ophthalmology.

[26]  B. McCarey,et al.  Modeling glucose distribution in the cornea. , 1990, Current eye research.