Effect of Laser Welding on Formability of DP980 steel

Limiting dome height (LDH) tests were used to evaluate the formability of laser butt welded blanks of the dual phase 980 steel in comparison with the base metal. Two different lasers were used: diode and Nd:YAG, giving a wide range of welding thermal cycles. A sharp decrease in LDH was observed in the welded specimens due to the formation of a softened zone in the outer heat affected zone. Softened zone characteristics were correlated with the LDH. Larger softened zones led to a larger reduction in the LDH. The welding orientation relative to the rolling direction or to the punch surface did not influence the formability, as the softened zone dominated the formability behavior. It was observed that in both uniaxial and biaxial strain tests, the fracture occurred in the softened zone of the welded samples consistently slightly farther out from the weld centerline than in the location of the minimum hardness. DOI: 10.1115/1.2969246

[1]  J. Ready.  LIA handbook of Laser materials processing , 2001 .

[2]  Formability Analysis of High Strength Steel Laser Welded Blanks , 2005 .

[3]  C. Albright,et al.  CO2 and Nd:YAG laser beam welding of 6111-T4 aluminum alloy for automotive applications , 2000 .

[4]  Johnny K. Larsson.  Supporting Welding Methods for Future Light Weight Steel Car Body Structures , 2002 .

[5]  R. H. Wagoner,et al.  Forming of tailor-welded blanks , 1996 .

[6]  C. L. Chow,et al.  Formability Analysis of Tailor-Welded Blanks of Different Thickness Ratios , 2005 .

[7]  Koichi Maeda,et al.  Welding of aluminum alloy with high power direct diode laser , 2003, SPIE LASE.

[8]  Y. T Keum,et al.  Evaluation of the mechanical properties of welded metal in tailored steel sheet welded by CO2 laser , 2001 .

[9]  N. T. Williams,et al.  Influence of weld orientation on forming limit diagram of similar/dissimilar thickness laser welded joints , 1996 .

[10]  D. Hughes,et al.  Methods of assessing influence of weld properties on formability of laser welded tailored blanks , 2001 .

[11]  Bon-Young Ghoo,et al.  Evaluation of Mechanical Properties of Welded Metal in Tailored Steel Sheet Welded by $ CO_2$ Laser , 2001 .

[12]  Ram Avtar,et al.  Resistance Spot Weldability of Comparatively Thick C-Mn-Cr-Mo Dual Phase Steel Sheet , 1990 .

[13]  Y. Zhou,et al.  A Comparative Study of Formability of Diode Laser Welds in DP980 and HSLA Steels , 2007 .

[14]  E. Wallach,et al.  The Influence of the Weld Structure on the Formability of Laser Welded Tailored Blanks , 1998 .

[15]  H. Suzuki,et al.  DETERMINATION OF NECESSARY PREHEATING TEMPERATURE IN STEEL WELDING , 1983 .