Strength of sandwich beams with interface debondings

Abstract The adhesive joint bonding the faces to the core material in a sandwich structure ensures that the loads are transferred between the components. However, debondings may arise either during the manufacturing process or due to overloading. These will reduce both the stiffness and the load bearing capacity of the structure. In the present paper, debondings in foam core sandwich beams are investigated assuming that cracks in the interface between the face and core are present. Stress intensity factors are found from an analytical model and compared to solutions from several finite element calculations. Fracture toughness values, determined from simple specimens, are used to predict the fracture loads for beams with simulated debondings subjected to four-point bending.

[1]  Maria Comninou,et al.  The Interface Crack in a Shear Field , 1978 .

[2]  Morton E. Gurtin,et al.  On the J-integral for Bi-material bodies , 1977, International Journal of Fracture.

[3]  Dan Zenkert,et al.  Strength of sandwich beams with mid-plane debondings in the core , 1990 .

[4]  I. Raju,et al.  Convergence of strain energy release rate components for Edge-Delaminated composite laminates , 1988 .

[5]  John W. Gillespie,et al.  Finite element analysis of the end notched flexure specimen for measuring mode II fracture toughness , 1986 .

[6]  A. H. England.  On stress singularities in linear elasticity , 1971 .

[7]  L. Gibson,et al.  Debonding in foam-core sandwich panels , 1989 .

[8]  S. A. Hamoush,et al.  Fracture energy release rate of adhesive joints , 1989 .

[9]  Morris Stern,et al.  The computation of stress intensity factors in dissimilar materials , 1978 .

[10]  K. Lin,et al.  Finite element analysis of stress intensity factors for cracks at a bi-material interface , 1976 .

[11]  Su-Su Wang,et al.  An analysis of interface cracks between dissimilar isotropic materials using conservation integrals in elasticity , 1984 .

[12]  J. Rice,et al.  Plane Problems of Cracks in Dissimilar Media , 1965 .

[13]  D. Zenkert.  Poly(vinyl chloride) sandwich core materials: Fracture behaviour under mode II loading and mixed-mode conditions , 1989 .

[14]  G. Sih.  Strain-energy-density factor applied to mixed mode crack problems , 1974 .

[15]  R. E. Smelser,et al.  Evaluation of stress intensity factors for bimaterial bodies using numerical crack flank displacement data , 1979, International Journal of Fracture.

[16]  Maria Comninou,et al.  The Interface Crack , 1977 .

[17]  F. Erdogan,et al.  Stress Distribution in Bonded Dissimilar Materials With Cracks , 1965 .